Elastic emulsion paint and method for preparing same

An elastic latex paint, low-speed stirring technology, applied in the field of latex paint, can solve the problems of poor stain resistance, can not be popularized and used, and the stain resistance of elastic latex paint is reduced, so as to achieve strong stain resistance, prevent rainwater from infiltrating, reduce coating The effect of installation cost

Inactive Publication Date: 2009-01-07
山西天时涂料装饰有限公司
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large temperature difference between the north and the south of our country, the elastic latex paint produced by most enterprises is only suitable for use in this area.
At the same time, it is generally required that the elongation of elastic latex paint is ≥ 350%, but with the increase of elasticity, the stain resistance of elastic latex paint will gradually decrease, and the technical requirements must be balanced between the two
At present, most of the elastic latex paints produced in my country can guarantee good elasticity, but the stain resistance is generally poor, so they cannot be popularized and used in large areas.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053]Add 3Kg of adipic acid dihydrazide into 180L of deionized water, and stir at a low speed of 600 rpm for 5 minutes to completely dissolve it. Add 2Kg hydroxyethyl cellulose, 20Kg propylene glycol, 6Kg 5040 dispersant, 1Kg defoamer DX-46, 1.2Kg preservative LXE and 1Kg pH stabilizer AMP-95, and stir at low speed for 5-10 minutes. Keep stirring, add 50Kg215 titanium dioxide, 100Kg wollastonite powder, 50Kg kaolin and 150Kg800 mesh heavy calcium in sequence, disperse at 1500 rpm for 45-55min at high speed, and detect the fineness to ≤45um. Reduce the rotation speed to 800 rpm, and add 100Kg water-based fluorocarbon resin, 80Kg styrene-acrylic emulsion and 300Kg elastic emulsion in sequence. After adding one raw material, stir for 5 minutes before adding the next raw material. Finally, add 10Kg film-forming aid TEXNOL and 1.5Kg wetting agent X-405, adjust the viscosity with 3KgWL-700 polyurethane rheology modifier and 6-8KgTT-935 thickener, and adjust the speed slowly to prev...

Embodiment 2

[0055] Add 5Kg of adipic acid dihydrazide into 180L of deionized water, and stir at a low speed of 600 rpm for 5 minutes to completely dissolve it. Add 1.5Kg hydroxyethylcellulose, 25Kg propylene glycol, 4Kg1124 dispersant, 1.5Kg defoamer DX-48, 1.5Kg preservative PROXEL-XL2 and 1.5Kg pH stabilizer AMP-95, and stir at low speed for 5-10 minutes. Under stirring, add 45Kg215 titanium dioxide, 120Kg wollastonite powder, 60Kg kaolin and 120Kg800 mesh heavy calcium, disperse at 1500 rpm for 45-55min at high speed, and detect the fineness to ≤45um. Reduce the rotation speed to 800 rpm, add 120Kg water-based fluorocarbon resin, 100Kg styrene-acrylic emulsion and 250Kg elastic emulsion. After adding one raw material, stir for 5 minutes before adding the next raw material. Finally, add 15Kg of film-forming aid TEXNOL and 2.5Kg of wetting agent X-405, mix 2Kg of 2020 leveling thickener and 6-8Kg of SCT-275 thickener with water in a ratio of 1:1, and adjust the viscosity of the product ...

Embodiment 3

[0057] Add 2.5Kg of adipic acid dihydrazide into 180L of deionized water, and stir at a low speed of 600 rpm for 5 minutes to completely dissolve it. Add 1Kg hydroxyethyl cellulose, 5Kg731A dispersant, 2Kg defoamer DX-46, 1Kg preservative PROXEL-AQ and 2KgpH stabilizer AMP-95, and stir at low speed for 5-10 minutes. Keep stirring, add 55Kg215 titanium dioxide, 150Kg wollastonite powder, 40Kg kaolin and 160Kg800 mesh heavy calcium in sequence, disperse at 1500 rpm for 45-55min at high speed, and detect the fineness to ≤45um. Reduce the rotation speed to 800 rpm, add 100Kg water-based fluorocarbon resin, 60Kg styrene-acrylic emulsion and 250Kg elastic emulsion. After adding one raw material, stir for 5 minutes before adding the next raw material. Finally, add 20Kg film-forming aid lauryl alcohol ester and 2Kg wetting agent X-405, mix 2KgUN-641 associative polyurethane rheology modifier and 6~8Kg963 thickener with water according to the ratio of 1:1, Adjust the viscosity of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an elastic emulsion paint which is prepared from raw materials of deionized water, adipic dihydrazide, hydroxyethylcellulose, propanediol, 215 titanium dioxide, wollastonite powder, kaolin, 800 coarse whiting, waterborne fluorocarbon resin, styrene-acrylic emulsion, elastic emulsion, and the like in dispersive mixing way. With good expansion rate, the elastic emulsion of the invention can be painted in brushing, rolling and spraying way, is provided with breakthrough in stain resistance and hydrophobic property and has the advantages of waterproof and breathable performance, strong anti-pollution performance, alkali and acid resistance and lasting weather resistance.

Description

technical field [0001] The invention relates to an emulsion paint, in particular to an elastic emulsion paint for interior and exterior walls. The invention also relates to a preparation method of the elastic latex paint. Background technique [0002] With the introduction of national energy conservation and environmental protection requirements, the requirements for the thermal insulation performance of building materials are getting higher and higher. There is a large difference between the north and the south of my country. The north is cold in winter and needs to be heated. However, the temperature difference between indoors and outdoors is large. The existing walls cannot effectively prevent the dissipation of heat. It is necessary to increase the supply and demand of heat and increase energy consumption. However, the summer weather in the southern region is relatively hot, which requires a large amount of power consumption to reduce the indoor temperature. Also due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/02C09D127/12C09D125/14
Inventor 姚红星刘爱虎
Owner 山西天时涂料装饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap