Aqueous adhesive for binding rubber and metal and preparation thereof

A metal bonding and adhesive technology, applied in the direction of adhesive types, ester copolymer adhesives, etc., can solve the problems of human and environmental hazards, damage to the atmospheric environment, no patents, etc., to achieve production and use safety, preparation process Simple, wide-ranging effects

Inactive Publication Date: 2009-05-20
GUANGDONG HENGDA NEW MATERIALS TECH
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the domestic adhesives used for rubber and metal bonding are basically solvent-based adhesives, such as neoprene, styrene-butadiene rubber, etc., but there are few types of water-based adhesives used in this area, and there are no related patents, and solvent-based adhesives are easy to use. Flammable and explosive, the volatilized organic solvent is poisonous, destroys the atmospheric environment, and is very dangerous to people and the environment in the process of production and use, and the solvent will easily cause rubber deformation and affect the appearance of rubber corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The parts by weight of each component of the adhesive are as follows:

[0037] Butyl Acrylate 67.3 Styrene 32.5

[0038] Butyl methacrylate 16.5 Acrylic acid 2.34

[0039] Ethyl hydroxymethacrylate 1.1 Methyl methacrylate 10

[0040] Ethoxylated Nonylphenol Sulfosuccinate Half Ester Disodium 3.0

[0041] Sodium Lauryl Sulfate 1.0

[0042] Sodium bicarbonate 0.65 Potassium persulfate 0.65

[0043] Ammonia (25%) 1.45 Antiseptic and fungicide 0.10

[0044] Deionized water 100

[0045] The preparation steps are as follows:

[0046] (1) Dissolve 1 / 2 of the total amount of sodium lauryl sulfate and 2 / 3 of the total amount of ethoxylated nonylphenol sulfosuccinic acid half ester disodium salt in 1 / 4 of the total amount In deionized water, add all the monomers under the stirring of a high-speed emulsifier for stirring and pre-emulsification for about 25 minutes to make a pre-emulsion, and the stirring speed is 800-1000 rpm;

[0047] (2) Three-fifths of the total amount ...

Embodiment 2

[0061] The parts by weight of each component of the adhesive are as follows:

[0062] Butyl Acrylate 52.5 Styrene 35

[0063] Butyl Methacrylate 5.0 Isooctyl Acrylate 10

[0064] Hydroxyethyl Methacrylate 1.2 Methyl Methacrylate 10

[0065] Sodium lauryl sulfate 1.1 Acrylic acid 2.25

[0066] Potassium persulfate 0.70

[0067] Ethoxylated Nonylphenol Sulfosuccinate Half Ester Disodium 3.2

[0068] Antiseptic and bactericide 0.10 Sodium bicarbonate 0.70

[0069] Deionized water 100 Ammonia (25%) 1.45

[0070] The preparation steps are the same as in Example 1.

[0071] Adhesive rubber and metal sample, bonding method and test inspection method are the same as embodiment 1.

[0072] The test results of this embodiment are shown in Table 2:

[0073] Table 2 The test and inspection results of the adhesive bonding rubber and metal prepared in Example 2

[0074] Test item (unit) Adhesion Test Inspection Results Exterior Milky white, uniform without particl...

Embodiment 3

[0076] The weight ratio of each component of the adhesive is as follows:

[0077] Butyl Acrylate 75 Styrene 35

[0078] Butyl Methacrylate 5.0 Isooctyl Acrylate 15

[0079] Hydroxyethyl Methacrylate 1.2 Methyl Methacrylate 5

[0080] Sodium Lauryl Sulfate 1.1 Acrylic Acid 3.0

[0081] Potassium persulfate 0.70

[0082] Ethoxylated Nonylphenol Sulfosuccinate Half Ester Disodium 5.2

[0083] Antiseptic and bactericide 0.10 Sodium bicarbonate 0.70

[0084] Deionized water 100 Ammonia (25%) 1.45

[0085] The preparation steps are the same as in Example 1.

[0086] Adhesive rubber and metal sample, bonding method and test inspection method are the same as embodiment 1.

[0087] The test results of this embodiment are shown in Table 3:

[0088] Table 3 The test and inspection results of the adhesive bonded rubber and metal made by embodiment 3

[0089] Test item (unit) Sample Test Inspection Results Exterior Milky white, uniform without particles PH v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based adhesive used for the bonding between rubber and metal; according to the parts by weight, the adhesive comprises 60-90 parts of soft monomer, 30-60 parts of hard monomer, 2-8 parts of functional monomer, 3-10 parts of emulsifier, 0.4-0.8 part of initiator, 0.6-1.0 part of pH buffer, 100 parts of deionized water or distilled water, 0.05-0.1 part of anticorrosive bactericide, and 1.4-1.6 parts of pH regulator. The invention also discloses a preparation method for preparing the water-based adhesive. The adhesive can replace the existing solvent-typed adhesive, effectively realizes the bonding between the rubber and the metal, has no poison, no combustion and no explosion, is safe and protects the environment. The preparation method which applies the seed latex polymerization has simple preparation process and high production efficiency and is beneficial for the industrial production.

Description

technical field [0001] The invention relates to a water-based adhesive, in particular to a water-based adhesive used for bonding rubber and metal, and belongs to the technical field of adhesives. Background technique [0002] The bonding of rubber to metal is widely used in industry, such as rubber-metal seals, shock absorbers, transmission belt installation, loudspeakers, various decorations and toys, and many other fields. At present, the domestic adhesives used for rubber and metal bonding are basically solvent-based adhesives, such as neoprene, styrene-butadiene rubber, etc., but there are few types of water-based adhesives used in this area, and there are no related patents, and solvent-based adhesives are easy to use. It is flammable and explosive, and the volatilized organic solvents are poisonous and damage the atmospheric environment. There is a great danger to people and the environment in the process of production and use, and solvents can easily cause rubber defo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08
Inventor 陈志方周为民
Owner GUANGDONG HENGDA NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com