UV photo-curing hydrophobic antifouling paint and preparation thereof

An ultraviolet light and hydrophobic technology, applied in the direction of coating, etc., to achieve the effect of good hydrophobic self-cleaning function, simple preparation method, and broad application prospects

Active Publication Date: 2009-02-25
湖州南浔杰辰高分子材料有限公司
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports in this respect in China. The domestic research on the surface properties of UV-cured coatings still focuses on the wear resistance and scratch resistance of the coating film (Xu Guocai, Zhao Shilin. Coating Industry, 2003, 33 (8))

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1: Preparation of hydrophobic stain-resistant coating

[0032] Take by weighing 60 parts of prepolymer bisphenol A epoxy acrylate resin 621A-80 (Changxing Chemical Industry Co., Ltd.); bifunctional monomer: 30 parts of tripropylene glycol diacrylate (Changxing Chemical Industry Co., Ltd.); Trifunctional monomer: 10 parts of trimethylolpropane triacrylate (Sartomer Chemical Co., Ltd.); Initiator: Irgacure184 (Jiangsu Huatai Chemical Co., Ltd.) is 5 parts (accounting for 5% of the active component); use.

[0033] Weigh 0.32 parts of ZonylTA-N (Zhejiang Yuanda Trading Co., Ltd.) and dissolve it in 20 parts of acetone to prepare a solution. Then add 8 parts of untreated nano-silica particles (Zhejiang Hongsheng Science and Technology Materials Co., Ltd.), stir, dry and pulverize, add to the above photosensitive resin, stir evenly, and then disperse the nanoparticles for 30 minutes with a three-roller machine , defoaming, to obtain the UV-cured hydrophobic stain...

Embodiment 2

[0035] Embodiment 2: the preparation of hydrophobic stain-resistant coating

[0036] Weigh 60 parts of prepolymer aliphatic polyurethane diacrylate resin 6514B-80 (Changxing Chemical Industry Co., Ltd.); bifunctional monomer: 30 parts of tripropylene glycol diacrylate; trifunctional monomer: trimethylol 10 parts of propane triacrylate; Initiator: 5 parts of Irgacure 184 (accounting for 5% of the active component); ready for use.

[0037] Weigh 0.32 parts of Zonyl TA-N dissolved in 20 parts of acetone to prepare a solution. Then add 8 parts of untreated nano-silica particles, after stirring, drying and pulverizing, add them to the above-mentioned photosensitive resin, stir evenly and then disperse the nanoparticles for 40 minutes with a three-roll machine, defoaming, and obtain the UV-cured Hydrophobic stain resistant coating.

[0038] The hydrophobic antifouling paint is coated on the glass substrate and cured under the irradiation of 1000W ultraviolet light to form a cured ...

Embodiment 3

[0039] Embodiment 3: the preparation of hydrophobic stain-resistant coating

[0040]Weigh 65 parts of prepolymer aliphatic polyurethane diacrylate resin 6514B-80; bifunctional monomer: 30 parts of adipate diacrylate (HDDA) (Changxing Chemical Industry Co., Ltd.); trifunctional monomer: ethoxy 5 parts of trimethylolpropane triacrylate (Sartomer Chemical Co., Ltd.); Initiator: 10 parts of Irgacure184 (accounting for 10% of the active component); stand-by.

[0041] Weigh 0.8 parts of Zonyl TA-N dissolved in 60 parts of acetone to prepare a solution. Then add 15 parts of untreated nano-silica particles, after stirring, drying and pulverizing, add them to the above-mentioned photosensitive resin, stir evenly, and then disperse the nanoparticles for 50 minutes with a three-roller machine, defoaming, and obtain the UV-cured Hydrophobic stain resistant coating.

[0042] The hydrophobic antifouling paint is coated on the glass substrate and cured under the irradiation of 1000W ultrav...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
contact angleaaaaaaaaaa
contact angleaaaaaaaaaa
surface energyaaaaaaaaaa
Login to view more

Abstract

The invention provides an effective UV-cured hydrophobic contamination-resistant coating and a preparation method thereof. The UV-cured hydrophobic contamination-resistant coating is obtained by adding modified nano-silicon dioxide to photosensitive resin, and dispersing and defoaming the modified nano-silicon dioxide. The modified nano-silicon dioxide accounts for 0.1%-20% of the mass of the photosensitive resin based on the mass of the silicon dioxide; the modified nano-silicon dioxide is made by the following method: nano-silicon dioxide particles are added to an organic solvent in which a surfactant is dissolved, evenly stirred, dried in vacuum and pulverized to obtain the modified nano-silicon dioxide. The coating has the main beneficial effects as follows: the preparation method is simple and easy to be operated, the obtained UV-cured hydrophobic contamination-resistant coating has good hydrophobic self-cleaning function and wide application prospect.

Description

(1) Technical field [0001] The invention relates to an ultraviolet light-cured hydrophobic and antifouling coating and a preparation method thereof. (2) Background technology [0002] Hydrophobic and stain-resistant materials refer to materials with hydrophobic and self-cleaning functions on the surface of the coating film. Due to its unique properties, it has broad application prospects in exterior wall and decorative coatings. [0003] Although there are also many reports and products about surface antifouling. But the main ones are solvent and latex coatings modified by silicone / fluorine (see: JP2007-290377377; JP2000-309749), and another example: Zhang Chaocan uses nano-SiO 2 The tarnish resistance of modified water-based exterior wall coatings (Zhang Chaocan; Tang Xianwen; He Dongming; Xie Minli; Shan Songgao Journal of Wuhan University of Technology, 2003, 10), Jia Zhengfeng introduced MPTMS, MPSAEA and methyl methacrylate copolymerization into the polymer containing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D7/12C09D5/00
Inventor 王德海马国杰
Owner 湖州南浔杰辰高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap