Universal water enamel

A water-based, enamel paint technology, applied in coatings, epoxy resin coatings, etc., can solve the problem of not getting users, and achieve the effects of easy construction, good leveling, and full and beautiful paint film.

Active Publication Date: 2013-03-27
广东大中三联科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, whether it is the products sold on the market or the technical solutions disclosed by Chinese patents, these products are often inferior to solvent-based paints in terms of paint film properties, such as hardness, adhesion, and paint film flexibility. Less than the general approval of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Universal water enamel
  • Universal water enamel
  • Universal water enamel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A kind of water-based universal enamel (varnish), comprises following components, and the percentage by weight of each component is: organosilicon modified water-based acrylic resin: 58%, acrylic acid modified water-based epoxy ester resin: 10%, nanoscale talcum powder: 3.8%; adhesion promoter: 0.8%; coalescent: 4%; anti-flash rust agent: 1.2%; dispersant: 0.4%; leveling agent: 0.2%; : 0.5%; fungicide: 0.3%; PH regulator: 0.2%; thickener: 1.5%, water: 18.8%.

[0049] Follow the steps below to prepare:

[0050] 1) Put the above-mentioned dispersant, wetting agent, water and 50% defoamer into a high-speed stirring container with a rotation speed of 1300 rpm, and add a thickener while stirring at a high speed until the thickener is completely dispersed Finally, add nano-talc powder and disperse at a high speed until the fineness of the scraper is below 20 microns;

[0051] 2) Pour the dispersed liquid in process 1) into the tank of the quick defoaming device. After defoa...

Embodiment 2

[0056] A kind of water-based universal enamel (varnish), comprises following components, and the percentage by weight of each component is: organosilicon modified water-based acrylic resin: 62%, acrylic acid modified water-based epoxy ester resin: 8%, nanoscale talcum powder: 3.6%; adhesion promoter: 0.4%; coalescent: 4%; anti-flash rust agent: 1%; dispersant: 0.3%; leveling agent: 0.3%; wetting agent: 0.3%; : 0.4%; fungicide: 0.2%; PH regulator: 0.3%; thickener: 1.6%, water: 17.6%.

[0057] Follow the steps below to prepare:

[0058]1) Put the above-mentioned dispersant, wetting agent, water and 50% defoamer into a high-speed stirring container with a rotation speed of 1500 rpm, and add a thickener while stirring at a high speed until the thickener is completely dispersed Finally, add nano-talc powder and disperse at a high speed until the fineness of the scraper is below 20 microns;

[0059] 2) Pour the dispersed liquid in step 1) into the tank of the quick defoaming devic...

Embodiment 3

[0065] A water-based universal enamel paint (red paint), comprising the following components, the weight percent of each component is: silicone modified water-based acrylic resin: 49%, acrylic acid-modified water-based epoxy ester resin: 12%, nanoscale talcum powder : 4.5%; adhesion promoter: 1.0%; coalescent: 3.3%; anti-flash rust agent: 1.5%; dispersant: 0.6%; leveling agent: 0.3%; Agent: 0.6%; Fungicide: 0.3%; PH regulator: 0.3%; Thickener: 1.0%, Water: 17.1%; Scarlet water-based color paste: 8%.

[0066] Follow the steps below to prepare:

[0067] 1) Put the above-mentioned dispersant, wetting agent, water and 50% defoamer into a high-speed stirring container with a rotation speed of 1300 rpm, and add a thickener while stirring at a high speed until the thickener is completely dispersed Finally, add nano-talc powder and disperse at a high speed until the fineness of the scraper is below 20 microns;

[0068] 2) Pour the dispersed liquid in step 1) into the tank of the qui...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides universal water enamel and a preparation method thereof. The universal water enamel comprises the following components by weight percent: 42-65% of organic silicon modified water acrylic resin, 8-12% of acrylic acid modified water epoxy resin, 10-20% of water, 0.20-0.80% of dispersant, 0.20-0.80% of wetting agent, 0.10-0.60% of flatting agent, 0.20-0.80% of defoaming agent, 3-5% of nano talcum powder, 0.20-0.50% of fungicide, 0.5-2% of thickening agent, 2-5% of film forming assistant, 0.30-1% of adhesion promoter, 0.50-2% of rust inhibitor, 0.10-0.50% of pH regulator and 0-10% of water colour paste. The universal water enamel of the invention has high hardness, strong adhesion and good film flexibility, can be applied to multiple substrates and has the characteristics of good levelling property, full and beautiful film and easy construction.

Description

technical field [0001] The invention relates to a water-based paint, in particular to a paint that dries at normal temperature and can be used on the surfaces of metals, medium and low temperature ceramics, glass, plastics, and interior walls, and has high hardness, strong adhesion, and good flexibility of the paint film. Versatile, water-based universal enamel. Background technique [0002] With the improvement of people's living standards, various types of engineering decoration have higher and higher requirements on the environmental protection of decorative materials. Ordinary solvent-based paints contain a large amount of organic solvents, which cause great pollution to the environment and cause harm to the human body when used, which does not meet environmental protection requirements. Therefore, the modern paint industry is working hard to reduce the use of solvents and has developed a high-efficiency paint. Environmentally friendly coatings such as solid content coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More