High-hardness and wear-resistance aqueous wood lacquer and preparation method thereof

A water-based wood paint and wear-resistant technology, applied in polyurea/polyurethane paint, coating, etc., can solve the problems of poor wear resistance and low hardness of water-based wood paint, and achieve the effect of improving wear resistance and convenient and quick operation

Inactive Publication Date: 2011-06-29
王奇
View PDF1 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a water-based wood paint with high hardness and wear resistance and its preparation method, so as to solve the problems of low hardness and poor wear resistance of the existing water-based wood paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Preparation of a kind of high hardness and abrasion resistance waterborne wood lacquer:

[0026] (1), preparation of nano-alumina slurry:

[0027] Directly adding nano-alumina powder into the wood lacquer system is not easy to disperse, because the stable nano-alumina slurry is prepared in advance, and then added to the wood lacquer system during the let-down stage.

[0028] a. Nano-alumina slurry is prepared from the following raw materials by weight: nano-alumina powder: 10, defoamer: 0.2, wetting agent: 0.2, stearic acid 0.5, aluminate 1.1, pH value adjustment Agent: 0.1, thickener: 0.4, deionized water: 87.5;

[0029] b. Preparation method: Add deionized water, defoamer, wetting agent, dispersant stearic acid and aluminate, and pH regulator in sequence in the stirring state of the disperser. After adding, disperse at a medium-low speed 5-10 minutes, then add nano-alumina powder, increase the speed to medium-high speed, then slowly add thickener, disperse at high s...

Embodiment 2

[0036] Preparation of a wood primer with high hardness and fullness for home decoration:

[0037] Step (1) is with embodiment 1.

[0038] (2), preparation of wood primer:

[0039] a. Water-based wood paint is prepared from the following raw materials by weight: water-based polyurethane dispersion: 500, acrylic emulsion 345, nano-alumina paste: 100, defoamer: 2, wetting agent: 5, pH adjustment Agent: 1. Coating agent: 14. Leveling agent: 4. Thickener: 4. Slip agent: 3. Deionized water: 20;

[0040] b. Preparation method: Add water-based polyurethane dispersion, acrylic emulsion, defoamer, wetting agent, and pH value regulator in order by weight in the stirring state of the disperser, disperse at a low speed for 5 minutes, and then slowly add nano-alumina slurry , disperse at medium speed for 20-30 minutes, defoam at low speed for 5-10 minutes, then add film-forming aids, leveling agents, thickeners, slip agents and deionized water in sequence, stir at medium speed for 5-15 mi...

Embodiment 3

[0042] Preparation of a wood primer with high hardness and fullness for furniture:

[0043] Step (1) is with embodiment 1.

[0044] (2), preparation of wood primer:

[0045] a. Water-based wood lacquer is prepared from the following raw materials by weight: water-based polyurethane dispersion: 845, nano-alumina paste: 100, defoamer: 2, wetting agent: 5, pH regulator: 1, Coating agent: 14, leveling agent: 3, thickener: 4, slip agent: 4, deionized water: 20;

[0046]b. Preparation method: Add water-based polyurethane dispersion, defoamer, wetting agent, and pH value regulator in sequence according to the weight of the disperser, disperse at low speed for 5 minutes, and then slowly add nano-alumina slurry, medium speed Disperse for 20-30 minutes, defoam at low speed for 5-10 minutes, then add film-forming aids, leveling agents, thickeners, slip agents and deionized water in sequence, stir at medium speed for 5-15 minutes, and filter out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-hardness and wear-resistance aqueous wood lacquer and a preparation method thereof. The wood lacquer is prepared from the following raw material in part by weight: 500 to 850 parts of aqueous polyurethane dispersion, 0 to 350 parts of acrylic acid emulsion, 90 to 110 parts of nano aluminum oxide slurry, 2 to 5 parts of defoaming agent, 4 to 6 parts of wetting agent, 1 to 2 parts of pH regulator, 13 to 15 parts of film-forming assistant, 3 to 5 parts of leveling agent, 3 to 5 parts of thickener, 2 to 4 parts of slipping agent and 15 to 25 parts of deionized water. Because the nano aluminum oxide additive is added into the aqueous wood lacquer system, the hardness and wear resistance of the aqueous wood lacquer are improved; and the aqueous wood lacquer is environmentally-friendly, stable in performance and suitable for home decoration and furniture industry.

Description

technical field [0001] The invention relates to the technical field of water-based wood lacquer, in particular to a water-based wood varnish with high hardness and wear resistance and a preparation method thereof. Background technique [0002] With the increasing awareness of environmental protection, the use of solvent-based coatings has been increasingly limited, and water-based coatings have the advantages of no environmental pollution, low toxicity and no fire hazards, and more and more people's attention and attention. In developed countries such as Europe and the United States, with the deepening of environmental protection regulations, the sales of solvent-based wood lacquers are decreasing year by year, and the consumption of water-based wood lacquers is increasing year by year. In our country, with the deepening of reform and opening up, the rapid development of the national economy and the improvement of people's living standards, low-pollution and high-performance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D133/00C09D7/12
Inventor 王奇
Owner 王奇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com