Naphthalene-containing polyetherimide polymer and preparation method thereof

A naphthalene polyetherimide and polymer technology, which is applied in the field of polyetherimide preparation, can solve the problems of low heat resistance level, achieve the effect of improving cost performance, reducing production cost, and improving hydrolysis resistance

Inactive Publication Date: 2011-12-28
JILIN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat resistance level of this type of polyetherimide is not high, and its glass transition temperature is concentrated at 210-290°C. In order to further improve the heat resistance level of polyetherimide without increasing its production cost, we designed A new type of six-membered ring polyetherimide containing naphthalene anhydride, this polymer has a higher glass transition temperature of 280-380°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Naphthalene-containing polyetherimide polymer and preparation method thereof
  • Naphthalene-containing polyetherimide polymer and preparation method thereof
  • Naphthalene-containing polyetherimide polymer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Atmospheric pressure (1.01×10 5 Pa) under, equipped with stirrer, condenser, water trap, thermometer, argon (argon gas is fed from the beginning of the experiment to the end of the experiment. The aforementioned reflux water device refers to the condenser and the separator here. Add 4.69g (0.02mol) 4-chloro-1,8-naphthalene anhydride, 2.00g (0.01mol) 4,4'-diaminodiphenyl ether, 40ml N,N -Dimethylacetamide (DMAc), 10ml of xylene, stirred at room temperature for 1 hour, then started to heat slowly, maintained at 150°C with water for 2 hours, and the system was reddish brown at this time. After the water is completely carried out, xylene is released, and then the temperature of the reaction system is raised to 160°C for 6 hours. After the reaction was completed, the solid was filtered out, then washed twice with acetone and ethanol to remove the residual solvent, and finally the obtained solid was dried in vacuum at 60°C for 5 hours to obtain 3.6 g of golden yellow solid p...

Embodiment 2

[0057] Atmospheric pressure (1.01×10 5 Pa), add 97.7g (0.4mol) 4-chloro-1,8-naphthalene anhydride, 40.0g (0.2 mol) 4,4'-diaminodiphenyl ether, 500ml N,N-dimethylacetamide (DMAc), 70ml xylene, stirred at room temperature for 1 hour, began to heat slowly, and maintained at 150°C with water for 6h, at this time The system is reddish brown. Wait for the water to be completely released, xylene is released, and the temperature is raised to 160°C for 12 hours. After the reaction was completed, the precipitated solid was filtered, then washed twice with acetone and ethanol to remove the residual solvent, and finally the obtained solid was dried in vacuum at 60°C for 15 hours to obtain 81.2 g of golden yellow solid powder, with a yield of 66.0%. (Monomer 1, name: 4,4'-bis(N-phenyl-4-chloro-1,8-naphthalimide) ether), higher than the yield of Example 1.

Embodiment 3

[0059] Atmospheric pressure (1.01×10 5 Pa), add 4.69g (0.02mol) 4-chloro-1,8-naphthalene anhydride, 1.08g (0.01 mol) p-phenylenediamine, 30ml N,N-dimethylacetamide (DMAc), 8ml xylene, stirred at room temperature for 1 hour, started to heat slowly, maintained at 150°C with water for 2 hours, and the system was reddish brown at this time. Wait for the water to be completely released, xylene is released, and the temperature is raised to 160°C for 8 hours. After the reaction was completed, the precipitated solid was filtered, then washed twice with acetone and ethanol to remove the residual solvent, and finally the obtained solid was dried in vacuum at 60° C. for 5 h to obtain 2.7 g of golden yellow solid powder (monomer 2, Name: 4,4'-bis(4-chloro-1,8-naphthalimide)benzene), yield 50.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polyetherimide preparation, and in particular relates to a naphthalene-containing polyetherimide polymer prepared by using a novel dihalogen monomer containing a naphthalene ring and a preparation method of the polymer. Dissolve 4-halo-1,8-naphthalene anhydride and diamine in DMAc, fully carry water in the presence of a water-carrying agent, and then dehydrate at high temperature to prepare a dihalogen monomer containing an imide structure. Using this monomer and bisphenol sodium salt in sulfolane (TMS) as a solvent, under the condition of xylene with water, high-temperature polymerization to synthesize a new type of polyetherimide containing naphthalene structure. The present invention has synthesized a kind of novel polyetherimide containing naphthalene ring structure, and this polyetherimide has higher glass transition temperature, and the introduction of the six-membered ring imide ring containing naphthalene ring structure is also beneficial to The hydrolysis resistance of polyimide materials has been improved to a certain extent. This polymerization method avoids the synthesis of ether-containing dianhydride, and the polymerization solvent sulfolane used can be recycled, which saves production costs.

Description

technical field [0001] The invention belongs to the technical field of polyetherimide preparation, and in particular relates to a naphthalene-containing polyetherimide polymer prepared by using a novel dihalogen monomer containing a naphthalene ring and a preparation method of the polymer. Background technique [0002] Since Staudinger published his famous treatise on polymerization reaction in 1932 and established modern polymer science, polymer science has developed at an astonishing speed. With a preliminary understanding, some polymer chemists began to try to design and synthesize various new polymers from the perspective of molecular design in order to obtain organic polymer materials with excellent properties, which made great progress in the field of polymer materials. As a result, various polyaddition and polycondensation polymers such as polyolefins, polyamides, and polyesters have emerged, and these polymers have been synthesized by various methods and realized ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G65/34
Inventor 党国栋李鹏陈春海周宏伟赵晓刚
Owner JILIN UNIV