PVC fine foaming wood-plastic coiled material and method of preparing the same

A wood-plastic coil and micro-foaming technology, which is applied in the field of PVC micro-foamed wood-plastic coil and its production, can solve the problems of high cost, high density, air pollution, etc., to avoid high resin content, reduce costs, The effect of protecting the environment

Inactive Publication Date: 2009-02-18
HUANGSHAN HUASU NEW MATERIAL SCI & TECH CO LTD +1
View PDF0 Cites 86 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional PVC coil is mainly inorganic filler reinforced PVC, which has high PVC content, high density and high cost
[0003] A large amount of waste PVC cable materials and plant fibers are produced in our country every year. Waste plastics are not easy to decompose and produce toxic substances when decomposed; burning waste plant fibers will cause air pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] a) Mixing process: the dried plant fiber and CaCO 3 Mix evenly in a hot mixer, heat up to 90°C, add coupling agent, and mix for 3 minutes, add the remaining materials, mix for 5 minutes, heat up to 120°C, discharge into cold mixing, and cold mix until the temperature is 50°C. ;

[0040] b) Granulation process: feed the uniformly mixed material into an extruder for granulation; the granulator is a conical twin-screw extruder, and its process conditions are: the temperature of the barrel is 120°C, and the screw speed is 30rpm ;

[0041] c) Shaping process: Send the produced particles into the molding machine, pass through a specific thin plate mold, and make a profile through vacuum shaping; the molding machine is a single-screw wood-plastic profile extruder, and the temperature of each zone of the barrel is 120 ° C, 130 ° C ℃, 140℃, 150℃, 165℃, 180℃, flange temperature 185℃, mold temperature 182℃, screw speed 14rpm.

[0042] d) Rolling process: the formed profile is e...

Embodiment 2

[0056] Get the raw material of following weight parts except described PVC micro-foaming wood-plastic roll material:

[0057] 20 copies of old PVC

[0058] 80 pieces of PVC

[0059] 30 mesh wood flour 35 parts

[0060] 35 parts of 15 mesh rice bran

[0061] CaCO 3 10 copies

[0062] Aluminate 1.5 parts

[0063] Calcium zinc heat stabilizer 6 parts

[0064] 3 parts stearic acid

[0065] 7 copies of CPE

[0066] 7 parts epoxy soybean oil

[0067] Foaming agent BTH 1.1 parts

[0068] Titanium dioxide 2 parts

[0069] Outside, all the other are identical with embodiment 1.

Embodiment 3

[0071] Get the raw material of following weight parts except described PVC micro-foaming wood-plastic roll material:

[0072]30 copies of old PVC

[0073] PVC 70 parts

[0074] 30 mesh wood flour 40 parts

[0075] 40 parts of 15 mesh rice bran

[0076] CaCO 3 15 copies

[0077] Aluminate 2.5 parts

[0078] Calcium zinc heat stabilizer 6 parts

[0079] 3 parts stearic acid

[0080] Polyethylene wax 2 parts

[0081] CPE 10 copies

[0082] 7 parts epoxy soybean oil

[0083] Foaming agent BTH 1 part

[0084] Titanium dioxide 2 parts

[0085] Outside, all the other are identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a PVC micro-foaming wood-plastic coiled material, including the following materials by weight portion:100 portions of PVC, 70-80 portions of waste vegetable fibers, 10-30 portions of CaCO3, 1-4 portions of coupling agent, 2-8 portions of heat stabilizer, 3-9 portions of lubricant, 7-12 portions of toughening agent, 3-7 portions of plasticizer, 0.6-1.2 portions of composite foaming agent and 2-3 portions of titanium pigment powder. Compared with the prior art, the composite material prepared by the method has high toughness, the disadvantages of high resin content, little filler and high cost of common PVC coiled materials are avoided. The coiled materials can be used as the coating materials of indoor floor, peripheries and walls with sophisticated shapes.

Description

technical field [0001] The invention belongs to a micro-foamed wood-plastic coil and a production method thereof, in particular to a PVC micro-foamed wood-plastic coil and a production method thereof. Background technique [0002] PVC micro-foamed wood-plastic coil has the advantages of good elasticity, high elongation, small shrinkage, convenient construction, beautiful appearance, good waterproof effect, and long service life. The traditional PVC coil is mainly inorganic filler reinforced PVC, which has high PVC content, high density and high cost. [0003] my country produces a large amount of waste PVC cable materials and plant fibers every year. Waste plastics are not easy to decompose and produce toxic substances when decomposed; waste plant fibers will cause air pollution when burned. Contents of the invention [0004] The first technical problem to be solved by the present invention is to provide a PVC micro-foamed wood-plastic coiled material that uses plant fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08J9/04B29B7/00B29B9/06B29C70/40B29C59/00B29K27/06B29K311/10
Inventor 方玉林巴旭民姚俊王宾
Owner HUANGSHAN HUASU NEW MATERIAL SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap