Dark colour-system reflection-type outer wall thermal insulation coating and preparation method thereof
A heat-insulating coating and reflective technology, applied in the direction of reflection/signal coatings, coatings, etc., can solve the problems of poor particle size control, poor product stability, and difficult dispersion, and achieve obvious heat insulation effect and good dispersion effect , Improve the effect of heat insulation performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1 is a reflective exterior wall heat insulation provided by the present invention. Its components include silicone-modified styrene-acrylic emulsion, rutile titanium dioxide (particle size range 0.107μm~0.687μm, rectangular), iron red, Iron black, medium chrome yellow, talc powder, kaolin, heavy calcium, additives and water. The addition amount of each component is: (mass percentage) organic silicon modified styrene-acrylic emulsion 20%, rutile titanium dioxide 6%, Iron red, iron black, medium chrome yellow 2%, talc powder, kaolin, heavy calcium 35%, additives 6%, water 31%, the preparation process is: first dispersing agent, wetting agent, defoaming agent, fiber Add the basic additives to 32% water and stir evenly at low speed, then add 6% rutile titanium dioxide, 35% talc, kaolin, and heavy calcium into the high-speed stirring for about 30 minutes, and enter the sand mill for sanding. When the particle size of the system reaches below 60μm, add defoamer, film-f...
Example Embodiment
[0020] Example 2 is a reflection type exterior wall heat insulation provided by the present invention. Its components include silicone modified styrene-acrylic emulsion, rutile titanium dioxide (particle size range 0.107μm~0.687μm, rectangular), iron red, Iron black, medium chrome yellow, talc powder, heavy calcium, additives and water. The addition amount of each component is: (mass percentage) organic silicon modified styrene-acrylic emulsion 23%, rutile titanium dioxide 7%, iron red , Iron black, medium chrome yellow 4%, talc powder, kaolin, heavy calcium 35%, auxiliary agent 6%, water 25%, the preparation process is: first dispersing agent, wetting agent, defoaming agent, cellulose auxiliary Add 25% of the water, stir evenly at low speed, then add 7% rutile titanium dioxide, 35% talc, kaolin, and heavy calcium into high-speed stirring for about 30 minutes, and enter the sand mill for sanding. When the particle size reaches 60μm or less, add defoamer, film forming aid, 23% s...
Example Embodiment
[0021] Example 3 is a reflective external wall heat insulation provided by the present invention, and its components include silicone-modified styrene-acrylic emulsion, rutile titanium dioxide (particle size range 0.107μm~0.687μm, rectangular), iron red, Iron black, medium chrome yellow, talc powder, heavy calcium, additives and water. The addition amount of each component is: (mass percentage) silicone modified styrene-acrylic emulsion 29%, rutile titanium dioxide 6%, iron red , Iron black, medium chrome yellow 5%, talc powder, kaolin, heavy calcium 34%, auxiliary agent 6%, water 20%, the preparation process is: first dispersant, wetting agent, defoamer, cellulose auxiliary Add 20% water and stir evenly at low speed, then add 6% rutile titanium dioxide, 34% talcum powder, kaolin, heavy calcium, etc. into high-speed stirring for about 30 minutes, and enter the sand mill for sanding. When the particle size of the system reaches below 60μm, add defoamer, film-forming aid, 29% sil...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap