Anti-static poly(ethylene terephthalate) material and preparation method thereof

A technology of polyethylene terephthalate and ethylene terephthalate is applied in the field of antistatic polyethylene terephthalate material and its preparation, and can solve the problem of weakening and disappearing of antistatic effect, etc. problem, to achieve the effect of excellent antistatic performance, mild conditions and good compatibility

Inactive Publication Date: 2008-07-30
合诚技术股份有限公司
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the use of the film, the antistatic effect will be weakene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] Preparation of antistatic agent: Weigh 1 mole of sodium polystyrene sulfonate and 1 mole of nano silver sol based on the sodium styrene sulfonate group and reflux in 500 ml of water for 5 hours, and then depressurize to vacuum at 80°C It is dried under the condition of 0.09MPa, is ground with a mechanical grinder, and grinds to a particle size of 0.1-5μm to obtain an antistatic agent.

[0024] Preparation of antistatic polyethylene terephthalate material: In parts by weight, weigh out 1,936 grams of polyethylene terephthalate, 60 grams of the antistatic agent prepared above, and 4 grams of antioxidant. After mixing uniformly, extrude and granulate at 255°C. Antioxidant is composed of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester and tris(2,4-di-tert-butylphenyl) phosphite at a molar ratio of 1 : 2 composition.

Example Embodiment

[0025] Example 2

[0026] Preparation of antistatic agent: Weigh 1 mole of sodium polystyrene sulfonate and 1 mole of nano silver sol based on the sodium styrene sulfonate group, reflux for 6 hours in 500 ml of water, and depressurize to vacuum at 100°C It is dried under the condition of 0.08MPa and ground to a particle size of 0.1-5μm by a mechanical grinding method to obtain an antistatic agent.

[0027] Preparation of antistatic polyethylene terephthalate material: In parts by weight, weigh 1,863 grams of polyethylene terephthalate, 130 grams of antistatic agent prepared above, and antioxidant (same as Example 1) 7 grams, mixed uniformly, extruded and pelletized at 260°C.

Example Embodiment

[0028] Example 3

[0029] Preparation of antistatic agent: Weigh 1 mole of sodium polystyrene sulfonate and 1 mole of nano-silver sol based on the sodium styrene sulfonate group and reflux for 5.5 hours in 500 ml of water, and depressurize to vacuum at 90°C It is dried under the condition of 0.07MPa, and pulverized to a particle size of 0.1-5μm by a mechanical grinding method to obtain an antistatic agent.

[0030] Preparation of antistatic polyethylene terephthalate material: In parts by weight, weigh 1790 grams of polyethylene terephthalate, 200 grams of antistatic agent prepared above, and antioxidant (same as Example 1) 10 grams, mixed uniformly, extruded and pelletized at 265°C.

[0031] In the above embodiment, the raw material sodium polystyrene sulfonate is the product of Aldrich Company in the United States; the nano silver sol is the product of Lucky Company; the antioxidant is composed of tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) ) Propionic acid] pentaerythritol este...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface resistivityaaaaaaaaaa
Volume resistivityaaaaaaaaaa
Surface resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic polyethylene glycol terephthalate and a preparation method thereof. The antistatic polyethylene glycol terephthalate calculated according to the parts by weight comprises 96.8-89.5 parts of polyethylene glycol terephthalate, 3-10 parts of antistatic agent, and 0.2-0.5 part of antioxidant. The antioxidant is composed of [Beta-(3,5-di-tert-butyl-4-hydroxy-phenyl) methyl acetic acid] pentaerythritol ester and tri dimethylphenyl phosphate (2,4-di-tert-butyl-benzyl) according to the mol ratio of 1:2. The antistatic agent comprises water-soluble polymer sodium polystyrene sulfonate and nano-silver colloid with equal molar, and the preparation method comprises the following steps: the water-soluble polymer sodium polystyrene sulfonate and the nano-silver colloid with equal molar flow back in water for 5-6 hours, the coordination reaction happens between the molar water-soluble polymer sodium polystyrene sulfonate and the nano-silver colloid to cause the molar water-soluble polymer sodium polystyrene sulfonate and the nano-silver colloid to be combined together, and then the composition is dried and ground. The antistatic polyethylene glycol terephthalate has good antistatic performance, the preparation process is simple, and the preparation method is convenient and easy to be operated.

Description

technical field [0001] The invention relates to the field of antistatic polyester, in particular to an antistatic polyethylene terephthalate material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate is a highly crystalline polymer with excellent physical and mechanical properties in a wide temperature range, good friction resistance and dimensional stability. As an important engineering plastic, it is widely used It is used in various fields of electronic appliances, information communication, and daily necessities. However, polyethylene terephthalate has a compact structure, high crystallinity, hydrophobicity, poor hygroscopicity, high specific resistance, large frictional voltage, and is prone to static electricity. Electrostatic charges are more likely to accumulate in low humidity environments. The accumulation of static electricity will cause vicious accidents such as vacuuming, electric shock, and even explosion after sparks ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/03C08K13/02C09K3/16C08K5/524
Inventor 蒋文真李文国李刚吴水珠赵建青
Owner 合诚技术股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap