Active carbon desulfurizer and preparation method thereof

A desulfurizer and activated carbon technology, which is applied in catalyst activation/preparation, chemical instruments and methods, and other chemical processes, etc., can solve the problems of the decrease of the specific surface area and pore volume of the activated carbon desulfurizer, and the reduction of the desulfurization speed and sulfur capacity. The effect of developed pore system, low production cost and high activity

Active Publication Date: 2010-03-10
一重集团大连工程建设有限公司
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above-mentioned prior art all adopts the impregnation method to impregnate the metal salt on the activated carbon. The disadvantage of this method is that the micropores of the activated carbon are reduced, thereby reducing the specific surface area and pore volume of the activated carbon desulfurizer, and reducing the desulfurization speed and sulfur content. Allow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The preparation method of activated carbon desulfurizer includes the following sequence and steps:

[0028] a. Take 2-5% copper oxide or 5-10% basic copper carbonate and 55-65% coal powder or charcoal powder and mix well with 5-13% water;

[0029] b. Add 20-30% tar, roll it, roll it evenly and extrude it into a strip, and dry it at room temperature;

[0030] c. Carbonize the dried carbon strips in a carbonization furnace at 450°C for 40 minutes;

[0031] d. Then it is activated with water vapor in an activation furnace at an activation temperature of 850°C and an activation time of 180 minutes to prepare a copper oxide activated carbon desulfurizer.

Embodiment 1

[0033] a. Take 5Kg of copper oxide and 65Kg of pulverized coal and mix it evenly with 13Kg of water:

[0034] b. Add 30Kg of tar, roll it, roll it evenly and extrude it into a strip, and dry it at room temperature;

[0035] c. Carbonize the dried carbon strips in a carbonization furnace at 450°C for 40 minutes;

[0036] d. Then it is activated with water vapor in an activation furnace at an activation temperature of 850°C and an activation time of 180 minutes to prepare a copper oxide activated carbon desulfurizer.

Embodiment 2

[0038] a. Take 2Kg of copper oxide and 55Kg of charcoal powder and mix it evenly with 5Kg of water:

[0039] b. Add 20Kg of tar, roll it, roll it evenly, extrude it into a strip, and dry it at room temperature;

[0040] c. Carbonize the dried carbon strips in a carbonization furnace at 450°C for 40 minutes;

[0041] d. Then it is activated with water vapor in an activation furnace at an activation temperature of 850°C and an activation time of 180 minutes to prepare a copper oxide activated carbon desulfurizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to an active carbon desulfurizer prepared by a kneading method and a preparation method thereof. The preparation method comprises the following steps: evenly mixing copper oxideor basic cupric carbonate and pulverized coal or charcoal powder with a certain quantity of water, then adding tar and rolling evenly, and then extruding bands to mold, drying and activating to prepare the active carbon desulfurizer for loading the copper oxide. Holes of the active carbon desulfurizer prepared by the kneading method are more than that of the active carbon desulfurizer prepared bya dipping method; the specific surface area of the active carbon desulfurizer is larger than 1,000<2> / g; the active carbon desulfurizer loading CuO and prepared by a kneading method is not only suitable for desulfuration in petrochemical industry, but also suitable for desulfuration of water gas; and when used for desulfuration of water gas, the active carbon desulfurizer not only has high activity, but also achieves over 30 percent of working sulfur capacity and has the advantages of regeneration, strong water resisting property, no argillization, low production cost and simple process.

Description

Technical field: [0001] The invention relates to a catalyst in petrochemical technology, in particular to a mixing method for preparing activated carbon desulfurizer and a method thereof Background technique: [0002] Activated carbon desulfurizer is one of the first dry desulfurizers used, and has been used for more than 70 years. Earlier activated carbon desulfurization technology equipment was huge, the regeneration and sulfur recovery process was complicated, and the operation was troublesome. It was gradually replaced by wet methods in the 1950s. In recent years, due to the improvement and simplification of regeneration methods, activated carbon desulfurizers for fine desulfurization and normal temperature fine desulfurization technology have been developed. Many medium and small synthetic ammonia plants, urea plants, and co-alcohol production plants use activated carbon desulfurizers for dry desulfurization. Hydrogen sulfide and some organic sulfur in the feed gas. This ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/236B01J23/72B01J21/18B01J37/04B01J20/20C10K1/34
Inventor 陆久民阎富山赵伟
Owner 一重集团大连工程建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products