Alloy steel roller and manufacturing process thereof

A manufacturing process and technology of alloy steel, applied in the field of alloy steel rolls to achieve the effect of high hardness and wear resistance

Active Publication Date: 2012-10-03
JIANGYIN RUNYUAN MACHINERY
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But to sum up, there are only three issues: one is the level of wear resistance (including roughness resistance), the second is the depth of the effective hardened layer, and the third is the size of crack resistance (including anti-stripping)
However, it is difficult to meet the above requirements with the rolls manufactured by the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alloy steel roller and manufacturing process thereof
  • Alloy steel roller and manufacturing process thereof
  • Alloy steel roller and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] One of the embodiments of the present invention is an alloy steel roll, the alloy steel in the alloy steel roll contains the following components: by weight percentage, the content of carbon (C) is 0.60%, the content of silicon (Si) is 1.6% %, the content of manganese (Mn) is 1.75%, the content of chromium (Cr) is 1.6%, the content of molybdenum (Mo) is 0.25%, the content of nickel (Ni) is 0.25%, and the content of vanadium (V) is 0.08% %, the content of niobium (Nb) is 0.06%, and the content of sulfur (S) and phosphorus (P) is less than or equal to 0.025%.

[0032] The technical solution of the present invention also provides a manufacturing process for producing alloy steel rolls using the above-mentioned alloy components. The manufacturing process includes a smelting process, a forging process and a heat treatment process. It is characterized in that the process steps of the above-mentioned process are:

[0033] The first step: smelting process, the smelting process ...

Embodiment 2

[0048] One of embodiment of the present invention is a kind of alloy steel roll, and the alloy steel in this alloy steel roll contains following composition: by weight percentage, the content of carbon (C) is 0.68%, the content of silicon (Si) is 1.8% %, the content of manganese (Mn) is 1.85%, the content of chromium (Cr) is 1.8%, the content of molybdenum (Mo) is 0.35%, the content of nickel (Ni) is 0.5%, and the content of vanadium (V) is 0.10% %, the content of niobium (Nb) is 0.08%, and the content of sulfur (S) and phosphorus (P) is less than or equal to 0.025%.

[0049] The technical solution of the present invention also provides a manufacturing process for producing alloy steel rolls using the above-mentioned alloy components. The manufacturing process includes a smelting process, a forging process and a heat treatment process. It is characterized in that the process steps of the above-mentioned process are:

[0050] The first step: smelting process, the smelting proce...

Embodiment 3

[0060] One of the embodiments of the present invention is an alloy steel roll, the alloy steel in the alloy steel roll contains the following components: by weight percentage, the content of carbon (C) is 0.64%, the content of silicon (Si) is 1.7% %, the content of manganese (Mn) is 1.80%, the content of chromium (Cr) is 1.7%, the content of molybdenum (Mo) is 0.30%, the content of nickel (Ni) is 0.375%, and the content of vanadium (V) is 0.09% %, the content of niobium (Nb) is 0.07%, the content of aluminum (Al) is 0.0225%, and the content of sulfur (S) and phosphorus (P) is less than or equal to 0.025%.

[0061] The technical solution of the present invention also provides a manufacturing process for producing alloy steel rolls using the above-mentioned alloy components. The manufacturing process includes a smelting process, a forging process and a heat treatment process. It is characterized in that the process steps of the above-mentioned process are:

[0062] The first ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an alloy steel roller and a manufacturing method thereof. Alloy steel in the alloy steel roller contains metal elements such as silicon, manganese, chromium, molybdenum, nickel, vanadium, niobium and the like, wherein the content of carbon is between 0.60 percent and 0.68 percent; and the content of sulfur and the content of phosphorous are smaller than or equal to 0.025 percent. The manufacturing method comprises a smelting process, a forging process and a thermal treatment process, wherein the thermal treatment process comprises a thermal treatment process after forging, a preparation thermal treatment process, a quenching thermal treatment process and a final annealing process. In the quenching thermal treatment process, a medium-frequency electromagnetic induction heating device and a water spraying device are adopted. By improvement on a material, i.e., improvement on the thermal treatment process, the continuous rolling time of the roller can be prolongedby more than 2 hours, surface hardness, the depth of a quenched case, surface wearing resistance and the resistance to events such as fracture and the like are remarkably enhanced, the comprehensive performance is remarkably improved, the loss of the roller is reduced, the roller changing frequency is remarkably lowered, and the production efficiency of a cold-roll steel sheet is further increased.

Description

technical field [0001] The invention relates to a metal cold-rolled and / or hot-rolled roll, in particular to an alloy steel roll. Background technique [0002] Prior art In the metal cold rolling production process, the roll is the main deformation tool of the rolling mill. Due to the problem of the material of the roll itself and the harsh working environment in which it is located, the roll often fails or even is scrapped. Such as: excessive wear of rolls, surface roughness (orange peel), grid pits, strangulation marks, cracking and peeling, etc. But to sum up, there are only three issues: one is the level of wear resistance (including roughness resistance), the second is the depth of the effective hardened layer, and the third is the size of crack resistance (including anti-stripping). Therefore, in order to improve the service life of the cold roll, first the roll must have a suitable material with high wear resistance, the hardness of the surface of the second roll mus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/58B21B27/00B23P15/00C21D8/00C21D9/38
Inventor 曹伟
Owner JIANGYIN RUNYUAN MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products