Water-soluble solid polishing wax

A polishing wax and water-soluble technology, which is applied in the field of polishing wax, can solve the problems of increased rate of electroplating defective products, high COD pollution in the environment, and high production costs, so as to simplify post-polishing treatment procedures, reduce COD pollution, and reduce production cost effect

Active Publication Date: 2009-03-25
江门市瑞期精细化学工程有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (1). During the post-treatment process of polishing, the residual wax film is easy to form hard blocks (difficult to emulsify), and the hard blocks are oily substances. Therefore, in the pre-treatment process of electroplating production, a large amount of wax remover is required Only with degreasing agent can the wax film and grease be removed, resulting in higher production costs
[0009] (2). If the wax film and grease are not removed cleanly, the electroplating solution will be seriously polluted, resulting in an increase in the rate of defective products in electroplating and a decrease in production efficiency
[0010] (3). It will cause high COD pollution to the environment and increase the difficulty and cost of wastewater treatment
[0011] This process has been practiced for hundreds of years and has not been improved. Therefore, it has become a factor that has troubled electroplating manufacturers for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1, respectively prepare the following raw materials in total weight percentage: 80% of aluminum oxide, 8% of stearic acid, 4% of animal fat and 8% of polymeric alcohols. The production process is as follows: first dissolve and mix polymerized alcohols with animal fat and stearic acid, then put in alumina, stir evenly, and then shape it. The polishing wax of this embodiment is aimed at the bright polishing of zinc alloy, aluminum alloy, and copper alloy hard surfaces, and its polishing effect is ideal, and it is easy to clean in high-temperature water.

Embodiment 2

[0027] Example 2, respectively prepare the following raw materials in total weight percentage: 65% of aluminum oxide, 15% of silicon carbide, 10% of stearic acid, 4% of animal fat and 6% of polymeric alcohols. The production process is as follows: first dissolve and mix polymerized alcohol with animal fat and stearic acid, then put in alumina and silicon carbide, stir evenly, and then shape it. The polishing wax of this embodiment is aimed at iron materials, has high cutting function, and the effect of fast throwing and automatic throwing is very good, and it is also easy to clean in high-temperature water.

Embodiment 3

[0028] In Example 3, the following raw materials were respectively prepared in the total weight percentage: 70% iron oxide, 15% stearic acid, 5% animal fat and 10% polymeric alcohol. The production process is as follows: first dissolve and mix polymerized alcohol with animal fat and stearic acid, then put in alumina and silicon carbide, stir evenly, and then shape it. The polishing wax of this embodiment is aimed at iron materials, has high cutting function, and the effect of fast throwing and automatic throwing is very good, and it is also easy to clean in high-temperature water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-soluble solid polishing wax which is at least made from a wear particle material, stearic acid, animal oil and polyalcohol substances. The polyalcohol substances which are added for preparing the polishing wax can emulsify and change water solubility and lubricating function, convert water insoluble components into components which can be soluble in water quickly, do not change the characteristics of the original polishing wax and improve the brightness of workpieces, residual waxed film can be dissolved in high temperature water and the application of chemicals such as a wax remover, a deoiling agent and the like can be reduced, thus fulfilling the purpose of reducing the cost, improving the benefit, decreasing COD pollution and realizing 'energy saving, consumption and pollution decrease and efficiency improvement'.

Description

technical field [0001] The invention relates to a polishing wax, in particular to a water-soluble solid polishing wax. Background technique [0002] Polishing refers to the process of leveling the surface of an object with polishing materials, reducing roughness, and improving surface gloss and appearance quality. Polishing wax (also known as polishing wax, polishing paste, polishing rod) is a solid form of polishing material and is widely used in China. It is mainly composed of abrasives and grease, and there are four commonly used ones: [0003] (1). White polishing wax (white oil) is a solid soft block composed of anhydrous, high-purity calcium oxide, a small amount of magnesium oxide, stearic acid, and paraffin. It is suitable for polishing soft metals (aluminum, copper and their alloys, etc.), plastics and bakelite. [0004] (2). Yellow polishing wax is composed of iron oxide, stearic acid, feldspar powder, grease and rosin. It is suitable for rough polishing of gen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09G1/02
Inventor 洪条民
Owner 江门市瑞期精细化学工程有限公司