Low-temperature self-crosslinking polyacrylate pigment printing binding agent and preparation method thereof

A technology of polyacrylate and pigment printing, applied in the direction of ester copolymer adhesives, adhesive types, etc., can solve the problems of hand feeling, environmental protection, fastness and stability, etc., achieve bright color, low cost, The effect of the simplicity of the polymerization process

Inactive Publication Date: 2012-03-28
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 67 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with similar foreign products, the adhesives produced in my country still h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] Mix 50.0 g of butyl acrylate, 25.0 g of isooctyl acrylate, 13.0 g of methyl methacrylate, 4.0 g of acrylonitrile, 2.0 g of methacrylic acid, 3.0 g of hydroxypropyl acrylate, 2.0 g of diacetone acrylamide, and emulsifier 1.7 g, 60g deionized water, stir evenly to make a pre-emulsion; dissolve 0.4g potassium persulfate in 8.0g deionized water to prepare an initiator solution; add 25.0g deionized water and 0.8 emulsifier to the polymerization reactor g and 0.3g of sodium bicarbonate, stir well; add 14g of the above-mentioned pre-emulsion and 2g of the above-mentioned initiator solution to the polymerization reactor, and heat to 78°C. After the blue light appears in the emulsion in the polymerization reactor, return to the polymerization reactor Add the remaining pre-emulsion and initiator solution 6g dropwise continuously, after 2h continuous dropwise addition, add the remaining initiator solution, raise the temperature to 85℃, keep it for 1h, then lower th...

Example Embodiment

[0031] Example 2

[0032] Mix 60.0 g of butyl acrylate, 16.0 g of isooctyl acrylate, 10.0 g of methyl methacrylate, 4.0 g of acrylonitrile, 2.0 g of methacrylic acid, 4.0 g of hydroxypropyl acrylate, 2.5 g of diacetone acrylamide, and 2.0 g of emulsifier. g, 60g deionized water, stir evenly to make a pre-emulsion; dissolve 0.35g potassium persulfate in 7.0g deionized water to prepare an initiator solution; in the polymerization reactor, add 25.0g deionized water and 1.0 emulsifier g and 0.2g of sodium bicarbonate, stir well; add 15g of the above pre-emulsion and 2.5g of the above initiator solution to the polymerization reactor, and heat to 80°C. After the blue light appears in the emulsion in the polymerization reactor, proceed to the polymerization reaction. Add 7g of the remaining pre-emulsion and initiator solution to the kettle continuously. After 3 hours of continuous dripping, add the remaining initiator solution, increase the temperature to 90°C, hold for 0.5h, and then ...

Example Embodiment

[0035] Example 3

[0036] Mix 68.0 g of butyl acrylate, 8.0 g of ethyl acrylate, 7.0 g of methyl methacrylate, 7.0 g of styrene, 2.5 g of methacrylic acid, 3.0 g of hydroxypropyl acrylate, 3.0 g of diacetone acrylamide, and 2.0 g of emulsifier. , 60g deionized water, uniformly stirred to make a pre-emulsion; dissolve 0.35g potassium persulfate in 7.0g deionized water to prepare an initiator solution; in the polymerization reactor, add 25.0g deionized water and 1.0g emulsifier And sodium bicarbonate 0.2g, stir evenly; add 16g of the above-mentioned pre-emulsion and 2.3g of the above-mentioned initiator solution to the polymerization reactor, and heat up to 82°C. After the blue light appears in the emulsion in the polymerization reactor, return to the polymerization reactor Add 8g of the remaining pre-emulsion and initiator solution dropwise continuously, after 2.5 hours of continuous dropwise addition, add the remaining initiator solution, raise the temperature to 88°C, keep it f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature self-crosslinking polyacrylate pigment printing binding agent and a preparation method thereof. The method comprises the following steps of: based on part by mass, preparing pre-emulsion from 70-90 parts of soft monomer, 10-30 parts of hard monomer, 5-10 parts of crosslinking monomer, 2-5 parts of ketone-containing carbonyl monomer, 0.6-3.0 parts of emulsifier and 50-70 parts of de-ionized water; adding 25-33 parts of de-ionized water, 0.2-1.0 part of emulsifier and 0.2-0.6 part of pH buffer; adding 14-16 parts of pre-emulsion and 2-2.5 parts of initiator solution; heating to 78-82 DEG C; dropwise adding remaining pre-emulsion and initiator solution after blue light occurs; heating to 85-90 DEG C and preserving heat for 0.5-1 hour; then cooling to be below 40 DEG C; adjusting pH value to be 6.5-7.0; and finally adding solution formed by dissolving 1-3 parts of hydrazide based monomer in 4-5 parts of de-ionized water. The agent is a formaldehyde-free environmentally-friendly product.

Description

technical field [0001] The invention relates to the field of polyacrylate adhesive emulsion for pigment printing, in particular to a low-temperature self-crosslinking acrylate pigment printing adhesive and a preparation method thereof. Background technique [0002] Pigment printing is a printing method in which finely dispersed pigment particles are attached to fabrics by means of a binder. Pigment printing has the advantages of simple process, energy saving and less environmental pollution. At present, the global pigment printing fabric accounts for more than 70% of the total output of printed cloth. In recent years, my country's pigment printing has also made great progress, but the product structure is not yet reasonable. Most of the middle and low-end products have meager profits. The quality and grade of pigment printing products depend to a large extent on the performance of pigment printing adhesives, so preparing high-performance adhesives is the most important meas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F220/14C08F220/46C08F212/08C08F218/08C08F218/00C08F2/24C09J133/08D06P1/52
Inventor 涂伟萍卢杰宏胡剑青王锋
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap