Hard polrvinyl chloride product and preparation method thereof

A rigid polyvinyl chloride and polyvinyl chloride technology, which is applied in the field of polyvinyl chloride materials and their preparation, can solve the problems that affect the appearance performance of polyvinyl chloride decorative materials, the refractive index of polyvinyl chloride is very different, and the decorative objects cannot be used. effect and other issues, to achieve the effect of improving flow performance, good appearance performance, and blocking penetration

Active Publication Date: 2010-08-04
ANHUI TIANAN NEW MATERIAL CO LTD
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Analyzing its reason, those skilled in the art find that other groups such as ester group, hydroxyl etc. are contained in the material used in the existing rigid polyvinyl chloride decoration material formula, and these groups are very easy to react with water, and its The refractive index of the reaction product is very different from that of polyvinyl chloride, which causes the product to become whitish and foggy. Even if it is made into a film or sheet, it cannot completely prevent the occurrence of this reaction, thus causing whitening of sensitive water. phenomenon, which greatly affects the appearance and performance of PVC decorative materials, and cannot achieve the effect of decorating the surface of objects, and this situation is particularly prominent on black plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hard polrvinyl chloride product and preparation method thereof
  • Hard polrvinyl chloride product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1. The preparation of rigid polyvinyl chloride product 1

[0045] Such as figure 1 As shown, the preparation method of the rigid polyvinyl chloride product of the present invention includes a high-speed stirring and mixing process, a low-speed stirring and cooling process, a planetary multi-screw extrusion process, a single-screw extrusion and filtration process, a calendering process, and a liquid cooling tank. Chilling process, annealing heat preservation and warming process, cooling process and finished product coiling process; its special feature is that in this embodiment, each component of the rigid polyvinyl chloride product and the component content in parts by mass are shown in the table 1 shows:

[0046] Components and content (parts by mass) of the rigid polyvinyl chloride product of Table 1 Example 1

[0047] Polyvinyl chloride (PVC) 100 parts,

[0048] Mercaptan organotin 1.6 parts,

[0049] Acrylic ester internal lubricant 0.6 part,

[0050...

Embodiment 2

[0055] Embodiment 2. Preparation 2 of rigid polyvinyl chloride products

[0056] Component and content (parts by mass) of the PVC bottom film of table 2 embodiment 2

[0057] Polyvinyl chloride (PVC) 100 parts,

[0058] Mercaptan organotin 1.8 parts,

[0059] Acrylic ester internal lubricant 0.8 parts,

[0060] Acrylic external lubricant 0.3 parts,

[0061] 10 parts of methyl methacrylate-butadiene-styrene copolymer,

[0062] Hydroxy-terminated linear reactive siloxane 0.3 parts

[0063] Rutile titanium dioxide 8.0 parts

[0064] Ultramarine EP-19 0.018 parts

[0065] According to the components and contents in Table 2, the rigid polyvinyl chloride product produced by the method in Example 1, because no plasticizer is needed, and the hydroxyl-terminated linear reactive silicone containing hydrophobic group is added Alkanes can significantly block the erosion of water molecules on the film, and better solve the problem of water-sensitive whitening on the surface of plast...

Embodiment 3

[0066] Embodiment 3. Preparation 3 of rigid polyvinyl chloride products

[0067] Component and content (parts by mass) of the PVC bottom film of table 3 embodiment 3

[0068] Polyvinyl chloride (PVC) 100 parts,

[0069] Mercaptan organotin 2.2 parts,

[0070] 1.0 part of acrylic internal lubricant,

[0071] 0.5 parts of acrylic external lubricant,

[0072] 14 parts of methyl methacrylate-butadiene-styrene copolymer,

[0073] Fluorine resin 0.5 parts

[0074] Rutile titanium dioxide 1.0 parts

[0075] P.V.19 red pigment 4.0 parts

[0076] P.R.122 red pigment 0.9 parts

[0077] According to the components and contents in Table 3, the rigid polyvinyl chloride products produced by the method in Example 1 can significantly block water due to the addition of plasticizers and the addition of fluororesins containing hydrophobic groups. The erosion effect of molecules on the film can better solve the problem of water-sensitive and whitening of the surface of plastic products. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hard polrvinyl chloride product, which contains the following components in parts by weight: 100 parts of polrvinyl chloride, 1.6-2.2 parts of organotin thiol, 0.6-1.0 part of internal lubricant, 0.2-0.5 part of external lubricant, 6-14 parts of impact-resistant modifier, 0.2-0.5 part of waterproof modifier, and proper amount of pigment is added. The invention also discloses a preparation method of the hard polrvinyl chloride product. The formula of the hard polrvinyl chloride product does not add any plasticizer, thus avoiding the phenomenon that the surface of the polrvinyl chloride product is water-sensitive and becomes white due to the influence of ester group of the plasticizer. In addition, the formula of the hard polrvinyl chloride product adds the waterproof modifier containing hydrophobic group, thus obviously improving the solvent resistance and the impermeability of the polrvinyl chloride product, effectively isolating the corrosion of external water or steam, protecting the surface of the polrvinyl chloride product, and leading the polrvinyl chloride product to have good appearance performance.

Description

technical field [0001] The invention relates to a polyvinyl chloride (PVC) material and a preparation method thereof, in particular to a rigid polyvinyl chloride product and a preparation method thereof. Background technique [0002] In daily life, it is often necessary to add decorative materials on the surface of the object to meet people's pursuit of the appearance of the object, and at the same time, it can also play a certain protective role. Among them, for high-gloss decorative materials, due to their high requirements on surface color and appearance, the colored decorative materials disclosed in the prior art generally have the problem of water-sensitive whitening, that is, those prepared by the prior art The rigid polyvinyl chloride decorative materials (including films and sheets, etc.), after being made into finished products, will more or less form a white mark on the surface of the film after encountering water vapor or soaking in water. It greatly affects the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L27/12C08L33/04C08K5/58
Inventor 吴启超丰俊湘贺光明
Owner ANHUI TIANAN NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com