Method for preparing hydroxyl acrylic acid water dispersoid

A technology of hydroxyacrylic acid and dispersion, which is applied in coatings, polyurea/polyurethane coatings, etc., and can solve problems such as the difficulty in achieving the performance of solvent-based two-component polyurethane coatings, large particle size of dispersions, and low gloss of coating films. Achieve the effect of small particle size, long pot life and improve comprehensive performance

Inactive Publication Date: 2009-06-17
ZHEJIANG HUANDA PAINT IND GROUP +1
View PDF4 Cites 93 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many domestic patents on the preparation of water-based hydroxyacrylic resins, such as patents CN1557892A, CN1583917A, CN1162964, and CN1230971, all of which are prepared by emulsion polymerization. The particle diameters of these dispersions are relatively large, and the final properties of the coating film such as gloss Low, low hardness of the paint film, poor water resistance of the paint film, etc., it is difficult to achieve the performance of solvent-based two-component polyurethane coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing hydroxyl acrylic acid water dispersoid
  • Method for preparing hydroxyl acrylic acid water dispersoid
  • Method for preparing hydroxyl acrylic acid water dispersoid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041]Firstly, 90 g of propylene glycol methyl ether acetate and 20 g of glycidyl tert-carbonate were added to a reaction kettle equipped with a condensing device and a stirring rod, and the temperature was raised to a reflux temperature of 140° C. while feeding nitrogen. After constant temperature, start to drop the mixed solution composed of non-functional (meth)acrylate, hydroxyl-containing (meth)acrylate, (meth)acrylic acid, vinyl monomer, partial initiator and chain regulator (20 g of methyl methacrylate, 10 g of styrene, 10 g of butyl acrylate, 30 g of hydroxypropyl acrylate, 15 g of acrylic acid, 1 g of dodecyl mercaptan, 4 g of t-amyl peroxyacetate). Control the dropping speed, add the monomer mixture within 2 to 3 hours, keep it for 0.5 to 1 hour, then add a mixed solution of 0.5g initiator and 5g propylene glycol methyl ether acetate, keep warm for 2 to 3 hours, and measure the hydroxyl The conversion rate of the acrylate resin reaches over 98%, and then the temperat...

Embodiment 2

[0049] First put 24g of glycidyl tert-carbonate and 80g of propylene glycol methyl ether acetate into a reaction kettle with a condensing device and a stirring rod, and raise the temperature to 140° C. while blowing nitrogen. After constant temperature, start to drop the mixed solution composed of non-functional (meth)acrylate, hydroxyl-containing (meth)acrylate, (meth)acrylic acid, vinyl monomer, partial initiator and chain regulator (30g methyl methacrylate, 10g styrene, 6g butyl acrylate, 10g hydroxypropyl acrylate, 14g hydroxyethyl methacrylate, 12g acrylic acid, 1g dodecyl mercaptan, 3g tert-amyl peroxyacetate) . The monomer mixture is dropped within 2 to 3 hours, and kept for 0.5 to 1 hour, then a mixed solution of 0.3g of initiator and 4g of propylene glycol methyl ether acetate is added, and the temperature is continued for 2 to 3 hours to measure the hydroxyacrylate resin. The conversion rate reaches over 98%, and then the temperature is lowered to 80° C., and part o...

Embodiment 3

[0054] First, 86g of propylene glycol methyl ether acetate and 20g of glycidyl tert-carbonate were added to a reaction kettle equipped with a condensing device and a stirring rod, and the temperature was raised to 130°C while blowing nitrogen. After constant temperature, start to drop the mixed solution composed of non-functional (meth)acrylate, hydroxyl-containing (meth)acrylate, (meth)acrylic acid, vinyl monomer, partial initiator and chain regulator (Methyl methacrylate 22g, styrene 10g, butyl acrylate 10g, hydroxyethyl methacrylate 32g, methacrylic acid 12g, dodecyl mercaptan 1g, tert-amyl peroxyacetate 3g. Monomer After the mixed solution is dropped within 2 to 3 hours, keep it for 0.5 to 1 hour, then add a mixed solution of 0.3g initiator and 5g propylene glycol methyl ether acetate, continue to keep warm for 2 to 3 hours, and measure the conversion rate of hydroxyacrylate resin reach more than 98%, then lower the temperature to 90°C, evaporate part of the solvent in vac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for the hydroxyl acrylic aqueous dispersion of high performance and two-component waterborne polyurethane, which comprises four steps: synthesizing hydroxyl acrylic resin, removing a solvent, a neutralization salt forming reaction and deionization and aqueous dispersion. The hydroxyl acrylic aqueous dispersion prepared by the invention has proper molecular weight and the molecular weight is distributed much narrower, thus being beneficial for forming a uniform coating, reducing the plasticizing effect of small molecule substance to the coating, and increasing the comprehensive performance of the coating. The dispersion can be combined with an isocyanate curing agent to be used as wood coatings, corrosion protective coatings, industrial maintenance coatings, floor coatings and the like, and also can be used for preparing a two-component waterborne polyurethane adhesive, etc.

Description

(1) Technical field [0001] The invention belongs to the field of chemical coatings, in particular to a method for preparing a hydroxyacrylic water dispersion used for high-performance two-component waterborne polyurethane. (2) Background technology [0002] Acrylic resin has many excellent characteristics such as weather resistance, good chemical stability, high gloss, etc., and is widely used in the field of chemical coatings. In recent years, with the enhancement of people's awareness of environmental protection and the requirement of building a resource-saving society, the use of solvent-based industrial coatings has become more and more strictly restricted. Hydroxyl-containing acrylic acid aqueous dispersion can be used with isocyanate curing agent to prepare water-based two-component polyurethane coatings. Water replaces toxic and harmful organic solvents. It has the advantages of non-toxicity, environmental protection, and energy saving. It has received extensive atten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L33/04C08F220/10C08F220/26C08F2/06C08F8/00C08J3/07C09D175/04
Inventor 刘娅莉余喜红曹银祥刘志平金土才任娜娜李红星
Owner ZHEJIANG HUANDA PAINT IND GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com