Aluminasol bonded alumina mould case and manufacturing method thereof

A kind of alumina and aluminum sol technology, applied in the direction of manufacturing tools, casting equipment, metal processing equipment, etc., can solve problems such as waste, casting surface pollution, damage to casting quality, etc., to achieve controllable process parameters and meet thermal shock resistance , the effect of not easily deformed

Active Publication Date: 2011-04-27
BEIHANG UNIV
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the new superalloy contains a certain amount of highly active metal elements such as Re, Ru, Hf, Cr, Y, and a relatively high content of Al elements. When using traditional silica sol as a binder to prepa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminasol bonded alumina mould case and manufacturing method thereof
  • Aluminasol bonded alumina mould case and manufacturing method thereof
  • Aluminasol bonded alumina mould case and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0064] Example 1:

[0065] Aluminum sol bonded alumina mold shell for directional solidification DD6 alloy (composition as shown in the table below)

[0066] ingredient

[0067] The first step: match the shell slurry

[0068] The shell slurry is made of aluminum sol (selected LA-25 aluminum sol produced by Zibo Jinqi Chemical), aluminum oxide powder, Cr 2 O 3 (Mineralizer), ammonium polyacrylate (dispersant), n-octanol (defoamer) and JFC (wetting agent), the content of each component is shown in the table below:

[0069] ingredient

[0070] Step 2: Prepare the mold shell

[0071] (A) Immerse the wax mold in the shape of a casting into the slurry prepared in the first step for 5 seconds and then take it out, and sprinkle with 80 mesh alumina sand to form the first preform;

[0072] (B) Place the first preform in a constant temperature and humidity environment with a temperature of 20° C. and a relative humidity of 60% for drying for 20 hours to obtain a second preform;

[0073] (C) ...

Example Embodiment

[0092] Example 2:

[0093] Pouring Ni 3 Aluminum sol bonded alumina mold shell for Al-based alloy (the composition is shown in the table below)

[0094] ingredient

[0095] The first step: match the shell slurry

[0096] The shell slurry is made of aluminum sol (select LA-20 type aluminum sol produced by Zibo Jinqi Chemical), aluminum oxide powder, MgO (mineralizer), ammonium polyacrylate (dispersant), n-octanol (defoamer) And JFC (wetting agent) composition; the content of each component is shown in the following table:

[0097] ingredient

[0098] Step 2: Prepare the mold shell

[0099] (A) Immerse the wax mold in the shape of a casting into the slurry prepared in the first step for 2 seconds, then take it out, and sprinkle with 80 mesh alumina sand to form the first preform;

[0100] (B) Place the first preform in a constant temperature and humidity environment with a temperature of 35° C. and a relative humidity of 70% and dry for 20 hours to obtain a second preform;

[0101] ...

Example Embodiment

[0117] Example 3:

[0118] Aluminum sol bonded alumina mold shell for directional solidification TMS75 alloy (composition as shown in the table below)

[0119] ingredient

[0120] The first step: match the shell slurry

[0121] The shell slurry is made of aluminum sol (select LA-25 type aluminum sol produced by Zibo Jinqi Chemical), aluminum oxide powder, TiO (mineralizer), ammonium polyacrylate (dispersant), n-octanol (defoamer) And JFC (wetting agent) composition; the content of each component is shown in the following table:

[0122] ingredient

[0123] Step 2: Prepare the mold shell

[0124] (A) Immerse the wax mold in the shape of a casting into the slurry prepared in the first step for 8 seconds, then take it out, and sprinkle with 80 mesh alumina sand to form the first preform;

[0125] (B) The first preform is placed in a constant temperature and humidity environment with a temperature of 25° C. and a relative humidity of 65% and dried for 25 hours to obtain a second pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminasol bonded alumina mould case and a manufacturing method thereof. The slurry of the alumina mould case comprises aluminasol, alumina powder, a mineralizing agent, a dispersing agent, a defoaming agent and a moisturizing agent. In the invention, the alumina mould case is manufactured by using a molten mould precision casting process. The aluminasol bonded alumina mould case of the invention fully utilizes the characteristics of the two materials of aluminasol and alumina at low temperature and high temperature, the morphology of the section of the manufacturedmould case is observed under a scanning electron microscope, and the section has obvious layering structure. The layering structure occurred in the aluminasol bonded alumina mould case is caused by different particle sizes of alumina sands connecting two adjacent layers of the slurry, which is beneficial to interlayer bonding. Thus, the strength of the mould case is increased, the air permeability of the mould case is also increased, and thus, the mould case has enough strength and air permeability when the mould case is used at high temperature.

Description

technical field [0001] The invention relates to a high-temperature alloy investment casting high-temperature alloy mold shell, more particularly, refers to a mold shell suitable for precision casting molding or directional solidification molding or directional solidification molding of smelted high-activity metals and alloys containing high-activity metals. Single crystal grown alumina sol bonded alumina formwork. Background technique [0002] Superalloy is an attractive and excellent structural material, which has the characteristics of low density, high specific strength and good corrosion resistance, and has been widely used in aviation and aerospace fields. However, the new superalloy contains a certain amount of highly active metal elements such as Re, Ru, Hf, Cr, Y, and a relatively high content of Al elements. When using traditional silica sol as a binder to prepare mold shells for precision casting or directional solidification, Often due to highly reactive metals a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C1/00B22C1/18B22C9/02
Inventor 唐晓霞吴良策崔永双张虎
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap