Unsaturated polyester glass fiber felt plate and production method thereof

A technology of polyester glass fiber and production method, which is applied in the field of glass fiber mat, can solve the problems of inability to produce products with high thickness, high investment cost of process equipment, high requirements for process equipment, etc., and achieve good mechanical strength and excellent mechanical strength. Excellent performance and arc resistance

Active Publication Date: 2009-04-01
河北福润达新材料科技有限责任公司
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The products produced by this method have the characteristics of precise size and easy control of tolerances, but the production efficiency of this method is low, and the requirements for process equipment (such as spraying equipment) are high, and the input cost of process equipment is high, so the production cost is increased. ;The size of the product board is single and the thickness range is narrow, so it is not possible to produce products with higher thickness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Unsaturated polyester glass fiber felt plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) Add 70Kg o-phthalic polyester resin and 25Kg polyvinyl chloride into the paste mixing tank, adjust the speed of the electric high-speed disperser to 800r / min and stir for 2 minutes, and then add 0.5Kg benzoic acid peroxide, 2.3Kg of hydroquinone and 3.2Kg of color paste, stirred at 800r / min for 3 minutes; under low-speed stirring, add 1.5Kg of stearic acid, 8Kg of antimony trioxide, 0.5Kg of the moisturizer produced by BYK Auxiliary Company of Germany, 800r Stir for 3 minutes at / min; then add 120Kg of aluminum hydroxide filler, gradually increase the speed to 900r / min during the addition process, and stir for 6 minutes; add 4.5Kg of magnesium oxide after the filler is evenly stirred, and stir at a high speed of 1000r / min for 3 minutes, At this time, the resin paste is uniform and free of impurities, and the color tone is consistent.

[0045]Spread the resin paste evenly on the upper and lower layers of polyethylene film, with a thickness of 0.40mm, and then spread ...

Embodiment 2

[0049] (1) Add 90Kg o-phthalic polyester resin and 30Kg polyvinyl chloride into the paste mixing tank, adjust the speed of the electric high-speed disperser to 900r / min and stir for 2.5 minutes, and then add 1.4Kg benzoic acid peroxide, 3.8Kg hydroquinone and 4.2Kg color paste, stirred at 900r / min for 3 minutes; under low-speed stirring, 3.5Kg stearic acid, 9Kg antimony trioxide, 0.9Kg moisturizer produced by BYK Auxiliary Company of Germany, 900r / min Stir for 3 minutes at / min; then add 130Kg of aluminum hydroxide filler, gradually increase the speed to 1000r / min during the addition process, and stir for 6 minutes; after the filler is stirred evenly, add 5.5Kg of magnesium oxide, and stir at a high speed of 1200r / min for 3 minutes, At this time, the resin paste is uniform and free of impurities, and the color tone is consistent.

[0050] Scrape the resin paste evenly on the upper and lower layers of polyethylene film, the thickness is 0.45mm, and then spread a layer of polyet...

Embodiment 3

[0054] (1) Add 78Kg o-phthalic polyester resin and 20Kg polyvinyl chloride into the paste mixing tank, adjust the speed of the electric high-speed disperser to 850r / min and stir for 3 minutes, then add 1Kg peroxide benzoic acid, 3Kg Hydroquinone and 2.5Kg color paste, stir for 3 minutes at 850r / min; add 3.5Kg of stearic acid, 9Kg of antimony trioxide, 0.8Kg of moisturizer produced by German BYK Auxiliary Company under low-speed stirring, 850r / min Stir for 3 minutes; then add 130Kg of aluminum hydroxide filler, gradually increase the speed to 1100r / min during the addition process, and stir for 4 minutes; add 4.8Kg of calcium oxide after the filler is evenly stirred, 1200

[0055] Stir at high speed at r / min for 3 minutes. At this time, the resin paste is uniform and free of impurities, and the color tone is consistent.

[0056] Spread the resin paste evenly on the upper and lower layers of polyethylene film, with a thickness of 0.55mm, and then spread a layer of polyethylene fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an unsaturated polyester glass fiber mat board which is obtained by pressing the glass fiber mat immersed with resin paste. The production method thereof comprises: after being stirred evenly, the resin paste is scraped and smeared on a polyethylene film evenly; later a layer of polyethylene film is respectively paved on the upper surface and the lower surface of the glass fiber mat, then a sizing mat is obtained after tight pressing; when the sizing mat is cured, the polyethylene films on the surfaces of the mat are removed; next, the sizing mat is delivered into a press for hot pressing at the temperature of 70 DEG C-145 DEG C and the pressure of 10-20MPa; according to the thickness of the eventually obtained mat board, the mat board with the thickness of each millimeter is hot-pressed for 3-15 minutes; and finally an unsaturated polyester glass fiber mat board is obtained. The unsaturated polyester glass fiber mat board has excellent flame resistance, insulation, electrical and mechanical properties. The production method of the unsaturated polyester glass fiber mat board improves the productivity, reduces the production cost, and can prepare board surfaces with various sizes; and the thickness of the product has large range.

Description

technical field [0001] The invention relates to a glass fiber mat, in particular to an unsaturated polyester glass fiber mat and a production method thereof. Background technique [0002] Unsaturated polyester fiberglass mat has the characteristics of good flame retardancy, good performance and excellent machinability, so it is widely used as insulating structural parts in motors and electrical equipment. At present, it is mainly prepared by molding processes such as pultrusion molding, resin transfer molding molding, and compression molding. In order to improve the electrical properties and flame retardant properties of unsaturated polyester fiberglass mat, a large amount of aluminum hydroxide filler can be added to the unsaturated polyester resin (this filler has good electrical properties, and belongs to the halogen-free green resistance Combustible materials), the resulting resin paste has a high viscosity, so it is not suitable for pultrusion and resin transfer molding...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08K13/04C08K7/14C08K5/13C08K5/14C08K3/22C08K5/02C08K5/08B29C70/40B29L7/00
Inventor 张文波
Owner 河北福润达新材料科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap