Composite material of polyetheretherketone/organizing montmorillonite and method of producing the same

A technology of organic montmorillonite and polyether ether ketone, applied in the field of special engineering plastics, can solve the problems of reducing the price of polyether ether ketone, etc., and achieve the effects of low production cost, stable processing performance and good mechanical properties

Inactive Publication Date: 2009-02-18
JILIN UNIV
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research on adding montmorillonite to polyether ether ketone for composite modification has not been reported before. If the excellent properties of montmorillonite can be introduced into polyether ether ketone, it will not only further improve the performance of polyetheretherketone, And you can consider adding a large amount to reduce the price of polyether ether ketone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material of polyetheretherketone/organizing montmorillonite and method of producing the same
  • Composite material of polyetheretherketone/organizing montmorillonite and method of producing the same
  • Composite material of polyetheretherketone/organizing montmorillonite and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1: Preparation of polyether ether ketone / organized montmorillonite composite material

[0025] First prepare organic montmorillonite: 50 grams of sodium montmorillonite is dispersed in 1000 ml of distilled water, stirred, and left to stand for 24 hours; organically modified in a water bath at 40 ° C, adding monooctadecyl trimethyl Ammonium chloride 55.85 g, stirred for 1 hour using an electric stirring paddle; the product was cooled to room temperature, washed with distilled water until AgNO was added dropwise 3 Until the solution does not precipitate; use a high-speed centrifuge to separate the organic montmorillonite from water, then dry it in an oven at 120° C., crush it, and pass it through a 200-mesh sieve to obtain the organic montmorillonite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of special engineering plastics, in particular to a polyether-ether-ketone / organic montmorillonite composite material and a preparation method thereof. Calculated by the mass, the polyether-ether-ketone / organic montmorillonite composite material is prepared by controlling the temperature in all sections of the charging barrel of a double-screw extruder after changing the addition (1 portion to 20 portions) of the organic montmorillonite with 100 portions of polyether-ether-ketone as reference. The polyether-ether-ketone / organic montmorillonite composite material can have properties, such as higher strength, modulus, the same processing window with polyether-ether-ketone, size stability and the like by adding a small amount of organic montmorillonite (1 portion to 10 portions); in addition, because montmorillonite is natural, the resource is rich and the price is low, a large amount of montmorillonite (15 portions to 20 portions) can be added, so as to reduce the cost of the polyether-ether-ketone composite material and not to affect the use properties.

Description

technical field [0001] The invention belongs to the field of special engineering plastics, and specifically relates to a polyether ether ketone / organized montmorillonite composite material and a preparation method thereof. Background technique [0002] Montmorillonite is an inorganic substance, and the composite material compounded with polymer has the following characteristics: only a small amount of montmorillonite (addition amount is 1 to 10 phr, that is, by mass, every 100 parts of polymer is added 1 ~10 parts of montmorillonite) can make the composite material have higher strength, modulus, thermal stability and dimensional stability. Because montmorillonite exists naturally, has abundant resources and is cheap, this composite material has become one of the hot spots in the field of new materials and functional materials in recent years. In 1987, Okada, the central research institute of Japan's Toyota Corporation, first synthesized nylon 6 / montmorillonite nanocomposite...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/00C08K9/04B29C47/92B29C48/40B29C48/92
CPCB29C47/92B29C48/92B29C2948/92704B29C48/40B29C48/9185B29C48/919B29C2948/92895B29C2948/92904
Inventor 王贵宾赵焱张淑玲姜振华任殿福周政吴忠文
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap