ABS (Acrylonitrile Butadiene Styrene) modified material with high heat resistance, high gloss and flame retardance and preparation method thereof

A modified material, high gloss technology, applied in the field of high heat resistance, ABS modified material, high gloss, flame retardant ABS modified material and its preparation field, can solve the problem of high heat resistance surface gloss and high gloss of ABS modified material. The flame retardant properties cannot be coordinated, and the scope of use of ABS modified materials is limited, so as to achieve the effect of expanding the scope of use, good flame retardant efficiency and high flame retardant efficiency.

Inactive Publication Date: 2010-11-03
SHENZHEN KEJU NEW MATERIAL
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be known from the above that the current ABS modified materials cannot be coordinated among high heat resistance, good surface gloss and flame retardancy, which limits the scope of use of ABS modified materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1, the parts by weight of selected raw materials are: 75.8 parts of ABS, 5 parts of SAN, 13 parts of flame retardant (compound mixture of tribromophenoxytriazine and antimony trioxide), heat resistant agent (N-benzene grafted maleimide) 5 parts, compatibilizer (copolymer of styrene, acrylonitrile and maleic anhydride) 1 part, antioxidant (hindered phenolic antioxidant and phosphite antioxidant compound mixture) 0.1 part, lubricant (N, N'-ethylene bisstearamide) 0.1 part. Wherein, the mass percent content of the component butadiene of ABS is 40%; The mass ratio of tribromophenoxytriazine and antimony trioxide is 3: 1, and the graft rate of maleic anhydride is 6%, hindered The mass ratio of phenolic antioxidant and phosphite antioxidant is 1:0.5.

[0048] Preparation method: Weigh the above raw materials, first mix ABS, SAN and lubricant evenly, then add other raw materials into the high mixer, stir and mix for 2 minutes; put the mixed raw materials in a twin-...

Embodiment 2

[0049] Embodiment 2, the parts by weight of selected raw materials are: 62.6 parts of ABS, 11 parts of SAN, 15 parts of flame retardant (compound mixture of tribromophenoxytriazine and antimony trioxide), heat resistant agent (N-benzene grafted maleimide) 8 parts, compatibilizer (copolymer of styrene, acrylonitrile and maleic anhydride) 3 parts, antioxidant (hindered phenolic antioxidant and phosphite antioxidant compound mixture) 0.2 parts, lubricant (N, N'-ethylene bisstearamide) 0.2 parts. Wherein, the mass percent content of the component butadiene of ABS is 50%; The mass ratio of tribromophenoxytriazine and antimony trioxide is 3: 1, and the graft rate of maleic anhydride is 20%, hindered The mass ratio of phenolic antioxidant and phosphite antioxidant is 1:1.

[0050] Preparation method: Weigh the above raw materials, first mix ABS, SAN and lubricant evenly, then add other raw materials into the high mixer, stir and mix for 5 minutes; put the mixed raw materials in a tw...

Embodiment 3

[0051] Embodiment 3, the parts by weight of selected raw materials are: 48.4 parts of ABS, 17 parts of SAN, 18 parts of flame retardant (compound mixture of tribromophenoxytriazine and antimony trioxide), heat resistant agent (N -Phenyl grafted maleimide) 11 parts, compatibilizer (styrene, acrylonitrile and maleic anhydride copolymer) 5 parts, antioxidant (hindered phenolic antioxidant and phosphite antioxidant Oxygen compound mixture) 0.3 parts, lubricant (N, N'-ethylene bisstearamide) 0.3 parts. Wherein, the mass percent content of the component butadiene of ABS is 45%; The mass ratio of tribromophenoxytriazine and antimony trioxide is 3: 1, and the graft rate of maleic anhydride is 11%, hindered The mass ratio of phenolic antioxidant and phosphite antioxidant is 1:1.5.

[0052] Preparation method: Weigh the above raw materials, first mix ABS, SAN and lubricant evenly, then add other raw materials into the high mixer, stir and mix for 3 minutes; put the mixed raw materials ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ABS modified material with high heat resistance, high gloss and flame retardance and a preparation method thereof. The material comprises ABS, SAN (Styrene Acrylonitrile), a flame retardant, a heat resistant agent, a compatibilizer, an antioxidant and a lubricating agent. The preparation method comprises the steps of: weighing raw materials; sequentially adding the raw materials into a high mixing machine in a material mixing sequence; stirring and mixing for at least 2 minutes; putting the mixed raw materials into a double-screw extruder for extruding and granulating, wherein the screw rotating speed is 200 to 450 revolutions / minute, the screw temperature is 180 DEG C to 220 DEG C, the residence time is 1 to 2 minutes and the melt pressure is 10 to 20MPa; extruding to obtain particles; and drying the particles at 60 DEG C to 90 DEG C for 2 to 4 hours. The invention provides the ABS modified material which achieves high heat resistance, flame retardance and high gloss.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to an ABS modified material, in particular to a high heat-resistant, high-gloss, flame-retardant ABS modified material and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene copolymer (ABS) is widely used in machinery due to its good rigidity, hardness, high toughness and processing fluidity, low cost and light weight. , household appliances, daily appliances and other industries. However, since the ABS material contains butadiene rubber, its oxygen index is about 18%, and it is a flammable product. If it is to be made into a home appliance, it needs to be modified for flame retardancy. On the other hand, the automotive industry and the home appliance industry also have an increased demand for ABS materials, such as automotive dashboards, grilles, electric water heater components, heating appliance shells (hair dryers, etc.), etc. ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L25/12C08K13/02C08K5/3415C08K5/3492C08K3/22
Inventor 谭善兴
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com