Halogen-free environmental protection flame-retardant asphalt for tunnel road surface

A kind of asphalt and environmental protection technology, applied in the direction of roads, roads, building insulation materials, etc., can solve the problems of aggravating the difficulty of escape for rescue and disaster relief personnel, and achieve the effects of ensuring the safety of life and property, improving flame retardancy, and increasing escape time

Inactive Publication Date: 2010-01-13
CHONGQING POFUN TRAFFIC TECH
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large amount of smoke and hydrogen halide gas (HCl or HBr, etc.) produced by halogenated flame retardants during combustion, these toxic and harmful hydrogen halide gases cannot dissipate in the tunnel for a long time, which increases the difficulty of rescue and rescue and personnel escape.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free environmental protection flame-retardant asphalt for tunnel road surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The group allocation ratio is as follows:

[0025] Component mass percentage is (%)

[0026] Zhonghai No. 70 asphalt 91

[0027] SBS modifier 6

[0028] Halogen-free flame retardant 3

[0029] Wherein, the mass percent of each component of flame retardant is:

[0030] Component mass percentage is (%)

[0031] Melamine Phosphonate 50

[0032] Magnesium hydroxide 40

[0033] KH-570 9.5

[0034] Molybdenum trioxide 0.5

[0035] According to the above-mentioned raw material proportioning, prepare according to the following process:

[0036] Step 1: Heat the Zhonghai No. 70 asphalt in the asphalt storage tank to 110°C by circulating heating oil, and dehydrate it at a constant temperature for 50 minutes.

[0037] Step 2: Heat up to 170°C, stir and shear at a speed of 1000r / min, and add SBS modifier at the same time. After the SBS modifier is completely submerged in the asphalt, the stirring speed is increased to 4000r / min, and the constant temperature is sheared for...

Embodiment 2

[0040] The group allocation ratio is as follows:

[0041] Component mass percentage is (%)

[0042] Zhonghai No. 70 asphalt 75

[0043] SBS modifier 5

[0044] Halogen-free flame retardant 20

[0045] Wherein, the mass percent of each component of flame retardant is:

[0046] Component mass percentage is (%)

[0047] Ammonium polyphosphate 75

[0048] Magnesium hydroxide 20

[0049] KH-550 3

[0050] Molybdenum trioxide 2

[0051] The preparation method is the same as in Example 1.

Embodiment 3

[0053] The group allocation ratio is as follows:

[0054] Component mass percentage is (%)

[0055] Zhonghai No. 70 asphalt 60

[0056] SBS modifier 30

[0057] Halogen-free flame retardant 10

[0058] Wherein, the mass percent of each component of flame retardant is:

[0059] Component mass percentage is (%)

[0060] Melamine 60

[0061] Magnesium hydroxide 30

[0062] KH-550 8

[0063] Molybdenum trioxide 2

[0064] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a halogen-free environmental protection flame-retardant asphalt for tunnel road surface, comprising asphalt, a modifier and a flame retardant, wherein the flame retardant is a halogen-free flame retardant, the weight of which is 3% to 20% of total weight of the product, and the flame retardant has the following components in percentage by weight: 50% to 75% of a nitrogen-series flame retardant, 20% to 40% of magnesium hydrate, 3% to 10% of a coupling agent, and 0.5% to 5% of a smoke suppressant. The asphalt does not contain halogen and produce a great deal of smoke and halogen hydride poisonous noxious gas (HCl or HBr, and the like) in combustion process, thereby buying more escape time for human, reducing the difficulty of emergency rescue work and guaranteeing the security of the lives and property to the utmost extent while improving the flame retardance of tunnel asphalt road, reducing the smoke produced with fire and delaying fire behavior.

Description

technical field [0001] The invention relates to an asphalt composition, in particular to a halogen-free environment-friendly flame-retardant asphalt for tunnel pavement. Background technique [0002] With the rapid development of expressways in our country, the number of highway tunnels is also increasing. At present, cement concrete or asphalt is generally used for pavement of most tunnel pavements in China. Compared with cement concrete pavement, asphalt concrete pavement has the characteristics of comfortable driving, low driving noise, good skid resistance and easy maintenance. Therefore, it is a trend that asphalt concrete gradually replaces cement concrete in pavement and bridge pavement. However, asphalt, as an organic mixture, is flammable under certain conditions. Once a vehicle fire occurs, the asphalt pavement will also catch fire or generate thick smoke at the same time, which invisibly increases the difficulty of emergency rescue and personnel escape. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L95/00C08K13/02C08J3/20E01C7/18C08K5/3492C08K3/22C08K3/32
Inventor 陈仕周吴家伟张文汪成夫
Owner CHONGQING POFUN TRAFFIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com