Method for producing green attapulgite polymer clay

Abstract

The invention discloses a method for producing green attapulgite polymer clay, the technical scheme thereof is characterized by adding green sand-grain shaped attapulgite mixture to a running horizontal type flour-mixing machine, slowly adding sodium polyacrylate sol-gel to the green sand-grain shaped attapulgite mixture, and stirring the mixture to obtain green massive attapulgite mixture; spraying methyl silicon oil on the green massive attapulgite mixture, and rubbing the sprayed mixture to obtain the semi-finished product of the green attapulgite polymer clay; and finally suppressing the green attapulgite polymer clay to form the flat green attapulgite polymer clay, and sealing and packaging the flat green attapulgite polymer clay to obtain the finished product. The green attapulgite polymer clay has the advantages of high viscosity, good soft plasticity, and small contractibility rate; in addition, the green attapulgite polymer clay is hardened after being subject to air dry, in no need of baking, and has nonoccurrence of cracks, no corrosiveness and non-greasy feeling. The green attapulgite polymer clay is mixed with other colorific attapulgite polymer clay for use, thus being capable of shaping artwares with clear patterns, fresh and lovely luster and vivid effect; and the green attapulgite polymer clay is suitable for the shaping of patterns, moulds and artwares.

Description

technical field [0001] The invention relates to clay, in particular to a production method of green attapulgite soft clay. Background technique [0002] The main raw materials of soft clay are polyvinyl chloride and calcium carbonate. The adhesion is not good at room temperature, and it is easy to age and fade after long-term storage. It is easy to foam when baking soft clay. If the temperature exceeds 200 ° C, it will not only make The finished product is scorched and melted, and may even cause combustion, generating irritating and toxic fumes containing chlorine. The sales price of soft clay is relatively high, which is not conducive to popularization and use. [0003] The Chinese patent publication number is: CN 101186736, open date: May 28, 2008, titled "a kind of soft clay and its preparation method", discloses: "a kind of soft clay and its preparation method, which consists of the following weight It is prepared from 15 parts: polyvinyl chloride paste resin 15-40, diz...

AI Technical Summary

Problems solved by technology

[0004] The disadvantage of the above-mentioned patents is that the main raw materials of the soft clay produced by this technology are polyvinyl chloride paste resin, dizinc grease and calcium carbonate, and the adhesion is not good under normal temperature, which is not conducive to making molding. Dizinc grease belongs to poisonous substance

[0006] The disadvantage of the above-mentioned patent is that the main raw materials of the transparent texture resin clay produced by this technology are powdery ethylene-vinyl acetate copolymer and starch, and the powdery ethylene-vinyl acetate copolymer is irritating to the eyes and skin, so it is not suitable for It is used to produce raw materials for making handicrafts. This product requires a large amount of starch, which is not conducive to popularization and use.