Formula of soles of PU-simulated foaming sneakers through injection and manufacturing method

A manufacturing method and technology of sports shoes, applied in soles, footwear, applications, etc., can solve the problems of short life, high density, no anti-slip performance, etc., and achieve the effect of low cost, high elasticity, and good anti-slip

Inactive Publication Date: 2010-08-18
泰亚投资集团有限公司
View PDF4 Cites 54 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of anti-skid, low density and long life-span PU imitation PU shoe sole which has no anti-slip performance, high density and short lifespan. Sole formula and manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula of soles of PU-simulated foaming sneakers through injection and manufacturing method
  • Formula of soles of PU-simulated foaming sneakers through injection and manufacturing method
  • Formula of soles of PU-simulated foaming sneakers through injection and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation method of the injection imitation PU foamed sports shoe sole mainly includes the following steps:

[0029] 1) Pound material

[0030] Weigh the raw materials according to the designed formula, bag the bridging agent and high temperature foaming agent separately, and mix the other materials together.

[0031] 2) Tantra

[0032] Pour the prepared raw materials into a 75-liter internal mixer, except for DCP and AC-6000H, start the internal mixing and mixing to make the materials evenly mixed. The banburying time of the first stage is 7-8 minutes, and the frequency of turning is 4-5 times. When the temperature reaches 110°C-112°C, add DCP and AC-6000H and start the internal mixing process again. The second stage of banburying time is 2-3 minutes, and the number of turning materials is 2-3 times, until the temperature continues to rise to 115°C-118°C, all the raw materials have been mixed uniformly, and the materials are poured out for smelting.

[0033] 3) Open ref...

Embodiment 1

[0048] Example 1: It is an experimental formula designed according to the traditional way of thinking, and its dosage is a sample developed and measured in grams.

[0049] Table 2

[0050]

[0051]

Embodiment 2

[0052] Example 2: Similar to Example 1, the difference is that the raw material formula is shown in Table 3.

[0053] table 3

[0054]

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a formula of soles of PU-simulated foaming sneakers through injection, which comprises the following raw materials in percentage by mass: 40 percent of 21 percent ethylene-vinyl acetate copolymer (EVA 7360), 16.7 percent of styrene butadiene copolymer SBBSJT-83, 12.5 percent of ethylene octylene copolymer POE8130, 8.3 percent of ethylene-propylene-diene copolymer 3745P, 65.9 percent of wear-resisting agent A-18, 8.3 percent of talcpowder, 0.25 percent of stearic acid, 0.42 percent of zinc stearate, 0.9 percent of zinc oxide, 0.08 percent of bridging auxiliary agent ET-102, 0.75 percent of bridging agent DCP, 1.7 percent of high-temperature foaming agent AC-6000H, 2.5 percent of titanium white powder R-103 and 1.7 percent of master batch. The preparation method comprises the steps of banburying, mixing, granulation, injection molding, physical property tests and the like. Thus, in the research and development and application, the PU-simulated foaming soles not only have the physical and chemical properties of no crease marks, high elasticity, low compression and wear resistance of PU soles, and but also have the advantages of low production cost, light specific gravity, good limited-slip properties, no hydrolysis and long service life.

Description

Technical field [0001] The invention relates to a special sports shoe sole, in particular to a foam sole formula with PU texture, anti-slip and long service life, and a manufacturing method thereof. Background technique [0002] China is the world's largest producer and exporter of footwear, with all kinds of footwear materials, among which polyurethane PU soles are all the rage. Its good wear resistance, good elasticity, strong folding resistance and unique texture have been praised and recognized by many consumers; but its high unit price, high density, non-slip, easy to hydrolyze and short service life, these shortcomings have made PU in the market The market share is getting less and less. Therefore, it is the direction and inevitable trend of shoe material development to improve these shortcomings of PU material and find and develop its substitutes. Sports have entered each of our lives, and sports shoes have also been used in every environment where humans live, especiall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L53/02C08L23/20C08L23/16C08K13/02C08K3/34C08K5/09C08K5/098C08K3/22A43B13/04
Inventor 林松柏
Owner 泰亚投资集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com