Union yarn of terylene fibers, viscose fibers and bamboo fibers, and production method thereof

A viscose fiber, polyester fiber technology, applied in polyester, blended yarn and its production, viscose and bamboo fiber blended yarn and its production field, can solve the problems of difficult dyeing, low moisture absorption, poor air permeability, etc. Overcome the effects of low hygroscopicity, poor alkali resistance and good alkali resistance

Inactive Publication Date: 2010-02-03
NANTONG SUZHONG TEXTILE
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(6) Low hygroscopicity, poor air permeability, and poor dyeability: polyester has a compact structure, high crystallinity, and no hydrophilic gene in the internal macromolecules, so the hygroscopicity is low and dyeing is difficult
[0006] The above three fibers all have their own advantages and disadvantages, and the fabrics made by spinning them alone also have corresponding advantages and disadvantages, so the application field is narrow. At present, there is no relevant blended yarn and its production method. to centralize and eliminate the respective shortcomings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] In the present embodiment, the raw material composition and production method steps of polyester, viscose and bamboo fiber blended yarn are as follows:

[0034] 1. Raw material and weight percentage:

[0035] Polyester fiber 1.4D×38mm, 80% by weight

[0036] Viscose fiber 2D × 51mm, 10% by weight

[0037] Bamboo fiber 5D×51mm, weight percentage 10%

[0038] 2. Production method:

[0039] (1) Flower cleaning: the three mixed raw materials are made into rolls through the flower cleaning machine;

[0040] (2) Carding: the rolls are made into raw sliver through the carding machine;

[0041] (3) Drawing: the raw sliver is merged with the mature sliver through the drawing frame;

[0042] (4) roving: the combined cooked sliver is drawn and thinned to become roving sliver by roving frame;

[0043] (5) Spinning: the roving is drafted into a certain number of yarns through the spinning frame;

[0044] (6) Winding: the spun yarn is wound into a conical cheese through the wi...

Embodiment 2

[0048] In the present embodiment, the raw material composition and production method steps of polyester, viscose and bamboo fiber blended yarn are as follows:

[0049] 1. Raw material and weight percentage:

[0050] Polyester fiber 1.4D×38mm, 75% by weight

[0051] Viscose fiber 2D × 51mm, 15% by weight

[0052] Bamboo fiber 5D × 51mm, weight percentage 10%

[0053] 2, method: same as embodiment 1

[0054] 3. Yarn count: 29.5tex (20S).

Embodiment 3

[0056] In the present embodiment, the raw material composition and production method steps of polyester, viscose and bamboo fiber blended yarn are as follows:

[0057] 1. Raw material and weight percentage:

[0058] Polyester fiber 1.4D×38mm, 85% by weight

[0059] Viscose fiber 2D×51mm, 10% by weight

[0060] Bamboo fiber 5D×51mm, 5% by weight

[0061] 2, method: same as embodiment 1

[0062] 3. Yarn count: 29.5tex (20S).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a union yarn of terylene fibers, viscose fibers and bamboo fibers, and a production method thereof. The union yarn comprises the following components by mass percentage: 78-85%of terylene fibers, 5-15% of viscose fibers and 5-15% of bamboo fibers. Since the union yarn of terylene fibers, viscose fibers and bamboo fibers fully combines the favorable properties of terylene fibers, viscose fibers and bamboo fibers, the respective defects are eliminated. The fabrics made of the union yarn have the advantages of high acid resistance, alkaline resistance, strength, heat resistance, elasticity, wrinkling resistance, wear resistance, hydroscopic property, ventilation property and dyeing property and can resist bacteria, prevent bacteria and resist ultraviolet radiation.

Description

technical field [0001] The invention relates to a blended yarn and a production method thereof, in particular to a polyester, viscose and bamboo fiber blended yarn and a production method thereof, belonging to the field of spinning engineering. Background technique [0002] Polyester fiber, viscose fiber and bamboo fiber are common spinning raw materials, and their characteristics are as follows. [0003] Polyester fiber: (1) acid resistance and alkali resistance; (2) high strength: the strength of polyester fiber is nearly 1 times higher than that of cotton and 3 times higher than that of wool, so polyester fabric is strong and durable; (3) good heat resistance: it can be used in Used at 70-170°C, it has the best heat resistance and thermal stability among synthetic fibers; (4) Good elasticity and good wrinkle resistance: the elasticity of polyester is close to that of wool, and its wrinkle resistance exceeds other fibers. (5) Good wear resistance: The wear resistance of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04
Inventor 黄立勇朱爱民吉维泽杨庆华
Owner NANTONG SUZHONG TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com