Glass fiber soaking agent and preparation method thereof

A technology of glass fiber and sizing agent, applied in the field of glass fiber sizing agent and its preparation, can solve the problems such as affecting the weaving process, breaking the whole bundle of yarn, unable to protect the stress condition of the glass fiber, etc., so as to improve the physical and chemical properties and solve the problem of broken yarn Effect

Active Publication Date: 2012-06-20
ANHUI DANFENG ELECTRONICS MATERIAL
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the general-purpose glass fiber electronic textile yarn sizing agent is not enough to improve the physical and chemical properties of glass fiber, and cannot protect the stress condition of glass fiber in the weaving process, resulting in the glass fiber electronic textile yarn under various tensions and frictions. Under these conditions, single fiber breakage or even the whole bundle of yarn breakage often occurs, which seriously affects the smooth progress of the textile process, and brings serious defects to textile products, greatly reducing the quality level of textile products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] ⑴ Put about 1000 liters of pure water in a 2000 liter preparation tank (take 1500 liters of preparation as an example), pour 3.5% modified amylose and 1.5% modified amylopectin, and heat to 95 ℃ to make the starch Gelatinization, forming a starch slurry.

[0041] (2) Weigh 0.5% microcrystalline paraffin, 0.5% hydrogenated vegetable oil, 0.1% quaternary ammonium salt 1827, 0.1% Span 80, 0.05% sodium dodecylbenzenesulfonate, 0.2% modified Pour the non-toxic epoxy resin adhesive into the homogenizing tank, and use a high-speed homogenizer to stir at a high speed above 6000 R / M at 80 ° C to form a uniform emulsion.

[0042] (3) Add the homogenized emulsion into the gelatinized starch slurry in the preparation tank.

[0043] (4) Add 0.01% defoamer polyoxyethylene polyoxypropylene pentaerythritol ether, add pure water until the total amount of sizing agent is 1500 liters, keep the temperature of sizing agent at 60°C, and it can be used for wire drawing production.

[0044] ...

Embodiment 2

[0046] ⑴Put about 1000 liters of pure water in a 2000 liter preparation tank (take 1500 liters of preparation as an example), pour 4.5% modified amylose and 2.5% modified amylopectin, heat to 90 ℃ to make the starch Gelatinization, forming a starch slurry.

[0047] (2) Weigh 1.5% of microcrystalline paraffin, 1.5% of hydrogenated vegetable oil, 0.5% of quaternary ammonium salt 1231, 0.5% of Span 80, 0.1% of sodium dodecylbenzenesulfonate, and 1.0% of modified Pour the non-toxic epoxy resin adhesive into the homogenizing tank, and use a high-speed homogenizer to stir at a high speed above 6000 R / M at 70 ° C to form a uniform emulsion.

[0048] (3) Add the homogenized emulsion into the gelatinized starch slurry in the preparation tank.

[0049] (4) Add 0.02% defoamer polyoxyethylene polyoxypropanolamine ether, add pure water until the total amount of sizing agent is 1500 liters, keep the temperature of sizing agent at 65°C, and it can be used for wire drawing production.

[00...

Embodiment 3

[0052] ⑴Put about 1000 liters of pure water in a 2000 liter preparation tank (taking 1500 liters of preparation as an example), pour 2.5% modified amylose and 1.5% modified amylopectin, and heat to 95°C to make the starch Gelatinization, forming a starch slurry.

[0053] (2) Weigh 1.5% of microcrystalline paraffin, 1.5% of hydrogenated vegetable oil, 0.2% of quaternary ammonium salt 1827, 0.1% of Span 80, and 0.02% of SAS, pour them into a homogenizing tank, and use them at 80°C The high-speed homogenizer stirs at a high speed above 6000R / M to form a uniform emulsion.

[0054] (3) Add the homogenized emulsion into the gelatinized starch slurry in the preparation tank.

[0055] (4) Add pure water until the total amount of sizing agent is 1500 liters, keep the temperature of sizing agent at 60°C, and then it can be used for wire drawing production.

[0056]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber soaking agent, which is mainly prepared from the following ingredients in percentage by weight: 2 to 6 percent of modified straight chain starch, 1 to 5 percent of modified amylopectin, 0.5 to 5 percent of microcrystalline wax, 0.5 to 5 percent of hydrogenated vegetable oil, 0.1 to 1 percent of quaternary ammonium salt cation lubricating agents, 0.1 to 1 percent of span 80, 0.01 to 0.5 percent of alkane sulfonate surfactants, 0 to 2.0 percent of modified epoxy resin bonding agents, 0 to 0.05 percent of defoaming agents and the balance water. The glass fiber soaking agent has the advantages that the physical and chemical properties of the glass fiber electronic weaving yarn can be fully improved, the stiffness is between 50 and 80, the tensile intensity is higher than 52 CN / TEX, and the yarn fracture and fuzzing problems in the weaving process are effectively solved.

Description

[0001] technical field [0002] The invention relates to a glass fiber sizing agent and a preparation method thereof. [0003] Background technique [0004] During the drawing production process of glass fiber electronic textile yarn, it is necessary to coat the surface of glass fiber monofilament with sizing agent to play the role of bonding, lubricating and protecting glass fiber, and at the same time improve the physical and chemical properties of glass fiber to make glass fiber electronic textile Yarn properties can be adapted to the needs of the textile process. [0005] At present, the general-purpose glass fiber electronic textile yarn sizing agent is not enough to improve the physical and chemical properties of glass fiber, and cannot protect the stress condition of glass fiber in the weaving process, resulting in the glass fiber electronic textile yarn under various tensions and frictions. Under such conditions, single fiber breakage or even the whole bundle of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C25/36
Inventor 徐大治童学功王新武
Owner ANHUI DANFENG ELECTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products