Quick-dry type acrylic modified alkyd paint and preparation method thereof

An acrylic, quick-drying technology, applied in the field of coatings, can solve the problem of high price, achieve the effect of high decoration, good gloss retention and weather resistance, and good recoatability

Inactive Publication Date: 2011-01-26
天津灯塔涂料工业发展有限公司
View PDF4 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Pure acrylic paint has good weather resistance and excellent overall performance, but the price is high, which is difficult for general users to accept. In order to meet market d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of quick-drying type acrylic acid modified alkyd paint, comprises following components, and every part by weight is calculated according to 10g,

[0028] Acrylic modified alkyd resin 350g, pigment 150g, filler 100g, anti-settling agent bentonite 5g, dispersant BYK-110 3g, leveling agent BYK-3003g, defoamer BYK-066N 3g, rare earth drier 20g, anti-coagulation Skin agent methyl ethyl ketone oxime 1g, heavy aromatics 100g, xylene 100g, 200# solvent gasoline 50g. (The specific names of the various agents listed above are listed above)

[0029] The preparation method of above-mentioned quick-drying type acrylic acid modified alkyd paint, carry out according to the following steps,

[0030] Add acrylic modified alkyd resin, pigments, fillers, anti-sedimentation agents, and dispersants into the batching tank, stir and mix evenly, disperse at high speed for 20 minutes, and grind in a sand mill until the fineness reaches 30 microns, then pour the pigment slurry into the l...

Embodiment 2

[0043] A kind of quick-drying type acrylic acid modified alkyd paint, comprises following components, and every part by weight is calculated according to 10g,

[0044] Acrylic modified alkyd resin 650g, pigment 250g, filler 250g, anti-settling agent bentonite 20g, dispersant BYK-110 10g, leveling agent BYK-300 6g, defoamer BYK-066N 6g, rare earth drier 50g, Skinning agent methyl ethyl ketone oxime 3g, heavy aromatics 200g, xylene 200g, 200# solvent gasoline 150g.

[0045] The preparation method of the above-mentioned quick-drying type acrylic modified alkyd paint is carried out according to the steps of Example 1.

[0046] (1) Wherein the acrylic modified alkyd resin comprises the following components, parts by weight are based on 10g, soybean oil 300g, pentaerythritol 100g, yellow lead 0.4g, acrylic resin prepolymer 300g, phthalic anhydride 200g, benzoic acid 50g, Heavy aromatics 200g, xylene 200g, 200# solvent gasoline 150g.

[0047] The preparation method of the above-menti...

Embodiment 3

[0052] A kind of quick-drying type acrylic acid modified alkyd paint, comprises following components, and every part by weight is calculated according to 10g,

[0053] Acrylic modified alkyd resin 450g, pigment 200g, filler 200g, anti-settling agent 10g, dispersant 8g, leveling agent 5g, defoamer 4g, drier 30g, anti-skinning agent 2g, heavy aromatics 150g, xylene 150g, mineral spirits 100g.

[0054] The preparation method of the above-mentioned quick-drying type acrylic modified alkyd paint is carried out according to the steps of Example 1.

[0055] (1) Wherein the acrylic modified alkyd resin comprises the following components, parts by weight are based on 10g, soybean oil 150g, pentaerythritol 70g, yellow lead 0.2g, acrylic resin prepolymer 200g, phthalic anhydride 150g, benzoic acid 35g, Heavy aromatics 150g, xylene 180g, 200# solvent gasoline 100g.

[0056] The preparation method of the above-mentioned acrylic acid modified alkyd resin is carried out according to the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to quick-dry type acrylic modified alkyd paint which is characterized by comprising the following components in parts by weight: 35-65 parts of acrylic modified alkyd resin, 15-25 parts of pigment, 10-25 parts of filling, 0.5-2.0 parts of anti-settling agent, 0.3-1.0 part of dispersant, 0.3-0.6 part of flatting agent, 0.3-0.6 part of antifoaming agent, 2-5 parts of drier, 0.1-0.3 part of anti skinning agent, 10-20 parts of heavy aromatic, 10-20 parts of xylene and 5-15 parts of prime city naphtha. The preparation method comprises the following steps of: adding the front four raw materials of the acrylic modified alkyd resin, and the like into a burdening pot; evenly stirring a mixture, dispersing the mixture for 20 minutes at high speed; grinding the mixture in a sand grinder into fineness of 30micron; filling pigment paste into a paint mixing tank; adding the last seven raw materials; evenly stirring; and filtering. The invention has the beneficial effects that various colors of acrylic modified alkyd paint is prepared by using the acrylic modified alkyd resin as a base material; and a paint film is quickly dried, and has the characteristics of good light retention property, weather resistance and recoatability, high decoration performance, and greatly improved comprehensive physical and chemical properties.

Description

technical field [0001] The invention belongs to coatings, in particular to a quick-drying acrylic modified alkyd paint and a preparation method thereof. Background technique [0002] Alkyd paint is a type of paint with alkyd resin as the main film-forming substance. Gloss, flexibility, abrasion resistance, weather resistance and adhesion are good, which can meet the general requirements of use, but the drying speed of alkyd paint is slow (6-8 hours for surface drying), and the hardness is low (0.25), which cannot meet some workpieces Construction requirements of fast drying, high hardness and high weather resistance. In order to modify the existing alkyd resin, many units have done a lot of research work, such as modifying alkyd resin with epoxy resin, acrylic resin, silicone resin, etc., so as to improve its adhesion, weather resistance, and durability respectively. thermal properties. The use of acrylic modified alkyd resin can greatly improve the drying speed (surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/08C08G63/49C08F220/14C08F212/08
Inventor 刘建颖莫书庚
Owner 天津灯塔涂料工业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap