Method for preparing antibacterial silver-plating leather

A leather and silver alloy technology, applied in leather surface treatment, special leather manufacturing, small raw hide/large raw hide/leather/fur treatment, etc., can solve the problems of raw leather material performance change, low utilization rate of antibacterial agents, environmental pollution and other problems , to achieve the effect of improving thermal conductivity, saving metal silver materials, and broad-spectrum antibacterial properties

Inactive Publication Date: 2009-12-23
XI'AN POLYTECHNIC UNIVERSITY
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to provide a method for preparing antibacterial silver-plated leather, which solves the problems that the existin...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Preparation of antibacterial silver-coated cowhide

[0027] Put the industrial ethanol into the metal groove, let the lower half of the rotating suede roller contact the industrial ethanol, and the upper half of the rotating suede roller contact the surface of the cowhide. The ethanol adsorbed on the cloth stick removes the surface stains of the cowhide material; the cowhide material after the stain removal is used as the substrate and put into the sputtering chamber, and pure silver is used as the sputtering target material, and the vacuum is pumped to ensure that the vacuum degree in the sputtering chamber is 2×10 -4 Pa, heat the substrate so that the temperature of the leather material is at room temperature, pass in the working gas argon to ensure that the pressure during sputtering is 0.1Pa, adjust the distance between the substrate and the target to 30mm; turn on the sputtering power supply, and perform sputtering coating , the sputtering power is 30W, and the spu...

Embodiment 2

[0030] Preparation of antibacterial silver-plated polyurethane leather

[0031] Put the industrial ethanol into the metal groove, let the lower half of the rotating suede roller contact with the industrial ethanol, and the upper half of the rotating suede roller contact the surface of polyurethane leather. When the polyurethane leather passes through the rotating suede roller, Use the ethanol adsorbed on the suede cloth stick to remove the surface stains of the polyurethane leather material; put the polyurethane leather material after the stain removal as the substrate into the sputtering chamber, and use the silver-nickel alloy with a silver content of 80% as the sputtering target material. Vacuumize to ensure that the vacuum degree in the sputtering chamber is 6×10 -4 Pa, heat the substrate so that the temperature of the leather material is 50°C, pass in the working gas argon to ensure that the pressure during sputtering is 5Pa, adjust the distance between the substrate and ...

Embodiment 3

[0034] Preparation of antibacterial silver-plated PVC leather

[0035] Put the industrial ethanol into the metal groove, let the lower half of the rotating suede roller contact with the industrial ethanol, and the upper half of the rotating suede roller contact the surface of PVC leather, when the PVC leather passes through the rotating suede roller, Use the ethanol adsorbed on the suede cloth stick to remove the surface stains of the PVC leather material; put the PVC leather material after the stain removal as the substrate into the sputtering chamber, and use the silver-aluminum alloy with a silver content of 90% as the sputtering target material. Vacuumize to ensure that the vacuum degree in the sputtering chamber is 4×10 -4 Pa, heat the substrate so that the temperature of the leather material is 40°C, pass in the working gas argon to ensure that the pressure during sputtering is 1Pa, adjust the distance between the substrate and the target to 130mm; turn on the sputtering...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing antibacterial silver-plating leather. The method is characterized in that the adopted sputtering method is magnetron sputtering and/or radio-frequency sputtering method and comprises the following steps of: removing spots on the surface of a leather material; and then putting the leather material as a substrate into a sputtering room, taking metal silver or silver alloy material as a sputtering target material, carrying out sputtering coating by adjusting technique parameters such as the temperature of the substrate and the temperature of the silver target material in the sputtering technique, and obtaining the antibacterial silver-plating leather. The method for preparing antibacterial silver-plating leather has no pollution, does not changethe performance of the raw leather materials and has high antibacterial efficiency.

Description

technical field [0001] The invention belongs to the technical field of leather processing, and in particular relates to a method for preparing antibacterial silver-plated leather. Background technique [0002] Leather materials include genuine leather (cowhide, pigskin, sheepskin) and synthetic leather (polyurethane, polyvinyl chloride), which are usually used as raw materials for clothing, luggage, shoes and other supplies. The current processing methods for genuine leather leather are: grouping and shaping , weighing, pre-soaking, fleshing, main soaking, lime-coating, hair pushing, weighing, liming, second fleshing, shaving board, re-ashing, washing, degreasing, deliming, softening, washing, Pickling, chrome tanning, drum aging, water squeezing, sawdust rolling, smoothing, trimming, weighing, degreasing, washing, retanning, washing, neutralization, color fixing, oiling for dyeing, color fixing, washing, lapping Horse, drying, trimming, dusting, grading. Synthetic leather...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C14C13/00C14C11/00
Inventor 来侃陈美玉孙润军姚穆刘呈坤
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap