Preparation of waste paper-reinforced regenerative high-density polyethylene composite material

A technology of high-density polyethylene and composite materials, applied in the field of material processing, can solve the problems of waste of resources, secondary pollution of waste paper, etc., and achieve the effects of saving resources, reducing pollution, and shortening the process

Inactive Publication Date: 2008-11-12
KUNMING UNIV OF SCI & TECH
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a waste paper-reinforced recycled high-density polyethylene composite material, which can be used to make all kinds of waste paper and recycled high-density polyethylene composite materials suitable for life, construction, chemical industry, environmental protection, transportation and other industries. This kind of product is a kind of material with excellent performance instead of wood, plastic and aluminum alloy, and can solve the problems of secondary pollution caused by waste of resources and waste paper at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) waste paper and water are put into the conventional mechanical agitation equipment of prior art by the mass ratio of 5:95, stirring and dispersing into concentration is 5% fiber pulp, after washing 2 times with clear water, air-dry stand-by;

[0029] (2) Fully mix the raw materials by the following mass ratio: waste paper: recycled high-density polyethylene HDPE=15 kilograms: 85 kilograms;

[0030] (3) Put 100 kilograms of above-mentioned mixtures into a conventional mixing furnace in the prior art, heat to 140° C., and mix for 20 minutes;

[0031] (4) Put the material mixed in step (3) into a mould, press and form it under the condition of a molding pressure of 5 MPa, and demould after cooling for 5 minutes to obtain a waste paper reinforced recycled high-density polyethylene composite material.

Embodiment 2

[0033] (1) waste paper and water are put into the conventional mechanical agitation equipment of prior art by the mass ratio of 10:90, stirring and dispersing into concentration is 10% fiber pulp, after washing 3 times with clear water, air-dry stand-by;

[0034] (2) Fully mix the raw materials by the following mass ratio: waste paper: recycled high-density polyethylene HDPE: γ-aminopropyltriethoxysilane KH550=5 kilograms: 94 kilograms: 1 kilogram;

[0035] (3) Put 100 kilograms of the above-mentioned mixture into a conventional mixing furnace in the prior art, heat to 160° C., and mix for 10 minutes;

[0036] (4) Put the material mixed in step (3) into a conventional product mold of the prior art, press and form it under the condition of a molding pressure of 10 MPa, cool for 1 minute and demould, and then the waste paper reinforced recycled high Density polyethylene composite.

Embodiment 3

[0038] (1) waste paper and water are put into the conventional mechanical agitation equipment of prior art by the mass ratio of 10:90, stirring and dispersing into concentration is 10% fiber pulp, after washing 3 times with clear water, air-dry stand-by;

[0039] (2) Fully mix the raw materials by the following mass ratio: waste paper: recycled high-density polyethylene HDPE: γ-aminopropyltriethoxysilane KH550=10 kilograms: 86 kilograms: 4 kilograms;

[0040] (3) Put 100 kilograms of the above-mentioned mixture into a conventional mixing furnace in the prior art, heat to 150° C., and mix for 8 minutes;

[0041] (4) Put the material mixed in step (3) into a conventional product mold of the prior art, press and form it under the condition of a molding pressure of 8 MPa, cool for 3 minutes and demould, and then the waste paper reinforced recycled high Density polyethylene composite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a waste paper reinforced recycled high density polyethylene composite material, which is characterized by comprising the following raw materials by mass percentage: 5 to 15 percent of waste paper, 85 to 95 percent of recycled high density polyethylene, 0 to 4 percent of coupling agent and 0 to 10 percent of compatilizer. The waste paper is mixed with the recycled HDPE, the coupling agent and the compatilizer after fiber dispersion, and the mixture is sent into an open dual-roller mixing device for mixing and homogenizing, pressed by a section mold, and then cooled, demoulded and made into the waste paper reinforced recycled high density polyethylene composite material. The waste paper reinforced recycled high density polyethylene composite material not only can fully utilize the waste paper and waste plastics and change the waste into the valuable but also can greatly improve the comprehensive utilization level of waste resources and save a large number of resources, and simultaneously can reduce the environmental pollution caused by mismanagement of waste material resources. Moreover, the waste paper reinforced recycled high density polyethylene composite material has the advantages of simple technique, short flow, low investment, no pollutant emission, energy conservation and low consumption, low cost of the raw materials, good texture and high strength of the composite material obtained, and no harmful gas emission, and is a waste utilization project which is favorable for the country, the people and the enterprises.

Description

technical field [0001] The invention relates to a composite material, in particular to a waste paper reinforced recycled high-density polyethylene composite material, which belongs to the technical field of material processing. Background technique [0002] Waste paper is a secondary fiber that contains a lot of impurities and does not have thermoplasticity. The recycling rate of waste paper in our country is low, and a large amount of waste paper has not been properly recycled, resulting in a great waste of resources. [0003] In order to protect the environment, reduce the processing load of municipal solid waste (of which waste paper accounts for about 1 / 3), reduce the felling of forest logs, and maintain ecological balance, it is an important topic that people pay attention to to study the recycling and utilization of waste paper. At present, countries around the world have made great progress in the research on waste paper recycling technology. my country's waste pape...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L1/02C08J5/04C08K5/54B29C70/40B29B7/00B29K23/00B29K311/12
Inventor 孙可伟张春红宋平
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products