PVC (Poly Vinyl Chloride) thermal contraction printing film

A printing film and heat-shrinking technology, which is applied in the field of PVC heat-shrinkable printing film, can solve the problems of lower ink printing quality, and the anti-static function of PVC heat-shrinkable printing film has not been effectively solved, so as to delay controllable effect and reduce defects. effect of influence

Active Publication Date: 2013-03-13
YIXING GUANGHUI PACKAGE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] To sum up, objectively, the existing technology is difficult to eliminate the static electricity of PVC heat-shrinkable printing film without reducing the quality of ink printing, and at the same time rarely increase the cost to reduce static electricity. Therefore, PVC heat-shrinkable printing film anti-static The function has not been effectively resolved for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (Poly Vinyl Chloride) thermal contraction printing film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1: Formula: 100 parts by weight of suspension method loose type (SG-5 type) PVC resin, 2.0 parts by weight of methyl tin mercaptide 181, 4.5 parts by weight of dioctyl phthalate (DOP), processing aid acrylic acid Ester copolymer (ACR-201) 1.5 parts by weight, impact modifier methacrylic acid-butadiene-styrene copolymer (MBS BTA-717) 3.2 parts by weight, internal lubricant diglyceryl ether monooleate (G-16) 0.9 parts by weight, external lubricant oxidized polyethylene wax (AC316A) 0.3 parts by weight, antistatic agent (SN) 0.8 parts by weight of isopropyl triisostearate titanate coupling treatment.

[0025] Antistatic agent coupling treatment: Add 2000g antistatic agent SN (stearamidopropyldimethyl-β-hydroxyethylammonium nitrate) and 24g isopropyl triisostearate titanate to a 5L high-speed Mix at high speed in a mixer with a rotation speed of 2960rpm. When the temperature of high-speed mixing rises to 110-120°C, discharge and cool to room temperature to obtain a ...

Embodiment 2

[0030] Embodiment 2: formula: 100 parts by weight of SG-7 type PVC resin, 2.5 parts by weight of methyl tin 191, 5.0 parts by weight of dioctyl terephthalate (DOTP), processing aid acrylate copolymer (ACR K- 120ND) 2.0 parts by weight, 4.0 parts by weight of impact modifier methacrylic acid-butadiene-styrene copolymer (MBS B521), 1.2 parts by weight of dicarboxylic acid ester (G60) of internal lubricant saturated fatty alcohol, 0.6 parts by weight of complex ester (G78) for external lubricant, 1.2 parts by weight of antistatic agent SP coupled with isopropyl triisostearate titanate.

[0031] Antistatic agent coupling treatment: Add 2000g antistatic agent SP (stearamidopropyl dimethyl-β-hydroxyethyl ammonium dihydrogen phosphate) and 20g isopropyl triisostearate titanate to Mix at medium speed in a 5L high-speed mixer with a rotation speed of 2960rpm. When the temperature rises to 110~120°C, release and cool to room temperature for later use.

[0032] Add 2400g antistatic agen...

Embodiment 3

[0035] Embodiment 3: formula: 100 parts by weight of SG-5 type PVC resin, 1.8 parts by weight of isooctyl dimercaptoacetate di-n-octyltin (DOTTG), 3.0 parts by weight of epoxy soybean oil (ESBO), processing aid acrylate copolymerization (ACR K-125) 1.8 parts by weight, impact modifier methacrylic acid-butadiene-styrene copolymer (MBS B22) 2.8 parts by weight, internal lubricant monoglyceride stearate (GMS) 0.8 parts by weight 0.3 parts by weight of the external lubricant oxidized polyethylene wax, and 1.0 parts by weight of the antistatic agent Atmos150 treated with isopropyl triisostearate titanate coupling.

[0036] Antistatic agent coupling treatment: Add 2000g Atmos150 (mono-diglycerides of palmitic acid and stearic acid) and 22g isopropyl triisostearate titanate to a 5L high-speed mixer and mix at a high speed at 2960rpm , when the temperature rises to 110~120°C, release and cool to room temperature for later use.

[0037] Add 1600g Atmos150 (mono-diglycerides of palmiti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PVC (Poly Vinyl Chloride) thermal contraction printing film, which is characterized in that 0.8-1.2 parts by weight of cation quaternary ammonium salt or nonionic esters antistatic agent are added into components; the added antistatic agent is firstly coupled and processed by coupling agent adaptive to the antistatic agent; in the film preparation process, the cation quaternary ammonium salt or a nonionic esters antistatic agent solution layer are applied to the surface of the film; and therefore the surface resistivity of the film is 108-1010 omega. Two different applied antistatic agents are applied to successively perform action. On the premise that other performances of the PVC thermal contraction printing film are guaranteed to be substantially unchanged, static charges in the production process are effectively prevented or eliminated from generating and accumulating, and the shortage brought by the static charges is avoided, and pollution on printing because the antistatic agent is excessively separated out can be avoided.

Description

technical field [0001] The invention is an improvement to the PVC heat-shrinkable printing film, and in particular relates to a PVC heat-shrinkable printing film which not only has antistatic function, but also does not reduce ink printing quality and rarely increases the cost. Background technique [0002] PVC heat-shrinkable printing film is a hard transparent PVC film, which is used for heat-shrinkable labels on product packaging after printing exquisite patterns. [0003] However, the surface resistivity of PVC heat shrinkable printing film is 10 14 ~10 16 Ω, has good insulation, and insulation leads to easy accumulation of static electricity. Objectively speaking, during the production and printing process of the film, the film will rub against multiple high-speed rollers, which is more likely to generate static electricity, and the accumulation of static electricity will easily lead to many quality problems. For example: the surface of PVC heat-shrinkable printing f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L51/00C08K13/06C08K5/58C08K5/12C08K5/20C08K5/103B29C55/28
Inventor 杨涛陈亚龙周军峰陈丽颖于世发殷宇晨钱鑫陈丽娜李涛杭崭东
Owner YIXING GUANGHUI PACKAGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com