Transition plate of inert composite electrode adopting EFT and preparation method thereof and electrolytic equipment containing transition plate

A technology for electrolysis equipment and electrode plates, applied in the direction of electrodes, electrolysis process, electrolysis components, etc., can solve the problems of easy aging, short service life, high consumption of electrode plate materials, and achieve stable distribution, protection of service life, and not easy to be corroded. Effect

Inactive Publication Date: 2011-03-16
蒋亚熙 +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Moreover, the soluble electrodes widely used at home and abroad are mostly iron plates and aluminum plates, which are used as coagulants for sewage treatment, but the electrode plate material consumption is too high, easy to accumulate fouling, easy to age, and has a short service life (about 30 days), which increases the Wastewater Treatment Costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transition plate of inert composite electrode adopting EFT and preparation method thereof and electrolytic equipment containing transition plate
  • Transition plate of inert composite electrode adopting EFT and preparation method thereof and electrolytic equipment containing transition plate
  • Transition plate of inert composite electrode adopting EFT and preparation method thereof and electrolytic equipment containing transition plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] Embodiment 1. Transition plate, a 9-layer structure composed of graphite layer, iron layer after sprinting, graphite layer, glass fiber reinforced plastic layer, graphite layer, aluminum layer, graphite layer, glass fiber reinforced plastic layer, graphite layer

[0107] Step 1: Preparation of Graphite Layer

[0108] Select high-quality expanded graphite worms with a content of more than 99.8% and press them into 5 composite flat plates with a thickness of 0.5mm.

[0109] Step 2: Preparation of FRP layer

[0110] Use high-quality epoxy resin and glass fiber to press into 2 composite flat plates with a thickness of 0.5mm.

[0111] Step 3: Preparation of active metal layer

[0112] Aluminum plates with a thickness of more than 1.0mm are selected, and active metal iron materials with a thickness of 0.1mm are selected for sprint treatment.

[0113] Step 4: Preparation of transition plate

[0114] After the 0.5mm graphite layer, the 0.1mm thickness of the sprinted active...

Embodiment 2

[0116] Embodiment 2. Transition plate, a 4-layer structure consisting of graphite layer, sprinted iron layer, graphite layer and aluminum layer in sequence

[0117] Step 1: Preparation of Graphite Layer

[0118] Select high-quality expanded graphite worms with a content of more than 99.8% and press them into 2 composite flat plates with a thickness of 0.8mm.

[0119] Step 2: Preparation of active metal layer

[0120] Aluminum plates with a thickness of 1mm are selected, and active metal iron materials with a thickness of 0.1mm are selected for sprint treatment.

[0121] Step 3: Preparation of transition plate

[0122] After the 0.8mm graphite layer, the 0.1mm thick sprinted iron layer and the 0.8mm graphite layer are sequentially bonded and flattened with conductive adhesive, the first composite material is obtained; then the composite material is combined with 1mm thick active metal aluminum After the layers are bonded and flattened with conductive adhesive, they are fixed...

Embodiment 3

[0123] Embodiment 3. Transition plate, a 5-layer structure composed of graphite layer, iron layer after sprinting, graphite layer, aluminum layer and graphite layer in sequence

[0124] Step 1: Preparation of Graphite Layer

[0125] Select high-quality expanded graphite worms with a content of more than 99.8% and press them into 3 composite flat plates with a thickness of 1mm.

[0126] Step 2: Preparation of active metal layer

[0127] An aluminum plate with a thickness of 1mm was selected, and an iron plate with a thickness of 0.3mm was selected for sprinting treatment to obtain two active metal layers respectively.

[0128] Step 3: Preparation of transition plate

[0129] After the graphite layer, the sprinted 0.3mm iron plate layer and the graphite layer are bonded and flattened with conductive adhesive in sequence, the first composite material is obtained; then the graphite layer and the 1mm thick aluminum plate layer are bonded and flattened with conductive adhesive in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an electrode plate of an inert composite electrode adopting environment friendly technology (EFT), in particular to a transition plate of the inert composite electrode, and a preparation method and application of the electrode plate. After using the electrode plate, the treated sewage can be discharged up to the standard and the service life of the electrode plate is greatly prolonged.

Description

technical field [0001] The invention relates to an electrode plate of an inert composite electrode of environment friendly technology (EFT, Environment Friendly Technology), especially a transition plate of an inert composite electrode, a preparation method of the electrode plate and an application thereof. Background technique [0002] Electrochemical water treatment technology is called "environmentally friendly" technology (EFT, Environment Friendly Technology. The main points of EFT electrochemical technology are: electrocoagulation / electrical floatation / co-precipitation technology, which is the application of electrochemical redox reaction principle, control Electrochemical method of pollution. Direct current of a certain voltage is passed into the electrolytic cell, and the wastewater passes through the electrolytic cell, so that the anion of the electrolyte in the wastewater moves to the anode, loses electrons at the anode and is oxidized, and the cation moves to the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25B11/00C02F1/461
CPCC02F1/46109C25B11/00C02F2001/46138
Inventor 蒋亚熙张定军
Owner 蒋亚熙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap