PLA (polylactic acid) resin-ABS (acrylonitrile-butadiene-styrene) resin composite material and method for preparing same

A resin composite material, polylactic acid resin technology, applied in the field of polylactic acid-ABS resin composite material and its preparation, can solve the problems of poor impact resistance and low heat distortion temperature

Inactive Publication Date: 2011-05-04
SHENZHEN KEJU NEW MATERIAL
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its application as a general-purpose plastic is still subject to certain restrictions, mainly because polylactic acid is brittle and has poor impact resistance; the thermal deformation temperature is low, and it cannot be used normally at the required temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PLA (polylactic acid) resin-ABS (acrylonitrile-butadiene-styrene) resin composite material and method for preparing same
  • PLA (polylactic acid) resin-ABS (acrylonitrile-butadiene-styrene) resin composite material and method for preparing same
  • PLA (polylactic acid) resin-ABS (acrylonitrile-butadiene-styrene) resin composite material and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The present invention also provides the preparation method of the above-mentioned polylactic acid-ABS resin composite material, its technological process is as follows figure 1 shown. The method comprises the steps of:

[0047] S1: Weigh each component according to the above formula of polylactic acid-ABS resin composite material;

[0048] S2: Mix the weighed components to form a mixed material;

[0049] S3: extruding and granulating the mixed material to obtain the polylactic acid-ABS resin composite material.

[0050]Specifically, in step S1 of the above-mentioned polylactic acid-ABS resin composite material preparation method, the formulation of the polylactic acid-ABS resin composite material is as described above without additives or the formulation of another preferred embodiment containing additives . In order to save space, details are omitted here. Among them, before weighing each component according to the above formula, it is preferable to dry the polyla...

Embodiment 1

[0056] The formula component of polylactic acid-ABS resin composite material weight percent is as follows:

[0057] 60% of polylactic acid resin and its copolymer with a molecular weight of preferably 300,000, 30% of ABS resin, 4% of compatibilizer of SEBS grafted maleic anhydride, 5% of toughening agent of polyethylene octene co-elastomer, particle size is 2000 mesh, 0.5% talcum powder with a whiteness of 95%, and 0.5% coupling agent of γ-aminopropyltriethylsilane.

[0058] The preparation method of polylactic acid-ABS resin composite material is as follows:

[0059] S11: First put the polylactic acid resin and its copolymer, ABS resin, and talc powder into a drying oven, wherein the polylactic acid resin and its copolymer are dried at 80°C for 4 hours, and the talc powder is dried at 110°C. Dry for 3 hours, then weigh each component according to the formula of the above-mentioned polylactic acid-ABS resin composite material;

[0060] S12: Mix the weighed components and put...

Embodiment 2

[0063] The formula component of polylactic acid-ABS resin composite material weight percent is as follows:

[0064] 65% of polylactic acid resin and its copolymer with molecular weight preferably 50,000, 20% of ABS resin, 5% of compatibilizer of POE grafted maleic anhydride, 8% of toughening agent of thermoplastic polyurethane elastomer, particle size of 4000 mesh, 1% of talc powder with whiteness of 98%, 1% of coupling agent of γ-ureidopropyltriethoxysilane.

[0065] The preparation method of polylactic acid-ABS resin composite material is as follows:

[0066] S11: First put the polylactic acid resin and its copolymer, ABS resin, and talc powder into a drying oven, wherein the polylactic acid resin and its copolymer are dried at 80°C for 4 hours, and the talc powder is dried at 110°C. Dry for 3 hours, then weigh each component according to the formula of the above-mentioned polylactic acid-ABS resin composite material;

[0067] S12: Mix the weighed components and put them i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
whitenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PLA (polylactic acid) resin-ABS (acrylonitrile-butadiene-styrene) resin composite material and a method for preparing the same. The PLA resin-ABS resin composite material is prepared form the following components by weight percent: 60-80% of PLA resin and copolymer thereof, 10-30% of ABS resin, 3-5% of compatibilizer, 5-10% of toughening agent, 0.5-2% of talcum powder and 0.5-1.5% of coupling agent. The components in proper content range interact mutually during extrusion, thus the PLA resin and ABS resin composite material has advantages of excellent impact strength, heat distortion temperature and biodegradable properties. The method for preparing the PLA resin and ABS resin composite material adopts the simple one-step mixing reaction-extrusion-granulation process, is convenient to operate, has high benefit and low cost and is suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to a polylactic acid-ABS resin composite material and a preparation method thereof. Background technique [0002] Polylactic acid is a thermoplastic aliphatic polyester that is artificially synthesized from corn and other crops and can eventually be decomposed into carbon dioxide and water in the environment, and will not cause pollution or damage to the environment. It has good mechanical properties and biodegradability, and is often used in biodegradable plastics. Biodegradable plastics can't exist in the environment for a long time due to its important advantage of being compostable and degradable, so it is often used in disposable consumer packaging materials, hotel keys, gift cards and other daily consumables. field. [0003] At present, there is research on compounding bio-resins to make composite materials, which can be applied in the field of durable ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L55/02C08K13/02C08K3/34B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/875B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 徐东徐永潘明熙
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap