Environment-friendly PE gloss black piano lacquer

A piano paint, an environmentally friendly technology, applied in polyester coatings, coatings, etc., can solve the problems of large shrinkage of the paint film, easy brittle cracking, uneven floating of thick wax, poor surface drying, etc., to achieve environmental protection. , Good mechanical properties, not easy to sag

Active Publication Date: 2010-02-24
珠海展辰新材料股份有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, PE wax-containing polishing system is mostly used for surface coating of black piano lacquer. During the actual film formation process, paraffin wax floats on the surface of the paint film, making the surface dull. It must be sanded and polished in multiple passes to obtain a bright coating film. It is not practical for the surface coating of pianos with carvings, grooves, etc. Brittleness and other technical defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A main ingredient formula

[0027] Unsaturated polyester topcoat resin 85 parts

[0028] Modified polyurethane BYK163 0.2 parts

[0029] Carbon black 0.8 parts

[0030] Hexamethoxymethyl melamine resin 5 parts

[0031] 0.6 parts of 12-hydroxystearic acid triglyceride

[0032] Hydroquinone 0.02 parts

[0033] Butanone 0.2 parts

[0034] Styrene 15 parts

[0035] Polydimethylsiloxane, using BYK333 0.4 parts

[0036] B thinner - styrene 100 parts

[0037] C Accelerator: Contains 6% Co 2+ 100 parts of cobalt naphthenate solution

[0038] D initiator: 100 parts of butanone peroxide solution containing active oxygen 10%

[0039] making process:

[0040] In the paint making process, carbon black must be prepared into 6% color paste with unsaturated resin, and sanded to a fineness of less than 15um. Cyanamide resin is dispersed at high speed and ground into a slurry with a fineness of less than 15um and a concentration of 8%; hydroquinone must be dissolved in methyl...

Embodiment 2

[0065] A main ingredient formula:

[0066] Unsaturated polyester topcoat resin 80 parts

[0067] Modified polyurethane BYK163 0.5 parts

[0068] Carbon black 1 part

[0069] Hexamethoxymethyl melamine resin 6 parts

[0070] 0.3 parts of 12-hydroxystearic acid triglyceride

[0071] Hydroquinone 0.04 parts

[0072] Butanone 0.4 parts

[0073] Styrene 17 parts

[0074] Polydimethylsiloxane, using BYK333 0.2 parts

[0075] B thinner - styrene 100 parts

[0076] C Accelerator: Contains 6% Co 2+ 100 parts of cobalt naphthenate solution

[0077] D initiator: 100 parts of butanone peroxide solution containing active oxygen 10%

[0078] During construction, stir and mix the main agent, diluent, accelerator and initiator according to the following weight ratio. Main ingredient: diluent: accelerator: initiator=100: (30-40): (1-1.2): (1.3-1.5). During spraying construction, the surface of the piano can be recoated 2-3 times wet-on-wet.

[0079] Construction methods:

[0080] A...

Embodiment 3

[0101] formula:

[0102] Unsaturated polyester topcoat resin 75 parts

[0103] Modified polyurethane BYK163 0.3 parts

[0104] Carbon black 1.1 parts

[0105] Hexamethoxymethyl melamine resin 4 parts

[0106] 0.5 parts of 12-hydroxystearic acid triglyceride

[0107] Hydroquinone 0.03 parts

[0108] Butanone 0.3 parts

[0109] Styrene 13 parts

[0110] Polydimethylsiloxane, using BYK333 0.3 parts

[0111] Thinner - styrene 100 parts

[0112] Accelerator: Contains 6% Co 2+ 100 parts of cobalt naphthenate solution

[0113] Initiator: 100 parts of butanone peroxide solution containing active oxygen 10%

[0114] Preparation process: with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
tack-free timeaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly PE gloss black piano lacquer, which comprises a main agent, a diluting agent, an accelerating agent and an initiator, wherein the main agent mainly comprises the following components in portion by weight: 75 to 85 portions of unsaturated polyester finishing paint resin, 0.2 to 0.5 portion of wetting dispersing agent, 0.8 to 1.1 portions of carbon black, 4 to 6 portions of hexamethoxymethyl melamine resin, 0.3 to 0.6 portion of anti-sagging agent, 0.02 to 0.04 portion of polymerization inhibitor, 0.2 to 0.4 portion of butanone, 13 to 17 portions of styrene, and 0.2 to 0.4 portion of levelling agent; the diluting agent mainly comprises 100 portions of the styrene; the accelerating agent contains 100 portions of cobalt naphthenate solution with6 percent of Co<2+>; and the initiator contains 100 portions of butanone peroxide solution with 10 percent of active oxygen. The environment-friendly PE gloss black piano lacquer can obtain a bright film coating without polishing, has better mechanical properties and fullness, is difficult to have cooling cracks, can solve the problem of northward transportation of south musical instruments, and simultaneously completely uses active diluting agent and is very favorable for environmental protection.

Description

technical field [0001] The invention relates to the field of unsaturated polyester paint, in particular to an environment-friendly polyester piano paint. Background technique [0002] At present, PE wax-containing polishing system is mostly used for surface coating of black piano lacquer. During the actual film formation process, paraffin wax floats on the surface of the paint film, making the surface dull. It must be sanded and polished in multiple passes to obtain a bright coating film. It is not practical for the surface coating of pianos with carvings, grooves, etc. Technical defects such as brittleness. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a PE glossy black piano lacquer for piano surface coating, which can obtain good mechanical properties, easy construction and excellent fullness without polishing. [0004] The technical scheme that the present invention solves the problems of the technologies...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06
Inventor 陈寿生
Owner 珠海展辰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com