Low-hydrogen super diphasic stainless steel electrode

A duplex stainless steel, low hydrogen technology, applied in welding media, welding equipment, welding/cutting media/materials, etc., can solve the problem of difficult ferrite-austenite phase structure ratio, high strength, and difficult manufacturing, etc. problem, to achieve the effect of excellent mechanical properties, good corrosion resistance, excellent pitting resistance

Inactive Publication Date: 2009-02-18
LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, super duplex stainless steel has been widely used in engineering construction in my country, but there is no welding material matching steel in China. Due to the high strength of super duplex stai

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1:

[0024] Marble: 35%; Fluorite: 33%; Titanium Dioxide: 5%; Potash Feldspar: 3%; Soda Ash: 0%; Ferroalloy: Ferrosilicon 2%, Molybdenum Ferro 3%; Metal Powder: Metal Manganese 3%, Metal Chromium 9%, nickel powder 5%; chromium iron nitride: 2%.

Example Embodiment

[0025] Example 2:

[0026] Marble: 40%; Fluorite: 26%; Titanium Dioxide: 3%; Potash Feldspar: 2%; Soda Ash: 1%; Ferroalloy: Ferrosilicon 9%, Molybdenum Ferro 6%; Metal Powder: Metal Manganese 2%, Metal Chromium 6%, nickel powder 4%; chromium iron nitride: 1%.

Example Embodiment

[0027] Example 3:

[0028] Marble: 45%; Fluorite: 20%; Titanium Dioxide: 0%; Potash Feldspar: 5%; Soda Ash: 2%; Ferroalloy: Ferrosilicon 5%, Molybdenum Ferro 5%; Metal Powder: Metal Manganese 4%, Metal Chromium 11%, nickel powder 3%; chromium iron nitride: 0%.

[0029] After mixing the raw materials of the above three coating components uniformly, add pure sodium water glass with a concentration of Pomei in the range of 1.4 to 1.5, and press the welding rod on the welding rod production equipment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-hydrogen type super duplex stainless steel welding rod. The prior duplex stainless steel wire is adopted as a welding core. The coating of the welding rod comprises the compositions in percentage by weight: 35 to 45 percent of marble, 20 to 33 percent of fluorite, 0 to 5 percent of titanium pigment, 2 to 5 percent of potassium feldspar, 0 to 2 percent of sodium carbonate, 5 to 15 percent of iron alloy, 10 to 20 percent of metal powder, and 0 to 2 percent of CrN iron, wherein the iron alloy consists of ferrosilicon and ferromolybdenum under the condition of constant total content, and the metal powder consists of manganese metal, chromium metal, and nickel powder under the condition of the constant total content. After raw materials of the compositions of the coating are mixed evenly, pure sodium water glass with certain Baume concentration is added, and the pressing of the welding rod is performed on welding rod production equipment. The use of the welding rod can satisfy the welding need of super duplex stainless steel in the national engineering construction, the welded welding seam has excellent mechanical property and good corrosion resistance, the tensile strength can reach 800MPa, and the welding rod has good low-temperature toughness.

Description

technical field [0001] The invention belongs to welding material technology, in particular to a low-hydrogen super duplex stainless steel welding rod. Background technique [0002] Super duplex stainless steel has high strength, good toughness, excellent corrosion resistance, especially excellent in chloride stress corrosion resistance and pitting corrosion resistance, and also has excellent welding performance, so it has been widely used in corrosion-resistant pressure vessels and pipelines, Construction of corrosion-resistant structures in large chemical tankers and offshore construction facilities. At present, super duplex stainless steel has been widely used in engineering construction in my country, but there is no welding material matching steel in China. Due to the high strength of super duplex stainless steel welding materials, it is difficult to obtain an appropriate ferrite-austenite phase structure ratio. It is very difficult to control and manufacture, so only a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/365B23K35/40
Inventor 王君民吴伦发王明林
Owner LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap