Low detonation velocity powdery emulsion explosive for explosive welding
A technology of powdery emulsion explosive and explosive welding, which is applied in the direction of explosives, etc., can solve the problems that the detonation performance is difficult to meet the requirements of explosive welding explosives, the requirements of explosive welding intensity cannot be met, and the power of ammonium oil explosive is low, so as to ensure the explosion Welding effect, moderate price, high power effect
Active Publication Date: 2014-03-26
ANHUI XIANGKE CHEM IND CO LTD
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Compared with the first type of explosive, this kind of explosive has the characteristics of stable quality and environmental protection, but has the disadvantages of low intensity and power, and the detonation performance is difficult to meet the requirements of explosive welding explosives.
Chinese patent CN1778777A discloses a low detonation velocity explosion welding explosive, which is made by mixing ammonium oil explosives and additives. This patent uses the wheel milling process that has been eliminated in the current civil explosive industry during processing, which cannot be implemented at present, and ammonium oil explosives The power is low, and the performance declines faster after adding inert substances, resulting in unstable performance, which cannot meet the violent requirements of explosive welding
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] Get common powdery emulsion explosive 160kg, talcum powder 40 kg, mix uniformly, can get a kind of powdery emulsion explosive that is used for explosion welding low detonation velocity of the present invention, detonation velocity 2800m / s, intensity 10.9mm, density 0.82 g / cm 3 .
Embodiment 2
[0014] Get 160kg of common powdery emulsion explosives, 30 kg of talcum powder, and 10 kg of perlite, and mix them uniformly to obtain a powdery emulsion explosive for explosive welding with low detonation velocity of the present invention. The detonation velocity is 2580m / s, the intensity is 9.2mm, and the density 0.72 g / cm 3 .
Embodiment 3
[0016] Get 120kg of common powdery emulsion explosives, 60 kg of talcum powder, and 20 kg of perlite, and mix them uniformly to obtain a powdery emulsion explosive for explosive welding with a low detonation velocity of the present invention. The detonation velocity is 2080m / s, the intensity is 8.5mm, the density 0.68 g / cm 3 .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| density | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a low detonation velocity powdery emulsion explosive for explosive welding, which is prepared by mixing the following components by weight percentage: 60-85% of powdery emulsion explosive and 15-40% of at least one of talcum powder and expanded perlite. Water content of the talcum powder is not greater than 0.5wt% and content of the talcum powder with fineness of 40 meshes is 70-85wt%. Water content of the expanded perlite is not greater than 0.5wt% and bulk density of the expanded perlite is 40-60kg / m<3>. Density of the low detonation velocity powdery emulsion explosive for explosive welding is 0.6-0.85g / cm<3>. The low detonation velocity powdery emulsion explosive for explosive welding has the advantages of easy production, stable performance, greater brisance and good explosive welding effect.
Description
technical field [0001] The invention relates to an emulsion explosive, in particular to a powdery emulsion explosive with a low detonation velocity for explosive welding. Background technique [0002] Explosive welding technology is a trinity metal welding process that uses explosives as the energy source of pressure welding, fusion welding and diffusion welding: using explosives as the energy source, through the pulse load generated by the explosive detonation, a material (multilayer) is pushed to a high-speed oblique collision Another material (base layer) realizes the metallurgical bonding of two metals by instantaneous high temperature and high pressure. The main purpose of the metal composite plate produced is to replace expensive stainless steel and non-ferrous metals for petrochemical, chemical, ship, vehicle, heat-resistant, wear-resistant and special equipment and components, so as to reduce the project cost. Due to the special requirements of welding technology, t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C06B31/28
Inventor 姚普华储国平王徐望
Owner ANHUI XIANGKE CHEM IND CO LTD