Long glass fiber reinforced recycled polypropylene material and preparation method thereof

A technology of long glass fiber and recycled polypropylene, which is applied in the field of reinforcement modification of thermoplastics, and can solve the problem that the interface between polypropylene and glass fiber is not obvious, and it is not suitable for long glass fiber reinforced polypropylene materials, causing pharyngitis and throat Inflammation and bronchitis and other problems, to achieve the effect of environmental protection, improve impregnation effect, improve interface binding force

Inactive Publication Date: 2010-02-03
惠东美化塑胶实业有限公司
View PDF3 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There are some shortcomings in the currently disclosed patents of long glass fiber reinforced polypropylene. For example, in the patent publication number CN 101338051A, the long glass fiber needs to be preheated and dried to make the surface temperature reach 60-80°C, and then the long glass fiber Introduce a surface treatment device to infiltrate the surface with a liquid coupling agent. This method requires additional supporting equipment, complex processes, and increased material costs. Moreover, it has a certain selectivity for the base resin, requiring the use of polypropylene with a medium melt index.
Another example is that in the patent with publication number CN 1810870A, unsaturated carboxylic acids or their anhydrides are directly used in the material formula for preparing long glass fiber reinforced polypropylene. Such substances usually pose a great hazard to human health, and can cause Pharyngitis, laryngitis and bronchitis have a strong irritating effect on human eyes and skin, and there is a danger of burning in case of high heat, which poses a great hidden danger to operators and safe operation; moreover, no coupling agent is used in this formula, The effect of improving the interface adhesion between polypropylene and glass fiber is not obvious
Another example is the use of composite blended yarns of polypropylene fibers and glass fibers in the patent CN1962732A to prepare continuous long glass fiber reinforced polypropylene materials. This method requires high selectivity of raw materials, and it is not suitable for granular or powdery polypropylene. Long glass fiber reinforced polypropylene material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Proportioning is carried out according to the following mass percentage composition: recycled polypropylene 39.2%, silane coupling agent KH5600.5% diluted with ethanol, maleic anhydride grafted polyolefin elastomer POE-g-MAH5%, peroxide diluted with acetone Dicumyl DCP 0.1%, antioxidant 10100.1%, antioxidant 1680.1%, polyethylene wax 3%, stearic acid 1%, color masterbatch 1%.

[0025] When preparing, first add the above materials into a high-speed mixer and stir evenly;

[0026] Then put the mixture into the hopper of the twin-screw extruder. The extruder is divided into six sections from the hopper to the die head. The screw speed of the control host is 280r / min, and the speed of the hopper feeding screw is 30r / min;

[0027] Then add long glass fibers accounting for 50% of the total mass percentage from the mold at the die head of the extruder, fully impregnated with the melt, and stretch to form polypropylene-coated long glass fibers, then cool and pelletize , to pr...

Embodiment 2

[0033] Proportioning is carried out according to the following mass percentage composition: 44.5% of recycled polypropylene pellets, silane coupling agent KH5501% diluted with ethanol, 8% of maleic anhydride grafted polyolefin elastomer POE-g-MAH, diluted with acetone Oxidized dicumyl benzene DCP 0.2%, antioxidant 10100.2%, antioxidant 1680.1%, polyethylene wax 3%, stearic acid 1%, color masterbatch 2%.

[0034] Similar to Example 1, during preparation:

[0035] First, add the above materials into a high-speed mixer and stir evenly;

[0036]Then put the mixture into the hopper of the twin-screw extruder. The extruder is divided into six sections from the hopper to the die head. The screw speed of the control host is 260r / min, and the speed of the hopper feeding screw is 30r / min;

[0037] Add 40% of the total mass percentage of long glass fibers from the mold at the die head of the extruder, fully impregnate with the melt, and stretch to form polypropylene-coated long glass f...

Embodiment 3

[0041] Proportioning is carried out according to the following mass percentage composition: recycled polypropylene 48.8%, silane coupling agent KH5501.2% diluted with ethanol, maleic anhydride grafted polyolefin elastomer POE-g-MAH 8%, diluted with acetone Oxidized dicumyl benzene DCP 0.2%, antioxidant 10100.15%, antioxidant 1680.15%, polyethylene wax 3%, stearic acid 1.5%, color masterbatch 2%.

[0042] Similar to Example 1, during preparation:

[0043] First, add the above materials into a high-speed mixer and stir evenly;

[0044] Then put the mixture into the hopper of the twin-screw extruder. The extruder is divided into six sections from the hopper to the die head. The screw speed of the control host is 320r / min, and the speed of the hopper feeding screw is 31r / min;

[0045] Then add long glass fibers accounting for 35% of the total mass percentage from the mold at the die head of the extruder, fully impregnated with the melt, and stretch to form polypropylene-coated l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses long glass fiber reinforced recycled polypropylene material and a preparation method thereof. The long glass fiber reinforced recycled polypropylene material comprises components according to mass percent: 25-55% of polypropylene, 30-60% of long glass fiber, 0.4-0.8% of coupling agent, 3-8% of graft of thermoplastic elastomer, 0.1-0.3% of fused finger modifier, 0.2-0.4% ofantioxygens, 1-4% of lubricant and 1-3% of selective assistant. The preparation method is as follows: mixing and stirring components except for long glass fiber, and then adding the components exceptfor long glass fiber to a screw extruder; adding long glass fiber, mixing, extruding, cooling, air drying and pelleting; as the fused finger modifier is added, the requirements on polypropylene are reduced; various recycled polypropylene materials can be used as backing material. The preparation method is simple and has low cost; the prepared long glass fiber einforced recycled polypropylene material has good comprehensive performances and can replace a plurality of metal parts to be applied to various fields.

Description

technical field [0001] The invention relates to the reinforcement and modification technology of thermoplastics, in particular to a long glass fiber reinforced recycled polypropylene material and a preparation method thereof. Background technique [0002] The utilization technology of recycled polypropylene is mainly divided into two aspects: physical processing and chemical processing. In terms of chemical processing and utilization technologies, there are mainly: chlorination of polypropylene, cross-linking modification of recycled polypropylene, catalytic cracking and thermal cracking of polypropylene, and other methods. Because there are many technical and equipment limitations in chemical recycling technology, it is generally less used. The most common application is physical processing and utilization, and the most common one is enhancement modification. The traditional method of reinforcement modification is generally realized by adding powders such as calcium carbo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L51/06C08K13/04C08K7/14C08K5/14C08J5/04
Inventor 袁海兵王玉梅
Owner 惠东美化塑胶实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products