Chlorinated polythylene fire retardant jacket compositions

A chlorinated polyethylene, flame retardant sheath technology, used in conductors, electrical components, circuits, etc.

Active Publication Date: 2010-07-14
四川川东电缆有限责任公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Currently, the main problem of CPE (chlorinated polyethylene) in the field of cables is: CPE (chlorinated polyethylene) series formulation problems regardless of CPE insulating rubber or sheath Rubber, in the specific application of various domestic manufacturers, there are problems in the aspect of immature formula, so that the product quality has substandard problems such as blistering, holes and cracks, so that not only can not use CPE in large quantities, but also increase the number of waste products due to the increase. Cost of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061]100 kg CPE135B, 5-8 kg compound rare earth stabilizer REC-LS, 5-6 kg active agent RA, 3-5 kg ​​vulcanizing agent thiadiazole 1680, 1.5-2 kg accelerator VOR240, 1-2 kg surface treatment agent ZnSt, 1-2 kg anti-aging agent RD, 2-3 kg processing aid WB222, 2-3 kg microcrystalline paraffin, 10-12 kg active magnesium oxide, 20-25 kg trioctyl TOTM, 20-25 kg nanometer Activated white carbon black, 25-30 kg of high-performance composite flame retardant HZR-2, 20-30 kg of white talc, 20-25 kg of nano calcium carbonate.

[0062] Take the following raw materials: 100 kg of CPE135B, 8 kg of composite rare earth stabilizer REC-LS, 6 kg of active agent RA, 5 kg of vulcanizing agent thiadiazole 1680, 2 kg of accelerator VOR240, 2 kg of surface treatment agent ZnSt, 2 kg of anti-aging agent RD, 3 kg of processing aid WB222, 3 kg of microcrystalline paraffin, 12 kg of activated magnesium oxide, 25 kg of trioctyl TOTM, 25 kg of nano-high active white carbon black, 30 kg of high-performanc...

Embodiment 2

[0064] Take the following raw materials: 100 kg of CPE135B, 5 kg of composite rare earth stabilizer REC-LS, 5 kg of active agent RA, 3 kg of vulcanizing agent thiadiazole 1680, 1.5 kg of accelerator VOR240, 1 kg of surface treatment agent ZnSt, 1 kg of anti-aging agent RD, 2 kg of processing aid WB222, 2 kg of microcrystalline paraffin, 10 kg of activated magnesium oxide, 20 kg of trioctyl TOTM, 20 kg of nano-high active white carbon black, 25 kg of high-performance composite flame retardant HZR-2, 20 kg of white talc, 20 kg of nanometer calcium carbonate.

Embodiment 3

[0066] Take the following raw materials: 100 kg of CPE135B, 7 kg of composite rare earth stabilizer REC-LS, 5.5 kg of active agent RA, 4 kg of vulcanizing agent thiadiazole 1680, 0.8 kg of accelerator VOR240, 1.5 kg of surface treatment agent ZnSt, 1.5 kg of anti-aging agent RD, 2.5 kg of processing aid WB222, 2.5 kg of microcrystalline paraffin, 11 kg of activated magnesium oxide, 23 kg of trioctyl TOTM, 23 kg of nano-high active white carbon black, 28 kg of high-performance composite flame retardant HZR-2, 25 1 kg of white talc, 23 kg of nanometer calcium carbonate.

[0067] Composite rare earth stabilizer REC-LS is produced by Qingdao Laosu Building Materials Group Company.

[0068] The processing preparation method of the embodiment of the present invention 1~3 is as follows:

[0069] Mixing process: Weigh the components according to the requirements of the formula, fully mix them on the rubber internal mixer according to a certain feeding sequence, mixing time and temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
retention rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chlorinated polyethylene flame-retardant sheath material compound. The flame-retardant sheath material compound comprises compositions with the following weight portions: 100 portions of chlorinated polyethylene, 5 to 8 portions of rare earth complex stabilizer REC-LS, 25 to 30 portions of high-performance complex flame retardant HZR-2, 3 to 5 portions of thiadiazole derivative curing agent, and 1.5 to 2 portions of aldehyde-amine condensate accelerant. A cable obtained by the invention has more comprehensive performance, good mechanical property, ozone-resistant andchemical-resistant performance, flame resistance and oil resistance, high temperature-resistant class, and free color matching.

Description

technical field [0001] The invention relates to the field of wire and cable processing, in particular to a chlorinated polyethylene flame-retardant sheath material composition. Background technique [0002] At present, the main problem of CPE (chlorinated polyethylene) in the field of cables is: CPE (chlorinated polyethylene) series formula problem No matter CPE insulating rubber or sheath rubber, there are immature formulas in the specific applications of domestic manufacturers. There are many problems in the field of production, and even the unqualified problems of product quality such as blistering, hole formation and cracking, so that not only can not use CPE in large quantities, but also increase the production cost due to the increase of waste products. Contents of the invention [0003] The present invention overcomes the above-mentioned shortcomings, and proposes a chlorinated polyethylene flame-retardant sheath material composition, which is suitable for use as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/28C08K5/47H01B7/295C08K5/17C08K3/22
Inventor 李永辉李章学邓一权
Owner 四川川东电缆有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com