A technology of oil agent and nylon, which is applied in the field of nylon FDY oil agent and preparation, can solve the problems of thermal stability, dynamic friction coefficient not reaching high-speed spinning, etc., to reduce the generation of fuzz, enhance cohesion, and pass rate high effect

Inactive Publication Date: 2011-01-19
JIAXING NEW & HIGH TECH FIBER
View PDF8 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the thermal stability and dynamic friction coefficient of domesti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] As an embodiment of the nylon FDY oil agent of the present invention, the present embodiment determines the ratio of each component by mass percentage:

[0027] (1) the mass percent of isooctyl stearate is 55%;

[0028] (2) The mass percentage of scouring agent is 7%;

[0029] (3) the mass percentage that oleic acid accounts for is 7%;

[0030] (4) the mass percent of coconut oil diethanolamine is 10%;

[0031] (5) The mass percentage of hydrogenated castor oil polyoxyethylene ether is 5%;

[0032] (6) The mass percent of fatty alcohol polyoxyethylene ether 4 is 7%;

[0033] (7) The mass percent of oleic acid sarcosine is 1.5%;

[0034] (8) The mass percentage of hypophosphorous acid is 1%;

[0035] (9) Potassium hydroxide accounts for 1.5% by mass;

[0036] (10) The mass percentage of the wetting agent is 5%.

[0037] After the above ratio is prepared, the preparation method of nylon FDY oil agent is as follows:

[0038] It includes the mixing stage, that is, a...

Embodiment 2

[0044] As an embodiment of the nylon FDY oil agent of the present invention, the present embodiment determines the ratio of each component by mass percentage:

[0045] (1) the mass percent of isooctyl stearate is 60%;

[0046] (2) The scouring agent accounts for 5% by mass;

[0047] (3) oleic acid accounts for 5% by mass;

[0048] (4) the mass percent of coconut oil diethanolamine is 8%;

[0049] (5) hydrogenated castor oil polyoxyethylene ether accounts for 7% by mass;

[0050] (6) The mass percent of fatty alcohol polyoxyethylene ether 4 is 5%;

[0051] (7) The mass percent of oleic acid sarcosine is 2%;

[0052] (8) The mass percentage of hypophosphorous acid is 1%;

[0053] (9) Potassium hydroxide accounts for 1.5% by mass;

[0054] (10) The mass percentage of the wetting agent is 5.5%.

[0055] After being prepared with the above-mentioned ratio, the difference between the preparation method of nylon FDY oil agent and embodiment one is:

[0056] In this embodiment...

Embodiment 3

[0060] As an embodiment of the nylon FDY oil agent of the present invention, the present embodiment determines the ratio of each component by mass percentage:

[0061] (1) the mass percent of isooctyl stearate is 57%;

[0062] (2) The mass percentage of scouring agent is 6%;

[0063] (3) oleic acid accounts for 6.5% by mass;

[0064] (4) the mass percent of coconut oil diethanolamine is 9%;

[0065] (5) The mass percentage of hydrogenated castor oil polyoxyethylene ether is 6%;

[0066] (6) The mass percent of fatty alcohol polyoxyethylene ether 4 is 6%;

[0067] (7) The mass percentage of oleic acid sarcosine is 1%;

[0068] (8) The mass percentage of hypophosphorous acid is 0.5%;

[0069] (9) Potassium hydroxide accounts for 1% by mass;

[0070] (10) The mass percentage of the wetting agent is 7%.

[0071] After being prepared with the above-mentioned ratio, the difference between the preparation method of nylon FDY oil agent and embodiment one is:

[0072] In this e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of auxiliary manufacturing in the fiber processing technology, in particular to finish for nylon FDY and a preparation method. The finish for nylon FDY comprises the following components: 55-60% of isooctyl stearate, 5-7% of scouring agents, 5-7% of oleic acid, 8-10% of coconut oil diethanolamine, 5-7% of hydrogenated castor oil polyoxyethylene ether, 5-7% of fatty alcohol polyoxyethylene ether 4, 1-2% of oleic acid sarcosine, 0.5-1% of hypophosphorous acid, 1-1.5% of potassium hydroxide and 5-7% of wetting agent. The preparation method comprises the process steps of mixing, stirring and testing. The finish for nylon FDY has good thermal stability, is less in volatilization and free of coking and has low coefficient of dynamic friction in the drawing stage and good cohesion.

Description

technical field [0001] The invention relates to the technical field of auxiliary agent manufacturing in fiber processing technology, in particular to nylon FDY oil agent and its preparation method. Background technique [0002] As an indispensable chemical auxiliary in the production and processing of synthetic fibers - spinning oil, the current spinning speed of nylon FDY high-speed one-step spinning has reached more than 4500 m / min. Under such high-speed operation, high shear force, The effect of high friction will inevitably increase the damage to the polymer, thereby generating heat and forming coke. At present, the thermal stability and dynamic friction coefficient of domestic high-speed spinning oils cannot meet the requirements of high-speed spinning. Contents of the invention [0003] The invention provides a nylon FDY oil with good thermal stability, less volatilization, no coking, low dynamic friction coefficient in the stretching stage, and good cohesion, and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/224D06M13/203D06M13/368D06M15/53D06M13/165D06M13/342D06M11/38D06M11/70D06M101/34
Inventor 于华龙顾培忠
Owner JIAXING NEW & HIGH TECH FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap