Modified high-density polyethylene composition used in extrusion blow molding, and preparation method thereof
A high-density polyethylene, extrusion blow molding technology, applied in the field of modified high-density polyethylene composition and its preparation, can solve the problems of low low-temperature impact performance, difficult control, high cost, etc., to improve processing performance and reduce processing Difficulty and the effect of reducing the torque value
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example
[0027] Examples 1 to 7, Comparative Examples 1 to 5
[0028] (1) Material mixing and extrusion granulation: Mix Crodamide URX (manufactured by Croda Company, brand Crodamide URX) and polyethylene glycol 10000 (Beijing Chemical Reagent Company, molecular weight 10000) in proportion; in the batching tank, the high Density polyethylene (produced by Sinopec Qilu Petrochemical Company, brand QBH18), styrene butadiene rubber (Sinopec Beijing Chemical Industry Research Institute, brand VP101, average particle size 100nm; gel content 65%), antioxidant (antioxidant 168 Compound with antioxidant 1010, Ciba company in Switzerland) by weight ratio of 1:1 into the high-speed mixer, continuous high-speed stirring at room temperature for 3 to 5 minutes, so that the components are fully mixed; the mixed raw materials, with 200 The rotation speed is ~350r.pm and the appropriate screw block is combined, and it is melted and extruded at a temperature of 215℃~235℃. After extrusion, it is cooled and ...
Example
[0033] Comparative Examples 6-10, Examples 8-12
[0034] In order to further investigate the effect of the compound lubricant, the fixed HDPE is 100 parts by weight, the styrene-butadiene rubber is 3 parts by weight, and the antioxidant is 0.2 parts by weight (using antioxidant 168 and antioxidant 1010 by weight The ratio is 1:1 compound), and different ratios of compound lubricant are added. The specific formula is shown in Table 2, and the processing process is the same as in Example 1.
[0035] The resulting composition is subjected to a torque reduction test: the material is subjected to a material extrusion test in a twin-screw extruder (produced by Corbelon) with a diameter of 18, and the blank sample is first extruded on the equipment to detect the torque during the extrusion process value. Extrude the sample with lubrication system under the same conditions, and detect the torque value during the extrusion process. The difference between the torque value and the blank samp...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap