Method for manufacturing high-strength direct-spreading knife-scraping tarpaulin

A manufacturing method and high-strength technology, applied in the field of textile materials, can solve the problems of low tear strength, insufficient softness, poor self-cleaning performance, etc., and achieve good economic and social benefits.

Active Publication Date: 2008-02-06
浙江锦达新材料股份有限公司
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Canvas plays an important role in people's daily production and life. From storage cloth, to vehicle and boat cloth, to military camping, tarpaulin is needed. However, most of the tarpaulin products on the market currently have fractures and tears. Low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of manufacture method of high-strength direct-coating type knife scraping method tarpaulin comprises the following steps:

[0027] 1), the following weight components are mixed into coating agent:

[0028] PVC paste resin (PSM-31) 100 parts

[0029] Plasticizer (DOP) 70 parts

[0030] Barium zinc stabilizer 2.5 parts

[0031] Calcium carbonate 30 parts

[0032] Antimony trioxide 5 parts

[0033] Zinc borate 2 parts

[0034] Titanium dioxide 4 parts

[0035] 2) Grind and filter the mixed coating agent, and filter with 80 mesh nylon mesh;

[0036] 3) Pass the 1000D*1000D polyester woven fabric with a density of 8*8 strands / cm through the coating machine at a uniform speed through the unwinding mechanism, and add 1.8kg of crosslinking agent to every 100kg of coating agent. The isocyanate group in the crosslinking agent (-NCO) content is 3%, coating weight is 105g / m 2 , evenly coated on the polyester woven fabric, and dried in an oven at a tempe...

Embodiment 2

[0038] Embodiment 2: a kind of manufacture method of high-strength direct-coating type knife scraping method tarpaulin comprises the following steps:

[0039] 1), the following weight components are mixed into coating agent:

[0040] PVC paste resin (R1069) 100 parts

[0041] Plasticizer (DOP) 68 parts

[0042] Calcium zinc stabilizer 2.5 parts

[0043] Calcium carbonate 40 parts

[0044] Antimony trioxide 11 parts

[0045] Zinc borate 6.5 parts

[0046] 8 parts phthalocyanine blue

[0047] 2) Grind and filter the mixed coating agent, and filter with 100 mesh nylon mesh;

[0048] 3) The polyester woven fabric with a density of 1000D*1000D of 8*8 strands / cm passes through the coating machine at a uniform speed through the unwinding mechanism, and 5kg of crosslinking agent is added in every 100kg of coating agent, and the isocyanate group in the crosslinking agent ( -NCO) content is 4%, is evenly coated on the polyester woven fabric, carries out drying treatment through t...

Embodiment 3

[0049] Embodiment 3: a kind of manufacture method of high-strength direct-coating type knife scraping method tarpaulin comprises the following steps:

[0050] 1), the following weight components are mixed into coating agent:

[0051] PVC paste resin (P440) 100 parts

[0052] Plasticizer (DINP) 75 parts

[0053] Organotin stabilizer 2 parts

[0054] Aluminum hydroxide 30 parts

[0055] 4 parts zinc borate

[0056] 8 parts antimony trioxide

[0057] Purple B 1.5 parts

[0058] 2) Grind and filter the mixed coating agent, and filter with 40 mesh nylon mesh;

[0059] 3) The polyester woven fabric with a density of 1000D*1000D of 8*8 strands / cm passes through the coating machine at a uniform speed through the unwinding mechanism, and 3kg of crosslinking agent is added to every 100kg of coating agent, and the isocyanate group in the crosslinking agent ( -NCO) content is 5%, is evenly coated on the polyester woven fabric, carries out drying treatment through the oven, then pas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a manufacturing method of tarpaulin with high strength and direct coating knife scraping, and the method is performed as per the following steps: (1)a composition with a certain weight including PVC paste resin, plasticizer, stabilizer, filling, fire resistant agent and painting is mixed to form coating agent; (2)the mixed coating agent is grinded and filtrated; (3)1-5kg cross-linking agent is added into each 100kg coating agent, and are evenly coated on a base cloth, and drying is executed; (4)after plasticizing and forming, surface treatment agent is used for treating. The tarpaulin manufactured with the method in the present invention has the advantages of waterproof, oil resistance, dirt resistance, fireproof, aging resistance, stripping resistance, etc., which can be used for carriage tarpaulin, carriage side curtain cloth and cloth for a container with the top opened; train tarpaulin and ship tarpaulin; building material, applied for building material for soft roof, such as a supermarket, a stadium and a sightseeing building; for military use, for temporary rest of the field army, headquarters during wartime, etc.

Description

technical field [0001] The invention belongs to the technical field of textile materials, in particular to a method for manufacturing tarpaulins by direct coating method. Background technique [0002] Canvas plays an important role in people's daily production and life. From storage cloth, to vehicle and boat cloth, to military camping, tarpaulin is needed. However, most of the tarpaulin products on the market currently have fractures and tears. Due to the shortcomings of low strength, poor fire performance, insufficient softness, and poor self-cleaning performance, customers expect new products with high strength, good flame retardancy, high breaking and tearing strength, and surface self-cleaning functions. Therefore, the old products urgently need to be upgraded to meet the requirements of customers, and are applied to new and expanding application fields such as soft cars, soft roofs and military equipment. Contents of the invention [0003] In order to make up for ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00B05D1/38D06M13/00
Inventor 叶雪康
Owner 浙江锦达新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap