A polishing liquid and stainless steel technology, applied in the field of polishing liquid, can solve the problems of low polishing efficiency, high production workers' experience and technical requirements, poor surface brightness, etc., to reduce costs, show high quality and surface finish, and improve production efficiency Effect
Active Publication Date: 2012-12-19
CHONGQING CHUANYI AUTOMATION
View PDF0 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] At present, the commonly used polishing liquid is prepared from diamond micropowder or cubic boron nitride micropowder and vegetable oil or mineral oil in a certain proportion. Stainless steel products polished with this polishing liquid have poor surface brightness, low polishing efficiency and long polishing time.
[0004] At present, the commonly used stainless steel mirror polishing liquid is cubic boron nitride micro-powder polishing liquid, which is directly prepared by cubic boron nitride micro-powder and vegetable oil or mineral oil in a certain proportion. Use this polishing liquid to polish stainless steel products, and the surface of stainless steel products Although the brightness is higher than that of diamond micropowder polishing fluid, due to the uneven distribution of cubic boron nitride micropowder, after standing for a certain period of time, it all settles at the bottom and gathers into agglomerates. During the polishing process, the polishing fluid must be constantly shaking or stirring, even so, the polishing liquid can not form a uniformly dispersed suspension
In practical applications, the polishing liquid will cause serious scratches and damage to the surface of the workpiece. Due to the unevenness of the abrasive concentration, the size of the workpiece is not easy to control, the processing efficiency is unstable, and the experience and technical requirements of the production workers are high, so it cannot be realized. batch processing
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0029] The components required for the polishing liquid are configured as described in Table 2:
[0030] Table 2
[0031] Serial number Cubic boron nitride powder (g) Stearic acid (g) Kerosene (g) 13150192 24200256 35250320 46300384
[0032] The specific steps of making stainless steel mirror polishing liquid are as follows:
[0033] (1) Weighing: Put a layer of clean white paper on the electronic balance, take out the cubic boron nitride powder with a medicine spoon and place it on the white paper, and accurately weigh the cubic boron nitride powder as described in Table 2.
[0034] (2) Baking: Put the white paper containing cubic boron nitride powder on the heating platform, and bake it at 100°C for 120 minutes, then take it out and cool it in the air for 30 minutes.
[0035] (3) Grinding: Grind in a medium agate mortar, grind and disperse the agglomerated cubic boron nitride powder, not more than 2 grams each time, and the time is not less than 30 minutes.
[0036] (4) Ultrasonic ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to polishing liquid used for a stainless steel mirror surface and a preparation method. The polishing liquid consists of the following components in part by weight: 3 to 6 parts of cubic boron nitride micropowder, 240 to 300 parts of stearic acid, and 320 to 480 parts of kerosene. The surface of a workpiece polished by using the polishing liquid of the invention has high surface finishment; an operation method is simple; technical requirements are low; and the polishing liquid is suitable for large-batch production. The polishing liquid prepared by adopting the method ofthe invention is permanent suspension without precipitate.
Description
Technical field [0001] The invention relates to a polishing liquid, in particular to a polishing liquid for a stainless steel mirror surface and a preparation method. Background technique [0002] Stainless steel has the characteristics of high hardness, good wear resistance, good corrosion resistance, excellent appearance and long life. It is widely used in construction, automobile industry, shipbuilding industry, marine equipment, mechanical equipment and chemical equipment industries. The high-quality mirror polishing of the surface of stainless steel products is one of the key factors to ensure that it is widely used in construction, automobile industry, shipbuilding, marine equipment, mechanical equipment and chemical equipment. The proportion of the surface polishing liquid of stainless steel products is the surface of stainless steel products. The key to achieving mirror quality. [0003] At present, the commonly used polishing liquid is made of diamond powder or cubic boro...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02
Inventor 柏教林
Owner CHONGQING CHUANYI AUTOMATION
Features
- R&D
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
Why Patsnap Eureka
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com