Self-levelling elastic mortar

A self-leveling and elastic technology, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problems of incompatibility between elasticity and self-leveling, and achieve the effect of improving the flexural strength

Inactive Publication Date: 2008-06-11
熊永强 +1
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing mortar preparation process, elasticity and self-leveling properties are usually incompatible, and there is no mortar product with excellent elasticity and self-leveling properties on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Raw material quality percentage (%) Remarks

[0034] Cement 20 425R

[0035] Quartz sand 60 60~200 mesh

[0036] Polymer emulsion 5 DL470

[0037] Water reducing agent 2 Melment F10

[0038] Defoamer 0.1 Dehydran 1922

[0039] Water 12.9

[0040] The cement is ordinary Portland cement 425R. The polymer emulsion used is DL 470 produced by Dow Reichhold Company, which is a styrene-butadiene copolymer emulsion with a solid content of 45%-47% (W%), a PH value of 8.5-11, and the Brookfield viscosity maximum The value is 100 cPs, and the glass transition temperature is 8°C. The water reducing agent used Melment F10 produced by Degussa, Germany. The defoamer used is Dehydran 1922 produced by Cognis.

[0041] Weigh the corresponding raw materials according to the above-mentioned weight ratio, mix cement and sand uniformly to prepare solid phase components, and mix polymer emulsion, water reducing agent, defoamer, and water uniformly to prepare liquid phase components. Add the solid...

Embodiment 2

[0043] Raw material quality percentage (%) Remarks

[0044] Cement 35 425R

[0045] Quartz sand 35 60~200 mesh

[0046] Polymer emulsion 15 DL470

[0047] Water reducing agent 0.5 Mighty 100

[0048] Defoamer 0.8 Foamaster PD-1

[0049] Water 13.7

[0050] Among them, the water-reducing agent uses the naphthalene-based water-reducing agent Mighty 100 from Kao Corporation of Japan. The defoamer used is Foamaster PD-1 produced by Cognis.

[0051] Weigh the corresponding raw materials according to the above-mentioned weight ratio, mix cement and sand uniformly to prepare solid phase components, and mix polymer emulsion, water reducing agent, defoamer, and water uniformly to prepare liquid phase components. Add the solid phase component to the liquid phase component and stir at a medium speed for 3 minutes to obtain the finished product. According to the above method, the results are as follows: initial fluidity, 147mm; impact resistance, no cracking or separation from the bottom plat...

Embodiment 3

[0053] Raw material quality percentage (%) Remarks

[0054] Cement 10 425R

[0055] Quartz sand 45 60~200 mesh

[0056]Fly Ash 10 Class II

[0057] Polymer emulsion 25 DL470

[0058] Water reducing agent 0.1 Mighty 100

[0059] Defoamer 1.5 Foamaster PD-1

[0060] Water 8.4

[0061] Weigh the corresponding raw materials according to the above weight ratio, mix cement, sand and fly ash uniformly to prepare solid phase components, and mix polymer emulsion, water reducing agent, defoamer, and water uniformly to prepare liquid phase components. Add the solid phase component to the liquid phase component and stir at a medium speed for 3 minutes to obtain the finished product. According to the above method, the test results are as follows: initial fluidity, 196mm; impact resistance, no cracking or separation from the bottom plate; tensile bond strength, 1.14MPa; flexural strength, 14.2MPa; compressive strength, 26.3MPa; compression ratio , 1.85.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to a technical field of building materials, providing self-leveling elastic mortar. The component and weight percentage of the self-leveling elastic mortar are that cement takes 10-35%, quartz sand takes 30-70%, admixture takes 0-10%, polymer emulsion takes 5-25%, water reducing agent takes 0.1-2%, defoamer takes 0.1-1.5% and water takes 0-20%. The film of the mortar of the invention is provided with elasticity and strength, simultaneously, the self-leveling of the mortar is good, which satisfies construction requirements.

Description

Technical field [0001] The invention relates to mortar for construction, in particular to a self-leveling elastic mortar. Background technique [0002] After decades of development, flooring has become a fairly mature industry in developed countries. It has a complete range, including hundreds of products in several series such as epoxy, chlorinated polyolefin, polyurethane, polyurea, etc., integrating protection, decoration, and functions. The application range of the floor ranges from general-purpose industrial plants, corridors, parking lots, shopping malls to highly decorative sports venues, hotel halls, and even high-performance conductive, spark-proof, chemical-resistant and other special floors, and the application surface growing. Since the reform and opening up, the construction of a large number of development zones and industrial plants has stimulated the development of the floor industry. As domestic specialized flooring companies gradually enter the fast lane of deve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/06C04B24/24C04B111/62
CPCC04B2111/503C04B2111/62C04B28/06C04B28/04Y02W30/91C04B14/06C04B14/28C04B18/08C04B24/24C04B2103/302C04B2103/50
Inventor 熊永强谭亮
Owner 熊永强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka