High-temperature cured two-component pouring sealant and preparation method thereof

A high-temperature curing, two-component technology, used in chemical instruments and methods, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of non-reuse, increased cost, environmental pollution, etc. Achieve the effect of prolonging the operation time, prolonging the service life and reducing the cost

Inactive Publication Date: 2011-06-15
YANTAI DARBOND TECH
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially potting glue, the general application time is 30-240 minutes, when there is too much mixing at one time, it cannot be reused, resulting in waste of raw materials
After treatment, it is easy to cause environmental pollution and increase costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature cured two-component pouring sealant and preparation method thereof
  • High-temperature cured two-component pouring sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Accurately weigh 100.00g of vinyl silicone oil, 9.98g of low-hydrogen silicone oil curing agent, 0.02g of vinyl siloxane, 25.00g of aluminum hydroxide with an average particle size of 5μm, and 55.00g of spherical alumina powder with an average particle size of 40μm. g, carbon black 10g, add in the dual planetary power mixing mixer successively, in vacuum degree-0.1MPa, the rotation speed is 400 rev / min, and revolution speed is under the condition of 8 rev / min, mechanical stirring obtains component A for 1 hour, Packaged and placed for use; 108.00g of vinyl silicone oil, 2.00g of platinum catalyst with a concentration of 1000ppm, 30.00g of aluminum hydroxide with an average particle size of 5μm, and 60.00g of spherical alumina powder with an average particle In a planetary power mixing mixer, under the conditions of vacuum degree -0.1MPa, rotation speed of 400 rpm, and revolution speed of 8 rpm, mechanically stir for 1 hour to obtain component B, which is packaged and pla...

Embodiment 2

[0040]Accurately weigh 79.98g of vinyl silicone oil, 30.00g of low-hydrogen silicone oil curing agent, 0.04g of alkyneoxysilane, 30.00g of aluminum hydroxide with an average particle size of 2μm, and 50.00g of spherical alumina powder with an average particle size of 60μm. g, 10.00g of spherical alumina powder with an average particle size of 0.10μm is added to the double planetary power mixer in turn, under the conditions of vacuum degree -0.08MPa, rotation speed of 1000 rpm and revolution speed of 15 rpm Component A was obtained under mechanical stirring for 1 hour, and the package was placed for use; 109.00 g of vinyl silicone oil, 1.00 g of platinum catalyst with a concentration of 5000 ppm, 25.00 g of aluminum hydroxide with an average particle size of 2 μm, and a class with an average particle size of 60 μm 45.00g of spherical alumina powder, 10.00g of spherical alumina powder with an average particle size of 0.10μm, and 10.00g of iron red are added to the double planetar...

Embodiment 3

[0044] Accurately weigh 29.69g of vinyl silicone oil, 0.30g of low hydrogen-containing silicone oil curing agent, 0.01g of alkyneoxysilane, 18.00g of zinc oxide powder with an average particle size of 5μm, and spherical alumina powder with an average particle size of 2μm 40.00g of aluminum powder, 10.00g of spherical aluminum powder with an average particle size of 2μm, 100.00g of spherical aluminum oxide powder with an average particle size of 25μm, and 2.00g of titanium dioxide. MPa, the rotation speed is 300 rpm, and the revolution speed is 5 rpm, and mechanically stirred for 2 hours to obtain component A, which is packaged and placed for use; 29.92g of vinyl silicone oil, 0.08g of platinum catalyst with a concentration of 3000ppm, 18.00g of zinc oxide powder with an average particle size of 5μm, 50.00g of spherical alumina powder with an average particle size of 2μm, 100.00g of spherical alumina powder with an average particle size of 25μm, and 2.00g of silver powder with a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature cured two-component pouring sealant and a preparation method thereof, and the heat-conducting pouring sealant is prepared by an A component and a B component according to the weight ratio of 100: 80-100: 125, wherein the A component comprises the following raw materials by weight percent: 45.00%-85.00% of heat-conducting powder, 14.00%-50.00% of low-viscosity liquid silicon oil, 0.15%-15.00% of silane curing agent, 0.005-0.02% of inhibitor, and 0.00-5.00% of color toner; and the B component comprises the following raw materials by weight percent: 45.00%-85.00% of heat-conducting material, 14.00%-55.00% of the low-viscosity liquid silicon oil, 0.04%-1.00% of catalyst and 0.00-5.00% of the color toner. The preparation method of the heat-conducting pouring sealant comprises the following steps: respectively preparing the A component and the B component, uniformly mixing the A component with the B component according to the weight ratio of 100: 80-100: 125 during the use, and heating and curing for 2 hours at the temperature of 60-80 DEG C for preparation.

Description

technical field [0001] The invention relates to a high-temperature curing heat-conducting silica gel, in particular to a high-temperature curing two-component potting silica gel and a preparation method thereof, which are applicable to potting applications of various electronic components and belong to the field of potting adhesives. Background technique [0002] At present, the use of dense circuits has become the mainstream of the modern electronics industry. The call for miniaturization and densification of electronic components is getting louder and louder, and its working environment is getting worse. Among them, the densification of electronic components makes the temperature of its working environment higher and higher, which greatly reduces its service life and safety, and limits the development of the electronic industry. [0003] High temperature resistant materials can improve the operating temperature of electronic devices and prolong their service life. However...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J183/07C09J183/05C09J11/04C09J11/06C09J11/08C09K3/10
Inventor 冒小峰王建斌解海华
Owner YANTAI DARBOND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com