Preparation method of graphene-base tin dioxide composite anode material for lithium ion batteries

A tin dioxide, graphene-based technology, applied in the fields of material science and electrochemistry, can solve the problems of metal oxide negative electrode materials that are difficult to get practical application, loss of electrical contact between ions, electrode cracks and brittleness, etc., and achieve good electrochemical performance. performance, improved electrochemical performance, mild conditions

Inactive Publication Date: 2011-02-09
SHANGHAI UNIV
View PDF2 Cites 62 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the alloying/dealloying process of such anode materials with lithium, the metal matrix may undergo large changes in both structure and volume, and at the same time, the mechanical pressure associated with volume changes can cause its mechanical stability. Rapid decay, causi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphene-base tin dioxide composite anode material for lithium ion batteries
  • Preparation method of graphene-base tin dioxide composite anode material for lithium ion batteries
  • Preparation method of graphene-base tin dioxide composite anode material for lithium ion batteries

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0030] 1. Prepare raw graphite oxide nanosheets according to the prior art (this technical method can refer to the document J.Am.Chem.Soc., 2008, 130(18), 5856-5857).

[0031] A certain amount of K 2 S 2 o 8 and P 2 o 5 Dissolve in concentrated sulfuric acid, add a certain amount of natural graphite after heating to 80°C, keep warm at 80°C for 4.5 hours, and then cool to room temperature; then dilute with deionized water and leave it overnight; then filter and wash, and put the obtained filter residue in Dry in a vacuum oven at 60°C; dissolve the dried filter residue in concentrated H 2 SO 4 , slowly add KMnO in ice bath 4 , stirred at 35°C for 2h; then diluted with deionized water, and slowly added 30% H 2 o 2 After filtering and washing, the washed product is dispersed in deionized water, and ultrasonically stripped to obtain graphite oxide nanosheets, which are centrifuged and dried for use.

[0032] 2. Preparation of graphene-based tin dioxide composite lithium-io...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a graphene-base tin dioxide composite anode material for lithium ion batteries, which belongs to the technical fields of material science and electrochemistry. The method for preparing graphene-base tin dioxide comprises the following steps: 1. dispersing graphite oxide nanosheets in an ethanol C2H5OH solution; 2. adding a certain amount of template agent cetyl trimethyl ammonium bromide (CTAB) into the suspension, adding a certain amount of tin tetrachloride hydrate (SnCl4.5H2O) and sodium hydroxide (NaOH) while vigorously stirring, and continuing stirring for 30 minutes; 3. after stirring, transferring the suspension into a high pressure reaction kettle, reacting in a baking oven at 160 DEG C for 20 hours, and washing the reaction product with ethanol and deionized water many times; and 4. carrying out vacuum drying on the product at 60 DEG C for 8 hours to obtain the graphene-base tin dioxide composite material.

Description

technical field [0001] The invention relates to a one-step method for preparing graphene-based tin dioxide composite lithium-ion battery negative electrode materials, belonging to the fields of material science and electrochemical technology. Background technique [0002] Lithium-ion energy materials can provide energy guarantee for modern communication and information technology. At present, the graphitized carbon anode materials that have been commercially promoted and used are increasingly unable to meet the requirements of technological development due to their low lithium storage capacity (<372mAh / g). Therefore, higher storage capacity and cycle life requirements are put forward for lithium-ion energy materials. In recent years, new lithium-ion energy materials with high specific capacity and excellent cycle performance have become a hot spot of scientific research. [0003] In recent years, on the basis of traditional graphite carbon materials, some new and excell...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/139H01M4/13
CPCY02E60/122Y02E60/10
Inventor 焦正张海娇徐盼盼刘刚李智勇王琳
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap