Anti-incrustation corrosion inhibitor for circulating water system with high concentration time and high chloride ion content

A technology of circulating water system and scale and corrosion inhibitor, which is applied in the field of scale and corrosion inhibitor, can solve the problems of increased chloride ion concentration, difficult to achieve the expected effect of the artificial corrosion effect, etc., and achieves reduced dosage and good corrosion inhibition effect. , the effect of slowing down the corrosion rate

Inactive Publication Date: 2010-06-30
上海淼清水处理有限公司
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the circulating water system operating at a high concentration multiple, due to the drop in pH and the increase in the concentration of chlo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 15g PBTC (2-phosphonobutane-1,2,4 tricarboxylic acid), 10g DTPMP (diethylenetriaminepentamethylenephosphonic acid), 2gPAPE (polyol phosphonate), 5g methylbenzene Mix triazole and add pure water to dilute to 50g, prepare scale and corrosion inhibitor A, mix 45g acrylic acid / acrylic acid ester / acrylic acid-2-acrylamide-2-methylpropanesulfonic acid / phosphonic acid tetrapolymer with 15g After mixing zinc sulfate heptahydrate, add water to dilute to 50g, and prepare scale and corrosion inhibitor B. When in use, A and B are used as scale and corrosion inhibitors and added to circulating water at the same time.

Embodiment 2

[0031] Mix 10PBTC (2-phosphonobutane-1,2,4 tricarboxylic acid), 5g polyamino polyether phosphonate, 5g HPAA (hydroxyphosphine acetic acid), 4g tolyltriazole Scale and corrosion inhibitor A, mix 40g of phosphine-terminated acrylic acid / acrylic acid-2-acrylamide-2-methylpropanesulfonic acid / maleic anhydride copolymer with 5g of zinc chloride, add water to dilute to 50g, and prepare scale inhibitor etchant B. When in use, A and B are used as scale and corrosion inhibitors and added to circulating water at the same time.

Embodiment 3

[0033]Mix 15g PBTC, 2g trisodium phosphate, 6g polyamine polyether phosphonate, 5g methyl benzotriazole and dilute to 50g with water to prepare scale and corrosion inhibitor A, mix 60g acrylic acid / allylsulfonic acid / mass Toic anhydride terpolymer is mixed with 5g of zinc and then diluted to 50g with water to prepare scale and corrosion inhibitor B. A and B are used as scale and corrosion inhibitors and added to circulating water at the same time.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Corrosion rateaaaaaaaaaa
Login to view more

Abstract

The invention relates to an anti-incrustation corrosion inhibitor for a circulating water system with a high concentration time and a high chloride ion content. The anti-incrustation corrosion inhibitor comprises the following components in parts by weight: 1-100 parts of phosphoric acid and salt thereof, 1-500 parts of organic phosphonic acid and salt thereof, 5-1,000 parts of acrylic copolymer, 1-20 parts of zinc salt, 10-200 parts of anode corrosion inhibitor and 0.5-5 parts of imidazoline non-ferrous metal corrosion inhibitor. Compared with the prior art, the invention can effectively suppress under-deposit corrosion and point corrosion caused by low pH value and high chloride ion content.

Description

technical field [0001] The invention relates to a new material, in particular to a scale and corrosion inhibitor used in a circulating water system with high concentration ratio and high chloride ion content. Background technique [0002] In recent years, with the development of my country's industry and the increase of population, the shortage of water resources has become more and more serious, which has become the main factor restricting the development of some areas. [0003] One of the reasons for water shortage is that the development of industry makes the consumption of industrial water surge. Industrial water consumes a lot of water and is used intensively, so it has huge saving potential. For example, in the petrochemical industry, water consumption as equipment cooling medium accounts for about 60% of the total industrial water consumption. The recycling of cooling water can effectively improve the recycling rate of water, greatly save water and reduce sewage dis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/08
Inventor 季淑浥蒋毅章
Owner 上海淼清水处理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap