Ethylene-propylene-diene rubber composition with high comprehensive performance and preparation method thereof
A technology of EPDM rubber with comprehensive properties, applied in the field of rubber, can solve the problems of poor oil resistance of EPDM, achieve excellent ozone resistance, easy procurement, and improve the effect of poor oil resistance
Inactive Publication Date: 2011-06-15
上海众力减振技术有限公司
View PDF2 Cites 28 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The present invention adopts the combination of EPDM rubber and CSM rubber to improve the comprehensive properties of the rubber. After testing, the combined rubber is aged in hot air at 180°C for 7 days: the hardness change value is +5, and the tensile strength change rate is +8 %, the change value of elongation at break is: -40%. At the same time, it effectively improves the shortcomings of EPDM's poor oil resistance, and ensures excellent ozone resistance, acid and alkali resistance. It is an excellent resistance to complex environmental conditions. High temperature rubber material
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2
Embodiment 3
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
rate of change of tensile strength | aaaaa | aaaaa |
hardness change | aaaaa | aaaaa |
rate of change of tensile strength | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides an ethylene-propylene-diene rubber composition with high comprehensive performance and a preparation method thereof. The ethylene-propylene-diene rubber composition is characterized by being prepared from 75 to 90 mass parts of ethylene-propylene-diene rubber, 10 to 25 mass parts of chlorosulfonated polyethylene rubber, 1.5 to 3 mass parts of anti-aging agent prepared by product of reaction of a ketone and amine, 1 to 3 mass parts of paraphenylenediamine anti-aging agent, 1.5 to 2.5 mass parts of physical anti-aging agent, 0.5 to 1.0 mass parts of stearic acid, 5 to 8 mass parts of active agent, 30 to 50 mass parts of reinforcing agent, 3 to 8 mass parts of plasticizer, 1.5 to 3 mass parts of vulcanizer and 2 to 4 mass parts of accelerator. The invention also provides the preparation method of the rubber composition, which is to blend in an internal mixer or an open mill. The product has high temperature resistance and high comprehensive performance.
Description
A kind of EPDM composition with excellent comprehensive performance and preparation method thereof technical field The invention relates to an EPDM rubber composition with high temperature resistance of 175°C-180°C, low compression deformation, good oil resistance, excellent ozone aging resistance, weather resistance, acid and alkali resistance and its preparation method, which is used for making low-cost comprehensive performance requirements The invention relates to rubber products used under high temperature conditions, and belongs to the technical field of rubber. Background technique Ethylene-propylene rubber has excellent weather resistance, ozone resistance, heat resistance, acid and alkali resistance, water vapor resistance, color stability, electrical properties, oil filling and room temperature fluidity. Ethylene-propylene rubber products can be used for a long time at 120°C, and can be used temporarily or intermittently at 150-180°C. Chlorosulfonated polyethyle...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/34C08L91/06C08K13/02C08K5/14C08K3/04C08K5/098C08K3/22C08K5/3437C08K5/18
Inventor 林然
Owner 上海众力减振技术有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com