Technique for producing aluminum magnesium plating copper wire copper-coating
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production process and copper plating technology, which is applied in the field of copper plating of aluminum-magnesium copper-plated wires, can solve the problems of poor adhesion, poor uniformity, peeling of aluminum-magnesium copper-plated rods, exposed aluminum, etc., and achieves light weight , excellent electrical conductivity, the effect of improving product quality
Inactive Publication Date: 2008-08-27
丹阳利华电子有限公司
View PDF0 Cites 20 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
If the adhesion and uniformity are not good, the aluminum-magnesium copper-plated rods produced will have peeling and aluminum exposure during the process of thinning
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] Embodiment 1; A kind of production technology of aluminum-magnesium copper-plated wire copper-plated, comprises the following steps:
[0012] 1. Putting wire;
[0013] 2. Alkaline washing;
[0014] 3. Washing;
[0015] 4. Sulfuric acid washing;
[0016] 5. Washing;
[0017] 6. Alkaline washing;
[0018] 7. Washing;
[0019] 8. The first zinc immersion: mix 62 parts of water, 7 parts of zinc oxide, 31 parts of sodium hydroxide, 2 parts of potassium sodium tartrate, and 0.06 parts of ferric chloride. The first zinc immersion is completed in the solution at 27°C.
[0020] 9. Washing;
[0021] 10. Nitric acid dezincification: nitric acid: water = 4:6;
[0022] 11. Washing;
[0023] 12. The second zinc immersion: mix 72 parts of water, 15 parts of zinc oxide, 9 parts of sodium hydroxide, 4 parts of potassium sodium tartrate, 0.01 part of ferric chloride, and 0.002 parts of sodium nitrate for 20-40 seconds , Complete the second zinc immersion in the solution with a ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
Login to view more
Abstract
A manufacturing process of plating copper by using aluminum-magnesium copper-plating wire comprises the following steps: arranging wire, cleaning by alkali, cleaning by water, cleaning by sulfuric acid, cleaning by water, cleaning by alkali, cleaning by water, a first time soaking zinc, cleaning by water, removing the zinc by nitric acid, cleaning by water, a second time soaking zinc, cleaning by water, cleaning by hot water, pre-plating nickel, cleaning by water, activating, acidicly plating copper, cleaning by water, carrying out the anti-oxidation treatment, cleaning by hot water, drying and taking out the wire. The manufacturing process is characterized in that the process of the first time zinc soaking is that completing the first time zinc soaking in solution with temperature of 12-27DEG C for 30-60 sec after mixing with 60 parts water, 7 parts zinc oxide, 31 parts superalkali, 2 parts potassium sodium tartrate and 0.06 parts iron trichloride. By adopting the manufacturing process of the invention, the aluminum-magnesium copper-plating wire has the double advantages that aluminium conductor has light weight and low cost, copper conductor has high conductivity and good chemical stability, wherein the specific weight of copper is about 18-19%, mean density is 2.8g / cm3, the length of aluminum-magnesium copper plating wire whose size and weight are the same with that of pure copper wire is 3.1 times than that of the pure copper wire, tensile strength is more than or equal to 210, which enables the aluminum-magnesium copper plating wire uneasily to break and improves the quality of the products.
Description
technical field [0001] The invention relates to a production method for coaxial cable inner conductors, audio and video line conductors, data cable telephone lines, network lines, and electric wire and cable conductor lines in electrical equipment, in particular to a production process for aluminum-magnesium copper-coated copper-plated wires. Background technique [0002] With the shortage of copper resources in the world and the technological progress of the material industry, the overall world's demand for copper resources is increasing and the earth's resources are decreasing. From the perspective of resources, the price increase of copper and other metals is an inevitable trend in the world in the future. . The emergence of bimetallic composite materials came into being. The conductivity of pure aluminum is very good, second only to silver and copper. In the power industry, it can replace part of copper as wires and cables. Copper and aluminum composite materials appear...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.