Luminescent gloze material

A luminous glaze and the following technologies are applied in the field of formulation of luminous glazes, which can solve the problems of inability to meet the production requirements of floor tiles and sanitary ware daily-use porcelain, and achieve the effects of long luminous duration, reasonable ratio and simple formula

Inactive Publication Date: 2012-07-11
陈新基
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the research on ceramic luminous glazes has made great progress and has been widely used, their maximum firing temperature is currently lower than 1100°C, which cannot meet the production requirements of floor tiles, sanitary ware, and daily-use porcelain.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Example 1 The following formula is used to prepare the luminous glaze of the present invention: raw materials in parts by weight: 20 parts of potassium feldspar, 10 parts of albite, 6 parts of red lead, 5 parts of boric acid, 3 to 8 parts of spodumene, quartz 20 parts, 4 parts of heavy calcium carbonate, 8 parts of barium carbonate, 3 parts of talc, 2 parts of zinc oxide, 5 parts of bone ash, 0.3 part of zircon sand, 0.5 part of vanadium pentoxide, 1.0 part of copper oxide, ferric oxide 1.5 parts, 3 parts of manganese oxide.

Embodiment 2

[0009] Example 2 The following formula is used to prepare the luminescent glaze of the present invention: raw materials in parts by weight: 25 parts of potassium feldspar, 8 parts of albite, 8 parts of red lead, 10 parts of boric acid, 3 to 8 parts of spodumene, quartz 24 parts, 6 parts of heavy calcium carbonate, 4.5 parts of barium carbonate, 2 parts of talc, 3.5 parts of zinc oxide, 4 parts of ashes, 0.4 parts of zircon sand, 1.0 parts of vanadium pentoxide, 1.5 parts of copper oxide, ferric oxide 1.0 parts, 8 parts of manganese oxide.

Embodiment 3

[0010] Example 3 The following formula is used to prepare the luminescent glaze of the present invention: raw materials in parts by weight: 30 parts of potassium feldspar, 5 parts of albite, 10 parts of red lead, 7 parts of boric acid, 3 to 8 parts of spodumene, quartz 30 parts, 2 parts of heavy calcium carbonate, 3 parts of barium carbonate, 5 parts of talc, 5 parts of zinc oxide, 2 parts of ashes, 0.5 parts of zircon sand, 0.7 parts of vanadium pentoxide, 2.0 parts of copper oxide, ferric oxide 1.0 parts, 5 parts of manganese oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a luminescent gloze material, which is prepared from the following components in parts by weight: 20-30 parts of potassium feldspar, 5-10 parts of soda feldspar, 6-10 parts of red lead, 5-10 parts of boric acid, 3-8 parts of spodumene, 20-30 parts of quartz, 2-6 parts of coarse whiting, 3-8 parts of barium carbonate, 2-5 parts of talc, 2-5 parts of zinc oxide, 2-5 parts of bone ash, 0.3-0.5 part of zircon sand, 0.5-1.0 part of vanadic oxide, 1.0-2.0 parts of copper oxide, 1.0-2.0 parts of ferric oxide and 3-8 parts of manganese oxide. The luminescent gloze material has a simple formula and a reasonable proportion; the luminescent gloze prepared with the formula is applied to ceramics or enamel luminescent products, has the characteristics of long luminescence time, and can meet burning under high-temperature conditions; and production is easy to control.

Description

technical field [0001] The invention relates to a luminous glaze, in particular to a formula of the luminous glaze. Background technique [0002] Luminescent glaze refers to a glaze that mixes basic glaze and luminescent substance in a certain proportion and then applies it on the surface of the green body. After firing, it has a luminous function. It can be used in the production of ceramic products and enamel products. Its luminescent products have the function of absorbing visible light and emitting strong light at night or in dark places, and can be used in many places such as reception rooms, bedrooms, and bathrooms. Decorate luminous ceramic or enamel signboards on stairs, subway stations, underground squares, railway stations and other places where people are concentrated, which can facilitate people's lives in emergency situations where lighting conditions are suddenly lost. [0003] In recent years, the research on luminous glazes has grown from scratch, and great ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 陈新基
Owner 陈新基