High-temperature resistance oil product oxidization resistance paint and preparation method thereof

An anti-oxidative coating and high-temperature resistant technology, applied in anti-corrosion coatings, fire-retardant coatings, coatings, etc., can solve problems such as environmental pollution and machine oil waste, and achieve long service life, good weather resistance, and anti-oxidation effects.

Inactive Publication Date: 2010-08-18
SHANGHAI EXCILON NEW MATERIALS
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This not only causes a waste of machine tool oil, but

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0029] Antioxidant coating of the present invention, can constitute according to following formula:

[0030] Composition Weight

[0031] Water-dispersed nano-scale alumina 350kg

[0032] Pigment 100kg

[0033] Packing 95kg

[0034] Potassium titanate whiskers 65kg

[0035] Nano silver particles 10kg

[0036] Methyltrimethoxysilane 320kg

[0037] Methyltriethoxysilane 60kg

[0038] These components add up to a total of 1000 kg.

[0039] The particle size of the alumina in the water-dispersed nano-scale alumina can be selected to be 20 nanometers.

[0040] The pigment therein may be iron oxide black. The anti-oxidation coating obtained in this way has a metallic black color.

[0041] The filler therein can be optional silicon dioxide whiskers. The whiskers have strong dispersibility, which helps to achieve the purpose of uniform mixing in the paint. On the other hand, because of the strength of the whiskers themselves, it is beneficial to strengthen the cohesion of the...

specific Embodiment 2

[0044] Antioxidant paint of the present invention can also be made up according to following formula:

[0045] Composition Weight

[0046] Water-dispersed nano-alumina 390kg

[0047] Pigment 90kg

[0048] Packing 70kg

[0049] Potassium titanate whiskers 50kg

[0050] Nano silver particles 10kg

[0051] Methyltrimethoxysilane 340kg

[0052] Methyltriethoxysilane 50kg

[0053] These components add up to a total of 1000 kg.

[0054] The particle size of the alumina in the water-dispersed nano-scale alumina can be selected to be 15 nanometers.

[0055] The pigment, in this embodiment, can be silica fume powder, which makes the anti-oxidation coating appear taupe, and the effect of dirt resistance and dust resistance is very good.

[0056] The filler therein may be nanoscale precipitated barium sulfate. The particle size of the barium sulfate can be selected to be between 10-100 nanometers.

[0057] The potassium titanate whiskers may be potassium tetratitanate whiskers....

specific Embodiment 3

[0058] An anti-oxidation coating can also be made according to the following formula:

[0059] Composition Weight

[0060] Water-dispersed nano-scale alumina 320kg

[0061] Pigment 110kg

[0062] Packing 80kg

[0063] Potassium titanate whiskers 80kg

[0064] Nano silver particles 40kg

[0065] Methyltrimethoxysilane 260kg

[0066] Methyltrichlorosilane 40kg

[0067] Phenyltrimethoxysilane 20kg

[0068] Methyltriethoxysilane 50kg

[0069] Together it is 1000kg.

[0070] The particle size of the alumina in the water-dispersed nano-scale alumina can be selected to be 25 nanometers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention provides high-temperature resistance oil product oxidization resistance paint and a preparation method thereof, which belong to the field of functional paint particularly applied to the aspect of oil product oxidation resistance under the condition of high temperature. Major ingredients of the paint comprise water-dispersible nanometer aluminum oxide, pigment, filling materials, potassium titanate whiskers, nanometer silver grains and one or two kinds of materials in methyltrimethoxysilane and methyl triethoxysilane. A coating layer prepared by the invention has the quality of the enamel surface, has advantages of fire resistance, high temperature resistance, high rigidity, high compactness and good weather resistance, and is completely harmless to human bodies. In addition, the invention can be used for effectively slowing down the oil product oxidation process. The edible oil can still maintain the nutritive and health quality through being placed in a high-temperature environment for a long time. The service life of the industrial oil can be prolonged.

Description

technical field [0001] The invention belongs to the field of functional coatings, and is particularly applied to the oxidation resistance of oil products under high temperature conditions. Background technique [0002] Various oil materials are widely used in industrial and agricultural production and daily life. From the perspective of edibility, it is divided into two types: edible oil and non-edible oil. Both of them may cause serious oxidation under high temperature environment. [0003] For example, when edible oil is used in an ordinary pot, the oil will react with oxygen in the air at high temperature to form peroxides, or form high polymers through dimers, resulting in an increase in the viscosity of the oil; In cooking oil with high concentration, a large number of fine and unbreakable air bubbles will be produced, and harmful cyclic polymers will be formed in the process. At the same time, the increase of oil viscosity will greatly reduce the heat conduction effi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D1/00C09D5/08C09D5/18
Inventor 李力锋
Owner SHANGHAI EXCILON NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap