Corrosion resistant brass alloy material for plate heat exchanger and processing technique thereof

A plate heat exchanger and corrosion-resistant brass technology, applied in the field of non-ferrous metal processing, can solve the problems of difficult processing, high chloride ion corrosion resistance, and high cost, and achieve low cost, good deep drawing performance, and easy processing. control effect

Active Publication Date: 2008-01-09
中铝洛阳铜加工有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the alloy materials used before are stainless steel, pure titanium, nickel and nickel alloy materials, all of which have defects such as high cost, difficult processing, and resistance to high chloride ion corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Example 1: Corrosion-resistant brass alloy coils for plate heat exchangers of 0.4×300×500mm

[0031] Use power frequency cored induction furnace for smelting, and make ingredients according to the proportion of ingredients: Cu79%, Al3.5%, Ni1.5%, B0.015%, As0.1%, the balance of Zn, the total amount of impurities 0.3% and Rare earth additive Ce0.05%. Feeding sequence: adding Zn ingot, Al ingot, Cu-Ni, Cu-B, Cu-As and other master alloys and rare earth additive Ce, melting temperature: 1050°C. Casting adopts vertical semi-continuous casting, casting speed: 3.5m / h, crystallizer cooling water pressure: 0.05MPa; heating: use walking heating furnace for ingot heating, heating temperature: 750℃, heating time 3 hours; annealing Divided into: intermediate annealing and finished product annealing, heating temperature used in intermediate annealing: 400°C, holding time: 4 hours; heating temperature used in finished annealing: 500°C, holding time: 3 hours; pre-finishing rolling, f...

Embodiment 2

[0032] Example 2: 8.5×1000×3000mm corrosion-resistant brass alloy strip for plate heat exchanger

[0033] Use power frequency cored induction furnace for smelting, and make ingredients according to the proportion of ingredients: Cu: 76%, Al: 1.0%, Ni: 0.3%, B: 0.002%, As: 0.01%, balance: Zn, total amount of impurities : 0.3%, feeding order: add Zn ingot, Al ingot, Cu-Ni, Cu-B, Cu-As and other intermediate alloys, melting temperature: 1250°C. Casting adopts vertical semi-continuous casting, casting speed: 6m / h, crystallizer cooling water pressure: 0.35MPa; heating: use walking heating furnace for ingot heating, heating temperature: 950℃, heating time 6 hours; For: intermediate annealing and finished product annealing, heating temperature used in intermediate annealing: 650°C, holding time: 10 hours; heating temperature used in finished product annealing: 750°C, holding time: 6 hours; pre-finishing rolling, finishing rolling: adopted processing rate : 70%.

[0034] To sum up: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

A corrosion-proof brass band for plate heat exchanger and its production are both disclosed herewith. It contains (wt%): Cn 76-79, Al 1.0-3.5, Ni 0.3-1.5, B 0.002-0.015, As 0.01-0.1, Ce 0.05-0.2, and balanced with Zn, and with impurity not more than 0.3. It is produced by: weighing, smelting, casting, hot rolling, end-surface milling, primary rolling, inter-annealing, cold rolling, inter-annealing, edge cutting, pre-rolling, inter-rolling, fine rolling, final annealing, surface treating, cutting, and packing. It is of size (0.4-8.5mm)X(300-1000mm)X(500-3000mm), performance of Rm not less than 410MPa, A11.3 not less than 40%, Hv1 not less than 90, grain 0.010-0.030mm, and Ra larger than 0.2um without scratches.

Description

technical field [0001] The invention belongs to the technical field of nonferrous metal processing, and in particular relates to a corrosion-resistant brass alloy material for a plate heat exchanger and a processing technology. Background technique [0002] At present, the plate heat exchanger (PHE) has become an efficient and compact heat exchange equipment, and is widely used in industrial heat exchange fields, such as seawater desalination, coastal aquaculture, geothermal, urban sewage treatment, etc. In addition, due to the harsh working environment of the washing machine, the key internal materials are required to have good corrosion resistance while maintaining a certain strength and wear resistance. Most of the alloy materials used before are stainless steel, pure titanium, nickel and nickel alloy materials, all of which have defects such as high cost, difficult processing, and resistance to high chloride ion corrosion. Contents of the invention [0003] In order t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/04C22C1/02C22C1/06B22D21/00C22F1/08
Inventor 娄花芬马可定黄国兴叶成效高双玲路俊攀蒋长乐陈少华刘富良韩卫光
Owner 中铝洛阳铜加工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More