Normal-temperature-curable high-temperature-resistant conveyer belt adhesive and preparation and application method thereof
A room temperature curing and adhesive technology, applied in the direction of bonding method, adhesive type, chloroprene adhesive, etc., can solve the problem of joint strength only reaching 60-70%, short service time, and poor bonding strength Advanced problems, to achieve good benefits, short operating time, good flex resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] First, according to the mass fraction ratio of chloroprene rubber 70, chlorinated rubber 30, zinc oxide 7, magnesium oxide 5, phenolic resin 20, coupling agent 5, and mixed solvent (toluene, ethyl acetate) 400, these solvents, The solid material was put into the reaction tank in turn, and stirred at 40 ° C for 2 hours to obtain the adhesive component A;
[0024] Then, at the time of use, the prepared A component is mixed with the B component which is mainly 3,3'-dimethyl-triphenylmethane-4,4',6,6'-tetraisocyanate polymer in a ratio of 10: The ratio of 1 is mixed evenly, that is, the room temperature curing high temperature resistant conveyor belt adhesive is obtained;
[0025] Before use, the prepared conveyor belt joints must be ground, cleaned and dried, and then coated with adhesive, the joints are bonded, and then rolled with a roller or a hand hammer to be compacted, cured at room temperature, and the conveyor belt can be used. .
Example Embodiment
[0026] Example 2
[0027] First, according to the mass ratio of chloroprene rubber 70, chlorinated rubber 30, zinc oxide 7, magnesium oxide 5, epoxy ester 20, coupling agent 5, mixed solvent (toluene, ethyl acetate) 400 parts by mass, these solvents , the solid material was put into the reaction tank in turn, and stirred at 45 ° C for 1.5 hours to obtain the adhesive component A;
[0028] Then, at the time of use, the prepared A component is mixed with the B component which is mainly 4,4'-dicarboxy-diphenylmethane-4,4',8,8'-hexaisocyanate polymer in a ratio of 10:1 The proportion of the mixture is evenly mixed, that is, the room temperature curing and high temperature resistant conveyor belt adhesive is obtained;
[0029] Before use, the prepared conveyor belt joints must be ground, cleaned and dried, and then coated with adhesive, the joints are bonded, and then rolled with a roller or a hand hammer to be compacted, cured at room temperature, and the conveyor belt can be use...
Example Embodiment
[0030] Example 3
[0031] First, according to the mass fraction ratio of chloroprene rubber 70, chlorinated rubber 30, zinc oxide 7, magnesium oxide 5, ethylene-vinyl acetate copolymer resin 20, coupling agent 5, mixed solvent (toluene, ethyl acetate) 400, These solvents and solid materials were put into the reaction tank in turn, and stirred at 50 ° C for 1 hour to obtain the adhesive A component;
[0032] Then, at the time of use, the prepared A component is mixed with the B component which is mainly 3,3'-diethyl-triphenylmethane-5,5',8,8'-heptaisocyanate polymer in a ratio of 10: The ratio of 1 is mixed evenly, that is, the room temperature curing high temperature resistant conveyor belt adhesive is obtained;
[0033] Before use, the prepared conveyor belt joints must be polished, cleaned and dried, and then coated with adhesive, the joints are bonded, and then rolled with a roller or a hand hammer to be compacted, cured at room temperature, and the conveyor belt can be us...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap