Boron-containing high speed steel roller and preparation method thereof
A high-speed steel and roll technology, applied in the field of steel rolling, can solve the problems of large fluctuations in mechanical properties and poor wear resistance, and achieve the effects of good machining performance, high tool consumption and low direct processing efficiency.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0048] The boron-containing high-speed steel roll material is smelted in a 500-kg medium-frequency induction furnace. The specific manufacturing process steps are:
[0049] 1) First, use scrap steel, recarburizer, ferrochrome, copper plate, ferrotungsten and ferromolybdenum to mix and heat and melt. After the molten steel is melted, add ferrosilicon. When the temperature rises to 1524°C, add aluminum and nitrogen-containing ferrochrome, and then add vanadium in sequence. Iron, ferro-boron and ferro-titanium, after adjusting the components before the furnace to pass, the temperature of the molten steel is raised to 1563°C, and the slag is removed from the furnace.
[0050] 2) Crushing iron bismuth, copper telluride master alloy, potassium-containing substance, sodium-containing substance and rare earth magnesium alloy (the rare earth element is cerium) into small pieces with a particle size of less than 10mm, dried at 200°C, and placed in a ladle At the bottom, the molten steel...
Embodiment 2
[0057] The boron-containing high-speed steel roll material is smelted in a 750-kg medium-frequency induction furnace. The specific manufacturing process steps are:
[0058] 1) First, use scrap steel, recarburizer, ferrochrome, copper plate, ferrotungsten and ferromolybdenum to mix and heat and melt. After the molten steel is melted, add ferrosilicon. When the temperature rises to 1549°C, add aluminum and nitrogen-containing ferrochrome, and then add vanadium in turn. Iron, ferro-boron and ferro-titanium, after adjusting the composition before the furnace to pass, the temperature of the molten steel is raised to 1580°C, and the slag is removed from the furnace.
[0059] 2) Crushing iron bismuth, copper telluride master alloy, potassium-containing substance, sodium-containing substance and rare earth magnesium alloy (specifically, the rare earth element is lanthanum) into small pieces with a particle size of less than 10mm, dried at 180°C, and placed in a ladle At the bottom, th...
Embodiment 3
[0066] The boron-containing high-speed steel roll material is smelted with a 750 kg medium-frequency induction furnace, and the manufacturing process steps are:
[0067] 1) First, use scrap steel, recarburizer, ferrochrome, copper plate, ferrotungsten and ferromolybdenum to mix and heat and melt, then add ferrosilicon after the molten steel is melted, and when the temperature rises to 1536°C, add aluminum and nitrogen-containing ferrochrome, and then add vanadium in sequence Iron, ferro-boron and ferro-titanium, after adjusting the composition before the furnace to pass, the temperature of the molten steel is raised to 1571°C, and the slag is removed from the furnace.
[0068] 2) Crushing iron bismuth, copper telluride master alloy, potassium-containing substance, sodium-containing substance and rare earth magnesium alloy (the specific rare earth element is yttrium) into small pieces with a particle size of less than 10mm, dried at 190°C, and placed in a ladle At the bottom, t...
PUM
Property | Measurement | Unit |
---|---|---|
height | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com